特殊钢 ›› 2020, Vol. 41 ›› Issue (6): 36-40.

含Ti铝镇静超低碳钢连铸过程水口堵塞控制实践

杨克枝，张乔英，常正昇

马鞍山钢铁股份有限公司技术中心,马鞍山243000

收稿日期:2020-05-29 出版日期:2020-12-01 发布日期:2022-05-07
作者简介:杨克41(1988-),男，硕士(2013年北京科技大学)，工程师， 2010年太原理工大学(本科)毕业，炼钢及连铸工艺改进与产品开发。

Practice on Control of Nozzle Clogging in Casting Process of Ti-Bearing Al-Killed Ultra-Low Carbon Steel

Yang Kezhi, Zhang Qiaoying ，Chang Zhengsheng

Technology Center of Masteel Co Ltd, Ma ^’ anshan 243000

Received:2020-05-29 Published:2020-12-01 Online:2022-05-07

摘要/Abstract

摘要： 分析水口堵塞物组成及其堵塞发生的机理得出,含Ti铝镇静超低碳钢连铸过程水口堵塞物呈分层结构,由反应层和粘结层组成,其中反应层为耐材酸性物质与钢水中Al反应以及钢水因与堵塞壁面接触温度降低、夹杂物析出反应所致,粘结层由夹杂物伴随冷钢堆积所致,且粘结层中Al含量由内至外呈增加的趋势,Ti含量则呈减少的趋势。通过顶渣改质将(FeO+MnO)控制在8%以下、RH脱碳终点[O]控制在0.030%以内,以及采用开浇前中间包充氩置换工艺等优化措施,含Ti铝镇静超低碳钢连浇炉数由原来的3炉提升至5炉,水口堵塞率由原来的80%降低至30%。

关键词: 铝镇静钢, 含Ti, 水口堵塞, 超低碳钢

Abstract: By analyzing on ingredient of nozzle clogging and mechanism of clogging-forming it is obtained, that the nozzle clogging in casting process of Ti-bearing Al-killed ultra-low carbon steel has a hierarchical structure, consisting of a reaction layer and a bonding layer; inside, the reaction layer is caused by the reaction of the acid material in refractory with Al in the steel and the precipitation of inclusions caused by the temperature of molten steel decreasing due to contact with the wall surface of the clogging, while the bonding layer is caused by the accumulation of inclusions accompanied by cold steel； the mass percentage of Al in the bonding layer increases from the inner to the outer layer, and the mass percentage of Ti decreases. By taking such measures as (FeO + MnO) is controlled below 8% by modifying top slags, the mass percent [0] after RH decarburization is controlled within 0. 030% , the tundish argon replacement process before casting is implemented and so on, the number of continuous casting heats of Ti-bearing Al-killed ultra-low carbon steel increases from original 3 to 5, and the nozzle clogging rate has been reduced from original 80% to 30%.

杨克枝, 张乔英, 常正昇. 含Ti铝镇静超低碳钢连铸过程水口堵塞控制实践[J]. 特殊钢, 2020, 41(6): 36-40.

Yang Kezhi, Zhang Qiaoying , Chang Zhengsheng. Practice on Control of Nozzle Clogging in Casting Process of Ti-Bearing Al-Killed Ultra-Low Carbon Steel[J]. Special Steel, 2020, 41(6): 36-40.

参考文献

[1] Wang Min, Bao Yanping and Cui Heng, et al. The Composition and Morphology Evolution of Oxide Inclusions in Ti-Bearing Ultra Low- Carbon Steel Melt Refined in the RH Process [J]. ISU International, 2010, 50(11) ：1606-1611.
[2] Alekseenko A A, Baibekova E V and Kuznetsov S N , et al. Problem of Nozzle Clogging during Continuous Billet Casting of an Aluminum- Killed Low-Carbon Low-Silicon Steel] J]. Russian Metallurgy, 2007 (7) 634-637.
[3]王庆祥，吴雄,喻承欢，等.浸入式水口堵塞的机理及其改善措施[J].钢铁,2005,40(2)：34-36.
[4]Somnath Basu, Shiv Kumar Choudhary and Narendra U Girase. Nozzle Clogging Behaviour of Ti-Bearing Al-Killed Ultra Low Carbon Steel[J], ISU International, 2004 , 44( 10) ： 1653-1660.
[5]Cui Heng, Bao Yanping and Wang Min , et al. Clogging Behavior of Submerged Entry Nozzles for Ti-Bearing IF Steel [ J ]. International Journal of Minerals Metallurgy and Materials T 2010, 17(2)： 154-158.
[6]Jung Woogwang, Kwon Ohduck and Cho Munkyu. Nozzle Clogging Mechanism in Continuous Casting for Titanium-Containing Steel [J]. Korean Journal of Materials Research, 2009 , 19(9) ：473-480.
[7]Kim Wanyi, Jo Jongoh and Changoh Lee, et al. Thermodynamic Relation Between Aluminum and Titanium in Liquid Iron [J]. ISU International, 2008, 48(1) ：17-22.
[8]Long Mujun, Zuo Xiaojun and Zhang Lifeng, et al. Kinetic Modeling on Nozzle Clogging during Steel Billet Continuous Casting [J]. ISU International, 2010, 50(5) ：712-720.
[9]Bernhard C, Xia G and Karasangabo A, et al.超低碳钢连铸过程中Ti和P对水口结瘤的影响[J].世界钢铁,2012,12(5) ：19- 28.
[10]Kaushik P, Kruse D and Ozgu M. Assessment of Castability Issues in Interstitial-Free( IF) Steels[J]. Revue De Metallurgie-Cahiers D Informations Techniques, 2008,105(2) ：92-101.
[11]Mariealine Van Ende, Guo Muxing and Rob Dekkers, et al. Formation and Evolution of Al-Ti Oxide Inclusions during Secondary Steel Refining[J]. ISIJ International, 2009, 49(8) ：1133-1140.
[12]Park Dongchul, Jung Inho and Prter Changhee Rhee, et al. Reoxidation of Al-Ti Containing Steels by CaO-Al₂0₃ -MgO-SiO₂ Slag [J]. ISIJ International, 2004, 44(10):1669-1678.
[13]苑鹏，章军,刘道正，等.超低碳钢中Al-Ti夹杂物的形成机理和控制技术[J].钢铁,2018,53(7):24-30.
[14]Young Seok Lee, Sung Mo Jung and Dong Joon Min. Interfacial Reaction Between Al₂0₃ -SiO₂ -C Refractory and Al/Ti~Killed Steels[J]. ISU International, 2014, 54(4) ：827-835.
[15]赵定国，王育飞，王书桓，等.耐材壁面夹杂物碰撞研究[J].钢铁钒钛,2017,38(6):113-120.