碱度对连铸保护渣结晶率的影响

特殊钢 ›› 2017, Vol. 38 ›› Issue (2): 6-10.

碱度对连铸保护渣结晶率的影响

王杏娟¹，樊亚鹏¹，朱立光¹，王立杰²，李曜光²

1. 华北理工大学冶金与能源学院河北省现代冶金技术重点实验室河北省高品质钢连铸工程技术研究中心，唐山 063009；
2. 河北钢铁集团唐山钢铁集团有限公司，唐山 063016;

收稿日期:2016-10-19 出版日期:2017-04-01 发布日期:2022-07-20
作者简介:王杏娟(1978-)，女，博士(2013年北京科技大学)，副教授， 2002年河北理工学院(本科)毕业，连铸保护渣相关研究。
基金资助:
国家自然科学青年基金项目(51404088);
河北省自然科学基金项目(E2015209217)资助;

Influence of Basicity on Crystallization Rate of Mold Flux for Continuous Casting

Wang Xingjuan¹ , Fan Yapeng¹ , Zhu Liguang¹ , Wang Lijie² , Li Yaoguang²

1. Key Laboratory for Advanced Metallurgy Technology and High Quality Steel Continuous Casting Engineering Technology Research Center of Hebei Province, College of Metallurgy and Energy Source, North China University of Science and Technology, Tangshan 063009；
2. Tangshan Iron and Steel Co, Hebei Iron and Steel Group, Tangshan 063016;

Received:2016-10-19 Published:2017-04-01 Online:2022-07-20

摘要/Abstract

摘要： 连铸保护渣玻璃体渣膜回温结晶现象对渣膜的热阻有重要影响。采用SHTT-Ⅱ型熔化结晶温度测定仪并结合金相显微镜,研究碱度（R 0.8~1.4）对保护渣（/%:28.22~49.73CaO，35.52SiO₂，4.00Na₂O，2.14MgO，14.55Al₂O₃，0.72TiO₂，0.93Fe₂O₃，0.32K₂O，0.32MnO₂，2.03CaF₂，6.18C）的结晶率的影响,构建了TTT曲线,计算了不同碱度下保护渣形核活化能,观察了在800,900,1000℃回温处理下不同碱度保护渣表面形貌。实验结果表明,随着碱度增加保护渣结晶温度和形核活化能不断降低;随着玻璃体渣膜回温处理温度的升高,玻璃渣膜表面出现凸起、凹坑以及大量的内部缺陷;提出合适的碱度范围为:低碳钢0.80~0.95,中碳钢≥1.2,高碳钢0.75~0.90。

关键词: 连铸, 结晶器, 渣膜, 碱度, SHTT热丝法, 结晶率

Abstract: The crystallization phenomenon of continuous casting mold flux vitreous membrane in reversion-heating process has important influence on thermal resistance of flux film. The influence of basicitv (R 0.8~1.4) on crystallization rate of casting mold flux (/% ：28.22〜49.73CaO, 35.52SiO₂, 4.00Na₂O, 2.14MgO, 14.55A1₂O₃, 0.72TiO₂, 0.93Fe₂O₃, 0.32K₂O, 0.32MnO₂, 2.03CaF₂, 6.18C) has been studied by using the SHTT-II melting crystallizing temperature measuring instrument and metallographic microscope to establish the TTT curves, the nucleation activation energy of mold flux with different basicity is calculated and the morphology of surface of mold flux with different basicity reversionheating at 800 °C , 900 °C and 1000 °C is observed. The test results show that with increasing basicity the recrystallization temperature of mold flux and the nucleation activation energy continuously decrease ； with reversion-heating temperature rise of vitreous flux film, the bulges and pits at surface and a mass of defects in inner of film occur. The suitable range of basicity of flux is put forward that is 0.80~0.95 for low carbon steel,≥l.2 for medium-carbon steel and 0.75〜0.90 for high carbon steel.

Key words: Continuous Casting, Mold, Flux film, Basicity, Single Hot Thermocouple Technique ( SHTT), Crystallization Rate

王杏娟, 樊亚鹏, 朱立光, 王立杰, 李曜光. 碱度对连铸保护渣结晶率的影响[J]. 特殊钢, 2017, 38(2): 6-10.

Wang Xingjuan , Fan Yapeng , Zhu Liguang , Wang Lijie , Li Yaoguang. Influence of Basicity on Crystallization Rate of Mold Flux for Continuous Casting[J]. Special Steel, 2017, 38(2): 6-10.

参考文献

[1] Hooli P 0. Mould Flux Film Between Mould and Steel Shell [J]. Ironmaking and Steelmaking, 2002, 29, (4)：293-296.
[2] 韩秀丽，张均，刘磊，等.连铸保护渣渣膜矿相结构对不同钢种板坯冶金质量的影响[J].特殊钢，2016, 37,(1)：6467
[3] 朱立光，李曜光，王杏娟，等.连铸保护渣脱玻化行为研究[J].钢铁钒钛，2015,36(4):94-100.
[4] Hou Le Jun, Wang Wan Lin, ZHou Ke Chao. Viscosity and Crystallization Behavior of F-free Mold Flux for Casting Medium Carbon Steels [J]. ISIJ International, 2015 ,55(9):1916-1924.
[5] 申俊峰，庞智杰.结晶器保护渣渣膜的研究[J].炼钢,1998,14(4):31-33.
[6] Mizuno Hidenori, Esaka Hisao, et al. Analysis of the Crystallization of Mold Flux for Continuous [J]. ISIJ International, 2008, 48(3):277-285.
[7] 董方，王艺慈，王宝峰.高速连铸结晶器保护渣渣膜凝固结晶组织研究[J].炼钢，2006,22(5)：4346.
[8] 赵紫锋，张炯明，王新华，等.中碳钢板坯保护渣玻璃质渣膜脱玻化[J],钢铁研究学报，2009, 21(11)：16-19.
[9] 杨秋红，姜中宏.玻璃析晶动力学判据研究[J].硅酸盐学报，1994, 22(5):1419-426.
[10] 沈铁.碱度对CaO-SiO₂-Al₂O₃-CaF₂-Na₂O保护渣结晶性能的影响[J].金属铸锻焊技术,2010,39(21):38-40. [11] 刘慧，文光华，唐萍.碱度对CaO-SiO₂-CaF₂-Na₂O四元渣系结晶临界冷却速度和孕育时间的影响[J].过程工程学报，2008 , 8(1)：266-270.
[12] 饶东生.硅酸盐物理化学(第1版)[M].北京：冶金工业出版，1986.
[13] 迟景颇，甘永年.连铸保护渣[M].沈阳：东北大学出版社, 1993.
[14] 朱立光，王杏娟.连铸保护渣理论与实践[M].北京:冶金工业出版社，2015.
[15] 李玉娣，江中块.梅钢2号连铸机包晶钢保护渣的优化与应用[J].梅钢科技，2010(2):26-28.
[16] 刘风云，张一夫.连铸高碳钢坯凝固基础理论探索[J].炼钢，1993, 9(4)：56-59,
[17] 周青峰，马建超，王敏花等，高碳钢小方坯粘结漏钢形成原因分析与控制[J],炼钢，2015,31(5):66-69.