乳化液润滑工艺对冷轧IF钢板表面质量的影响

特殊钢 ›› 2018, Vol. 39 ›› Issue (6): 36-39.

乳化液润滑工艺对冷轧IF钢板表面质量的影响

夏垒¹, 李岩², 张红梅³

1中国石油化工股份有限公司石油化工科学研究院，北京100083；
2海洋装备用金属材料及其应用国家重点实验室鞍钢集团钢铁研究院，鞍山H4009；
3辽宁科技大学材料与冶金学院，鞍山114051

收稿日期:2018-06-12 出版日期:2018-12-01 发布日期:2022-05-25
作者简介:夏垒(1988-),男，博士研究生(石油化工科学研究院)， 2011年燕山大学(本科)毕业，摩擦磨损，润滑技术和表面质量研究。
基金资助:
国家自然科学基金项目(51474127；51671100)資助

Effect of Emulsion Lubrication Process on Surface Quality of Cold Rolled IF Steel Plate

Xia Lei¹, Li Yan² , Zhang Hongmei³

1 Research Institute of Petroleum Processing, SINOPEC, Beijing 100083 ；
2 State Key Laboratory of Metal Material for Marine Equipment and Application, Iron & Steel Research Institutes of Ansteel Group Corporation, Anshan 114009 ；
3 Department of Material and Metalling, University of Science and Technology liaoning, Anshan 114051

Received:2018-06-12 Published:2018-12-01 Online:2022-05-25

摘要/Abstract

摘要： 分析了无润滑和釆用两种不同乳化液润滑轧后IF钢板表面质量，并通过对乳化液摩擦学性能分析研究了造成轧后表面质量差异的原因。研究发现，釆用乳化液润滑可以使轧后钢板表面更加平整、光滑，改善表面质量;LP-2润滑时轧后钢板表面质量比使用LP-1润滑时更好，主要是因为LP-2乳化液其油膜强度更高，润滑过程中油膜更加稳定，抗磨减摩效果更好。

Abstract: The surface quality of the IF steel strips rolled without lubrication and with two different emulsions lubrication was analyzed, and the reasons for the difference of surface quality lubricated by different emulsions were studied by analyzing the tribological properties of emulsions. The results showed that the lubrication of emulsions in cold rolling process could make the steel strip surface more smooth and improve the surface quality. The reason for the better surface quality of the steel strip lubricated by LP-2 than lubricated by LP-1 is mainly that the LP-2 emulsion had higher oil film strength which could form more stable oil film in the lubrication process, and get better anti-friction and anti-wear effects.

夏垒, 李岩, 张红梅. 乳化液润滑工艺对冷轧IF钢板表面质量的影响[J]. 特殊钢, 2018, 39(6): 36-39.

Xia Lei, Li Yan , Zhang Hongmei. Effect of Emulsion Lubrication Process on Surface Quality of Cold Rolled IF Steel Plate[J]. Special Steel, 2018, 39(6): 36-39.