70tBOF-LF-VD-CC-HR流程试制磨球钢80MnCr棒材的开发

特殊钢 ›› 2017, Vol. 38 ›› Issue (3): 37-40.

70tBOF-LF-VD-CC-HR流程试制磨球钢80MnCr棒材的开发

刘发友^1,2，王国承¹，汪琦¹，田钱仁¹，毛福来²

1辽宁科技大学材料与冶金学院，鞍山 114051 ；
2山东寿光巨能特钢有限责任公司，寿光 262700

收稿日期:2016-12-17 出版日期:2017-06-01 发布日期:2022-07-20
作者简介:刘发友(1970-),男，博士生,1993年山东大学(本科)毕业,特殊钢冶金研究。

Development of 80MnCr Steel Bar for Grinding Ball by 70t-BOF-LF-VD-CC-HR Flowsheet

Liu Fayou^1,2, Wang Guocheng¹, Wang Qi¹, Tian Qianren¹，Mao Fulai²

1 School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051;
2 Shandong Shouguang Juneng Special Steel Co Ltd, Shouguang 262700

Received:2016-12-17 Published:2017-06-01 Online:2022-07-20

摘要/Abstract

摘要： 试制的80MnCr钢（/%:0.79~0.81C,0.92~0.97Mn,0.26~0.32Si,0.009~0.017P,≤0.005S,0.92~0.97Cr,0.06Mo,0.03~0.05Ti,0.027~0.032Al,0.00040~0012O）的生产流程为BF-70t BOF-LF-VD-Φ450mm圆坯连铸-Φ90mm棒材轧制。通过控制BOF终点[P]≤0.015%,终点[C]≥0.12%,出钢用1.5kg/t钢芯铝预脱氧、LF喂铝线脱氧,精炼渣碱度≥4,VD后喂钙线,连铸结晶器和末端电磁搅拌等工艺措施,钢中非金属夹杂物级别为:粗系0、细系≤0.5;低倍组织级别为:中心疏松≤1.5、一般疏松≤0.5、中心偏析≤0.5、锭型偏析0;钢材经超声波无损探伤检测,合格率达93.07%。

关键词: 80MnCr磨球钢, 70t BOF-LF-VD-CC流程, 低倍组织, 非金属夹杂, 超声波探伤

Abstract: The production flowsheet of pilot-produced steel 80MnCr (/%: 0.79~0.81C, 0.92~0.97Mn, 0.26~0.32Si, 0.009~0.017P, ≤0.005S, 0.92~0.97Cr, 0.06Mo, 0.03~0.05Ti, 0.027~0.032Al, 0.0004~0.0012O) is BF-70t BOF-LF-VD-Φ450mm Round bloom casting-rolling to Φ90mm bar. With the process measures including controlling BOF end [P]≤0.015% and end [C]≥0.12% , pre-deoxidizing with 1.5kg/t steel cored aluminium at tapping, deoxidation by feeding aluminium wire in LF, refining slag basicity N4, after VD feeding calcium wire, mold-EMS and end-EMS in casting, the rating units of inclusions in steel are heavy series 0 and thin series ≤0.5, the rating of macrostructure are central porosity ≤1.5, general porosity ≤0.5, central segregation ≤0.5 and ingot square-segregation zone 0； and the qualified rate of steel products by ultrasonic nondestructive measuring is up to 93.07%.

Key words: 80MnCr Steel for Grinding Ball, 70t BOF-LF-VD-CC Flowsheet, Macrostructure, Nonmetallic Inclusions, Ultrasonic Detection

刘发友, 王国承, 汪琦, 田钱仁, 毛福来. 70tBOF-LF-VD-CC-HR流程试制磨球钢80MnCr棒材的开发[J]. 特殊钢, 2017, 38(3): 37-40.

Liu Fayou, Wang Guocheng, Wang Qi, Tian Qianren, Mao Fulai. Development of 80MnCr Steel Bar for Grinding Ball by 70t-BOF-LF-VD-CC-HR Flowsheet[J]. Special Steel, 2017, 38(3): 37-40.

[1]	袁麟, 胡小强, 刘洋, 李殿中, 谢晶, 陈伟. 稀土精炼与电渣重熔3%Cr轧辊钢对比分析[J]. 特殊钢, 2024, 45(5): 1-7.
[2]	刘烨, 桂煜琳, 尹青, 吴小林, 缪新德. 机器人谐波减速机柔性轴承用钢的超高旋转弯曲疲劳强度的研究[J]. 特殊钢, 2024, 45(3): 105-113.
[3]	尉文超, 谢地荣, 时捷, 王毛球. S含量对18CrNiMo7-6齿轮钢中夹杂物和疲劳性能的影响[J]. 特殊钢, 2024, 45(1): 111-116.
[4]	韩顺, 厉勇, 赵肃武, 王瑞, 孙勇, 李建新, 王春旭. 商用飞机起落架用单真空300M钢疲劳性能控制现状及展望[J]. 特殊钢, 2023, 44(5): 53-59.
[5]	尹青, 曹文全, 吴小林, 王存宇, 王辉, 俞峰. 高洁净轴承钢GCr15滚动接触疲劳机制研究[J]. 特殊钢, 2023, 44(5): 113-120.
[6]	夏云峰, 周仲成, 胡永平, 林雨. WB36厚壁无缝钢管低倍组织气泡分析及工艺研究[J]. 特殊钢, 2023, 44(2): 29-32.
[7]	屠兴圹, 徐建飞, 周淼, 苏振伟, 林俊, 万文华. 低碳铝脱氧20钢钢水洁净度控制研究[J]. 特殊钢, 2022, 43(3): 35-38.
[8]	屠兴圹, 徐建飞, 杨成威, 苏振伟, 黄云飞. BOF-RH-CC与BOF-LF-CC流程对冷镦钢ML08Al洁净度的影响[J]. 特殊钢, 2022, 43(3): 56-59.
[9]	飞尚才, 蒋小霞, 苟宁年, 徐楠. CSP生产DQ深冲低碳钢连铸薄板坯中非金属夹杂物研究[J]. 特殊钢, 2020, 41(4): 37-39.
[10]	卢乃双, 梁娜, 黄涛. 25MnBM履带板用钢非金属夹杂物控制工艺研究[J]. 特殊钢, 2020, 41(3): 25-27.
[11]	邢国成, 刘桂江, 李涛, 程丽杰, 孙大利. 超声波探伤不合格T91钢棒材的分析和工艺改进[J]. 特殊钢, 2019, 40(3): 8-12.
[12]	刘兵. 40%铁水-50 t EAF-LF-VD-CC流程16MnCr5齿轮钢的开发[J]. 特殊钢, 2019, 40(2): 42-45.
[13]	谢志彬, 邵青立, 张国平, 王凯, 何宁. 酸性渣重熔含硫高速钢M35的质量研究[J]. 特殊钢, 2019, 40(1): 27-30.
[14]	卫争艳, 史普辑. 2Cr12NiMo1WlV不锈钢Φ180mm棒材低倍中心黑色区缺陷分析和退火工艺改进[J]. 特殊钢, 2018, 39(2): 44-46.
[15]	李德军, 李泽林, 赵志刚, 许孟春, 李晓伟, 于赋志. 单辊轻压下对高碳钢SWRH72B 180mmx180mm铸坯内部质量的影响[J]. 特殊钢, 2017, 38(6): 33-36.