石灰活性和微观结构对铁水脱磷的影响

特殊钢 ›› 2016, Vol. 37 ›› Issue (5): 10-13.

石灰活性和微观结构对铁水脱磷的影响

薄荷¹，董建君¹，任倩倩²，张玉柱^2,3，郝素菊³，蒋武锋³，郝华强²

1. 唐山科技职业技术学院冶金工程系，唐山 063000；
2. 东北大学冶金学院，沈阳 110004；
3. 华北理工大学冶金与能源学院，唐山 063009;

收稿日期:2016-04-11 出版日期:2016-10-01 发布日期:2022-07-28
通讯作者: 郝素菊，张玉柱
作者简介:薄荷(1983-)，女，硕士(2014年华北理工大学)，讲师， 2006年内蒙古科技大学(本科)毕业，炼钢、冶金动力研究。
基金资助:
国家自然科学基金项目(51174075,51274084)；
河北省自然科学基金项目(E2014209157)；

Effect of Activity and Microstructure of Lime on Dephosphorization of Hot Metal

Bo He¹ , Dong Jianjun¹ , Ren Qianqian² , Zhang Yuzhu^2,3 , Hao Suju³ , Jiang Wufeng³ , Hao Huaqiang²

1. Department of Metallurgical Engineering, Tangshan Vocational College of Science and Technology, Tangshan 063000；
2. School of Metallurgy, Northeastern University, Shenyang 110004;
3. College of Metallurgy and Energy, North China University of Science and Technology, Tangshan 063009;

Received:2016-04-11 Published:2016-10-01 Online:2022-07-28
Contact: Hao Suju ,Zhang Yuzhu

摘要/Abstract

摘要： 通过管式电阻炉,用工业铁块、磷铁和硫化亚铁配制0.40%P试验用铁水,造渣剂石灰:萤石=9:1,造渣剂与铁水的比例为1:50,熔融温度1600℃。采用场发射扫描电镜和全自动压汞仪研究了石灰的微观结构-比表面积（1.05~4.75 m²/g）、平均孔径（605~1404 nm）、孔容积（0.23~0.78 mL/g）、体积密度（0.80~3.10 g/cm³）和活性度（298~350 mL）对铁水脱磷的影响。结果表明,随着石灰活性度的增加,铁水脱磷率逐渐增加;随着比表面积、平均孔径、孔容积和体积密度的增加铁水的脱磷率均先增加后降低,当石灰比表面积2.5 m²/g,平均孔径750~850 nm,孔容积0.45~0.55 mL/g,体积密度2.0 g/cm³时铁水的脱磷率达到最好,其铁水脱磷率达到63.0%。

关键词: 石灰, 活性度, 微观结构, 脱磷率

Abstract: The tested hot metal containing 0.40% P is made from commercial iron, phosphoric iron and ferrous sulfide with slagging forming material lime : fluorite =9 ：1 and slagging forming material : metal = 1 ：50, and melted at 1600℃. by a tube-type electric resistance furnace. The effect of the microstructure of lime-specific surface area (1.05~4.75 m²/ g) , average pore diameter (605~ 404 nm) , pore volume (0.23~0.78 mL/g) and bulk density (0.80~3.10 g/cm³), and the activity of lime (298~350 mL) on dephosphorization of hot metal has been studied by field emission SEM and automatic pressure mercury device. Results show that with increasing the activity of lime the dephosphorization ratio increases gradually ； with increasing the specific surface area, average pore diameter, pore volume and bulk density, the dephosphorization ratio of metal increases first and then decreases ； with lime specific surface area 2.5 m²/g, average pore diameter 750~850 nm, pore volume 0.45 ~0.55 mL/g and bulk density 2.0 g/cm³, the dephosphorization ratio of metal is highest, it is up to 63.0%.

Key words: Lime, Activity, Microscopic Structure, Dephosphorization Rate

薄荷, 董建君, 任倩倩, 张玉柱, 郝素菊, 蒋武锋, 郝华强. 石灰活性和微观结构对铁水脱磷的影响[J]. 特殊钢, 2016, 37(5): 10-13.

Bo He , Dong Jianjun , Ren Qianqian , Zhang Yuzhu , Hao Suju , Jiang Wufeng , Hao Huaqiang. Effect of Activity and Microstructure of Lime on Dephosphorization of Hot Metal[J]. Special Steel, 2016, 37(5): 10-13.

[1]	马少晨, 袁志鹏, 张彩军. 高拉速薄板坯保护渣剪切变稀行为和表面性质[J]. 特殊钢, 2024, 45(5): 76-84.
[2]	陈君, 苏春阳, 姜亚清. 基于多元线性回归的转炉石灰加入量计算模型[J]. 特殊钢, 2024, 45(1): 42-47.
[3]	邸天成, 王杏娟, 刘增勋, 翟俊, 李欢, 朴占龙. 430不锈钢用连铸保护渣渣圈形成长大机理分析和控制措施[J]. 特殊钢, 2022, 43(5): 63-67.
[4]	李小明. 渗硼工艺对汽车用45CrNiMoV热锻模具钢性能的影响[J]. 特殊钢, 2021, 42(1): 57-60.
[5]	高琦, 智建国, 吴伟, 张志兵, 张晓峰, 关键. 100t 转炉留渣双渣法冶炼高硅高磷铁水试验[J]. 特殊钢, 2020, 41(6): 41-45.
[6]	吴明, 杨芳, 吕鸣. 复合喷吹石灰与镁粉配比对铁水脱硫效果的影响[J]. 特殊钢, 2018, 39(5): 18-20.
[7]	李晨晓, 郝华强, 王书桓, 赵定国, 陈建军, 刘善喜. 唐钢60t转炉石灰石替代部分石灰造渣炼钢的工业试验[J]. 特殊钢, 2017, 38(6): 16-18.
[8]	郝素菊, 兰吉然, 蒋武锋, 张玉柱, 郝华强. 渣料中石灰活性度对铁水脱硫的影响[J]. 特殊钢, 2017, 38(2): 16-18.
[9]	郝华强, 崔鹏辉, 蒋武锋, 郝素菊, 张玉柱. 活性石灰对造渣速率的影响[J]. 特殊钢, 2016, 37(4): 1-4.
[10]	郝赳赳, 李宏, 胡龙飞, 李晨晓. 60 t转炉石灰石替代石灰造渣脱磷的试验研究[J]. 特殊钢, 2016, 37(3): 28-30.
[11]	郝华强, 任倩倩, 张玉柱, 郝素菊, 蒋武锋, 张卫攀. 石灰微观结构对铁水预处理脱硫的影响[J]. 特殊钢, 2016, 37(2): 16-18.
[12]	秦登平, 杨建平, 危尚好, 张建师, 孙剑光, 刘金旭. 100 t 顶吹氧气转炉石灰石造渣炼钢技术的分析和工艺实践[J]. 特殊钢, 2014, 35(5): 34-36.
[13]	解英明. 石灰石作为120 t顶底复吹转炉终点钢水调温剂的生产应用[J]. 特殊钢, 2013, 34(5): 44-46.
[14]	俞海明, 解英明, 陈跃军, 段建勇, 胡永胜, 兰飞鹏, 李栋, 王瑞利. 70 t电弧炉热兑转炉液态渣的工艺实践[J]. 特殊钢, 2012, 33(4): 36-38.
[15]	张羡夫, 方岩, 杨艳玲. 石灰基铁水预脱硫剂最佳配方和用量的试验研究[J]. 特殊钢, 2006, 27(3): 8-10.