硼对780 MPa低碳贝氏体钢组织和力学性能的影响

特殊钢 ›› 2018, Vol. 39 ›› Issue (2): 65-67.

硼对780 MPa低碳贝氏体钢组织和力学性能的影响

赵燕青¹，孙力¹，刘宏强¹，王九清²，安会龙¹，罗应明²，车金锋²

1河钢集团钢研总院,石家庄050023；
2河钢集团舞钢公司,平顶山462500

收稿日期:2017-10-30 出版日期:2018-04-01 发布日期:2022-07-04
作者简介:赵燕青(1984-)，男，硕士(2011年北京科技大学)，工程师，2008年河北工业大学(本科)毕业，轧钢工艺及金属热处理研究。

Effect of Boron on Structure and Mechanical Properties of 780 MPa Low Carbon Bainite Steel

Zhao Yanqing¹, Sun Li¹ , Liu Hongqiang¹, Wang Jiuqing², An Huilong¹, Luo Yingming², Che Jinfeng²

1 General Research Institute, Hesteel Group, Shijiazhuang 050023 ；
2 Wuyang Iron and Steel Co Ltd, Hesteel Group, Pingdingshan 462500

Received:2017-10-30 Published:2018-04-01 Online:2022-07-04

摘要/Abstract

摘要： 试验低碳贝氏体钢（/%:0.08C,0.11~0.13Si,1.10~1.20Mn,0.008~0.009P,0.002S,0.21~0.23Ni,0.020~0.021Ti,0.003~0.004Nb,0~0.0010B,0.000 7~0.0008O,0.0031~0.0033N）由50kg真空感应炉熔炼,轧成45mm钢板,并经930℃淬火,610℃回火。研究了0.0010%硼对780 MPa低碳贝氏体钢45mm板组织和力学性能的影响。结果表明,硼可显著提高试验钢的淬透性,不含硼试验钢淬火后得到粒状贝氏体,0.0010%硼试验钢淬火后得到板条贝氏体。硼明显改善试验低碳贝氏体钢的力学性能,含0.0010%硼试验钢淬、回火后的抗拉强度834MPa和屈服强度771MPa远高于不含硼试验钢的抗拉强度702MPa和屈服强度591MPa,实际生产中应加入适量硼可使低碳贝氏体钢得到板条贝氏体。

关键词: 硼, 低碳贝氏体钢, 组织, 力学性能

Abstract: The tested low carbon bainite steel (/%: 0.08C, 0.11~0.13Si, 1.10~1.12Mn, 0.008〜0.009P, 0.002S, 0.21~0.23Ni, 0.020~0.021Ti, 0.003〜0.004Nb, 0~0.0010B, 0.0007~0.0008O, 0.0031~0.0033N) is melted by a 50kg vacuum induction furnace, rolled to 45mm plate, quenched at 930℃ and tempered at 610°C. The effect of 0.0010% boron on structure and mechanical properties of 45mm plate of 780MPa low carbon bainite steel has been studied. Results show that boron can remarkably improve the hardenability of tested steel, the structure of quenched tested steel without bearing boron is granular bainite, and the structure of quenched 0.0010% boron tested steel is lath bainite. The boron can obviously improve the mechanical properties of tested low carbon bainite steel, the tensile strength 834MPa and yield strength 771MPa of quenched-tempered bearing 0.0010% boron tested steel is higher than the tensile strength 702MPa and yield strength 591MPa of quenched-tempered without bearing boron tested steel. Adding suitable boron in steel in practical production the low carbon bainite steel can get lath bainite structure.

赵燕青, 孙力, 刘宏强, 王九清, 安会龙, 罗应明, 车金锋. 硼对780 MPa低碳贝氏体钢组织和力学性能的影响[J]. 特殊钢, 2018, 39(2): 65-67.

Zhao Yanqing, Sun Li , Liu Hongqiang, Wang Jiuqing, An Huilong, Luo Yingming, Che Jinfeng. Effect of Boron on Structure and Mechanical Properties of 780 MPa Low Carbon Bainite Steel[J]. Special Steel, 2018, 39(2): 65-67.

[1]	孟庆勇, 单庆林, 潘宏伟, 路博勋, 石晓伟, 温巨文. 高铬耐候钢Q350EW高温热塑性分析 [J]. 特殊钢, 2024, 45(6): 23-27.
[2]	张艳梅, 余海存, 仇秋玲. 固溶工艺对3Al-310S耐热钢组织和力学性能的影响[J]. 特殊钢, 2024, 45(6): 95-101.
[3]	赵广迪, 臧喜民, 刘志超, 井玉安. 淬火工艺对A514CrQ齿条钢显微组织演变及硬度的影响[J]. 特殊钢, 2024, 45(6): 73-82.
[4]	徐临超, 叶赛男, 王文权, 张新戈, 陆有, 郭威. 热处理工艺对锻造430F铁素体不锈钢组织和性能的影响[J]. 特殊钢, 2024, 45(6): 83-87.
[5]	袁麟, 胡小强, 刘洋, 李殿中, 谢晶, 陈伟. 稀土精炼与电渣重熔3%Cr轧辊钢对比分析[J]. 特殊钢, 2024, 45(5): 1-7.
[6]	唐远寿, 张十庆, 李方, 何钦生, 赵振, 王宏, 邹兴政, 王建桥, 黄雅丽. 淬火温度对M₆C强化2 200 MPa级超高强度钢力学性能的影响[J]. 特殊钢, 2024, 45(5): 108-112.
[7]	张明. 显微组织对薄壁X65M管线钢落锤试验性能的影响[J]. 特殊钢, 2024, 45(5): 123-126.
[8]	徐烨玲, 王冲, 侯翔益, 黄嘉良, 廉心桐, 黄烁. GH4706合金涡轮盘锻件不同部位的组织及高温力学性能[J]. 特殊钢, 2024, 45(5): 102-107.
[9]	李晴. 固溶温度对GH4163合金显微组织及拉伸性能的影响[J]. 特殊钢, 2024, 45(5): 97-101.
[10]	李阳, 赵广迪, 臧喜民, 姜昊源, 王兆宇. B对Fe-Cr-B-C合金热处理后显微组织和强韧性的影响[J]. 特殊钢, 2024, 45(5): 25-33.
[11]	李建平, 唐正友, 张翰文, 邓通武. Si对缆索钢丝绳用热轧盘条组织和力学性能的影响[J]. 特殊钢, 2024, 45(5): 19-24.
[12]	袁志钟, 陈露, 张伯承, 刘海明, 牛宗冉, 王致远, 鞠玉琳, 程晓农. LB/M复相热处理工艺对冷作模具钢DC53组织和力学性能的影响[J]. 特殊钢, 2024, 45(4): 153-160.
[13]	孙中豪, 李强, 张明亮, 马程款, 夏志斌, 钟云波. 磁控电渣重熔对M2高速钢凝固组织及力学性能的影响[J]. 特殊钢, 2024, 45(4): 68-76.
[14]	张宏, 李旭, 陈华, 唐琴, 李林森, 王立, 高首磊. 热处理工艺对140 ksi等级In718合金组织与性能的影响[J]. 特殊钢, 2024, 45(4): 139-145.
[15]	范晓烁, 刘玉峰, 袁华. 粉末处理对FGH95氧含量、微观组织及力学性能的影响[J]. 特殊钢, 2024, 45(4): 124-130.