特殊钢 ›› 2017, Vol. 38 ›› Issue (3): 61-65.

100tBOF-LF-RH-CC流程冶炼GCr15轴承钢非金属夹杂的演变

刘佳伟¹，岳峰²，王子健³

1.北京科技大学1工程技术研究院,
2钢铁共性技术协同创新中心，北京100083；
3江苏沙钢集团淮钢特钢股份有限公司总工办，淮安223002

收稿日期:2016-12-05 出版日期:2017-06-01 发布日期:2022-07-22
作者简介:刘佳伟(1990-),男，硕士研究生,2014年华北理工大学(本科)毕业,RH工艺冶炼高品质轴承钢夹杂物控制；岳峰，高级工程师。

Evaluation of Nonmetallic Inclusions in Bearing Steel GCr15 Steelmaking by 100t BOF-LF-RH-CC Flowsheet

Liu Jiawei¹, Yue Feng², Wang Zijian³

1 Institute of Engineering Technology,
2 Collaborative Innovation Center of Steel Technology, University of Science and Technology,Beijing 100083;
3 Chief Engineer Office, Huaigang Special Steel Co Ltd, Jiangsu Shagang Group, Huai'an 223002

Received:2016-12-05 Published:2017-06-01 Online:2022-07-22

摘要/Abstract

摘要： 试验GCr15轴承钢（/%:1.00C,0.20Si,0.39Mn,0.015P,0.005S,1.50Cr,0.003Ti,0.015Als）的冶炼工艺流程为预脱硫铁水-100t BOF-LF-RH-200mm×200mm坯连铸。主要工艺特点为BOF出钢过程加1.2kg/t铝脱氧,LF精炼采用白渣操作,精炼初渣主要成分为（/%:22Al₂O₃,56CaO,10SiO₂,5MgO）,RH67Pa,25min,连铸过程保护浇注。两炉钢冶炼分析结果表明,钢中氧氮含量在RH破空样品中同时达到最低分别为7×10^-6~8×10^-6和24×10^-6~26×10^-6,钢中非金属夹杂尺寸主要集中在3~8μm,并且单位面积夹杂物数量在RH破空样中达到最小;铸坯中非金属夹杂以Al₂O₃-CaO夹杂为主;在高碱度渣的条件下,钙铝酸盐与镁铝尖晶石很容易发生反应,碱度为2~3时会出现少量MgO-Al₂O₃,在渣碱度达到4以上时不会出现MgO-Al₂O₃系夹杂物,并且高碱度条件下MgO-Al₂O₃-CaO系夹杂物中MgO含量会降低。

关键词: 100t BOF-LF-RH-CC流程, 轴承钢GCr15, 夹杂物, 尺寸, 成分, 演变

Abstract: The steelmaking flowsheet of tested bearing steel GCr15 (/%: 1.00C, 0.20Si, 0.39Mn, 0.015P, 0.005S, 1.50Cr, 0.003Ti, 0.015Als) is pre-desulphurized hot metal-100t BOF-LF-RH-200mmX200mm billet casting. The main process characteristics are adding 1.2kg/t aluminium for pre-deoxidation in BOF tapping, using white slag operation in LF refining with initial slag main ingredient (/%: 22Al₂O₃,56CaO, 10SiO₂, 5MgO), RH 67Pa for 25min and shield casting in cast process. Analysis results of two heats malting show that the oxygen and nitrogen content in liquid at end RH are lowest respectively 7X10^-6~8x10^-6 and 24x10^-6~26x10^-6, the size of majority inclusions in steel is 3~8μm, and the number of inclusions in steel at unit area is lowest at end RH, and the main nonmetallic inclusions in cast billet are Al₂O₃-CaO; with condition of high basicity refining slag the calcium aluminate easily reacts with magnesiumaluminum spinel, with slag basicity 2~3 the small amount of MgO-Al₂O₃ occurs and with slag basicity more than 4 the MgO-Al₂O₃ series inclusions don't occur, besides with condition of high basicity the MgO content in MgO-Al₂O₃-CaO series inclusions is able to decrease.

刘佳伟, 岳峰, 王子健. 100tBOF-LF-RH-CC流程冶炼GCr15轴承钢非金属夹杂的演变[J]. 特殊钢, 2017, 38(3): 61-65.

Liu Jiawei, Yue Feng, Wang Zijian. Evaluation of Nonmetallic Inclusions in Bearing Steel GCr15 Steelmaking by 100t BOF-LF-RH-CC Flowsheet[J]. Special Steel, 2017, 38(3): 61-65.

[1]	倪卓文, 朱红春, 李花兵, 姜周华, 孙正鑫, 何志禹. H13模具钢电渣锭中夹杂物的类型以及分布规律分析[J]. 特殊钢, 2024, 45(6): 48-52.
[2]	王利, 刘成宝, 李浩秋, 王毅, 孙宗辉, 刘春伟, 杨超云, 付志豪. 稀土对20CrMnTi齿轮钢夹杂物和疲劳性能的影响[J]. 特殊钢, 2024, 45(6): 117-124.
[3]	谢康, 莫金强, 张威, 王丽君. 稀土Ce对441铁素体不锈钢碳氮化物析出的影响与控制[J]. 特殊钢, 2024, 45(6): 1-7.
[4]	郑安民, 樊轩宇, 黄增鑫, 毛旺旺, 于彦冲, 张金玲, 王社斌. 稀土Ce对20MnTiB冷镦钢中夹杂物演变的影响[J]. 特殊钢, 2024, 45(6): 37-47.
[5]	赵广迪, 臧喜民, 刘志超, 井玉安. 淬火工艺对A514CrQ齿条钢显微组织演变及硬度的影响[J]. 特殊钢, 2024, 45(6): 73-82.
[6]	赵昊乾, 张育明, 马博, 巩延杰, 孟耀青. LF精炼结束后软吹时间对帘线钢LX82 A夹杂物控制的影响[J]. 特殊钢, 2024, 45(6): 53-56.
[7]	袁麟, 胡小强, 刘洋, 李殿中, 谢晶, 陈伟. 稀土精炼与电渣重熔3%Cr轧辊钢对比分析[J]. 特殊钢, 2024, 45(5): 1-7.
[8]	赵吉庆, 万五霞, 李造宇, 杜丽萍. 125ksi超级马氏体油管成分-组织-性能-工艺综合控制技术[J]. 特殊钢, 2024, 45(5): 40-46.
[9]	唐远寿, 张十庆, 李方, 何钦生, 赵振, 王宏, 邹兴政, 王建桥, 黄雅丽. 淬火温度对M₆C强化2 200 MPa级超高强度钢力学性能的影响[J]. 特殊钢, 2024, 45(5): 108-112.
[10]	张明. 显微组织对薄壁X65M管线钢落锤试验性能的影响[J]. 特殊钢, 2024, 45(5): 123-126.
[11]	杨建华, 巨银军, 杨俊. 帘线钢XLX72 A中氧化物夹杂的演变解析与去除[J]. 特殊钢, 2024, 45(5): 66-71.
[12]	刘泳, 张雲飞, 赵英利, 赵楠, 赵峥嵘, 樊明强, 田志强. 改善模具钢洁净度与抛光性能的冶炼工艺实践[J]. 特殊钢, 2024, 45(5): 47-52.
[13]	曹玉龙, 张赛康, 汪秀秀, 马崇圣, 李光强. 加热温度对高钒高速钢中M₂C碳化物分解转变行为的影响[J]. 特殊钢, 2024, 45(4): 146-152.
[14]	杨曙磊, 王曦伟, 田强, 王田田, 杨树峰. GH4742合金真空自耗铸锭中夹杂物分布特征[J]. 特殊钢, 2024, 45(4): 61-67.
[15]	孙中豪, 李强, 张明亮, 马程款, 夏志斌, 钟云波. 磁控电渣重熔对M2高速钢凝固组织及力学性能的影响[J]. 特殊钢, 2024, 45(4): 68-76.