X80管线钢238 mm x 1 650 mm连铸坯温度场及凝固末端位置的数学模拟

特殊钢 ›› 2016, Vol. 37 ›› Issue (4): 5-8.

X80管线钢238 mm x 1 650 mm连铸坯温度场及凝固末端位置的数学模拟

周亚罗¹，刘文广²，李国旳²，孟凡伟¹

1华北理工大学电气工程学院，唐山063009；
2首钢京唐公司制造部，唐山063200

收稿日期:2016-05-20 出版日期:2016-08-01 发布日期:2022-07-29
作者简介:周亚罗(1982-),女，硕士(2007年河北理工大学)，讲师， 2004年河北理工大学(本科)毕业，冶金自动化研究。
基金资助:
国家自然科学基金资助(61171058)

Mathematical Simulation on Terminal of Solidification and Temperature Field of Casting X80 Pipe Line Steel 238 mm x 1 650 mm Slab

Zhou Yaluo¹, Liu Wenguang², Li Guoyun²，Meng Fanwei¹

1 College of Electrical Engineering, North China University of Science and Technology, Tangshan 063009;
2 Manufacturing Division, Shougang Jingtang United Iron & Steel Co Ltd, Tangshan 063200

Received:2016-05-20 Published:2016-08-01 Online:2022-07-29

摘要/Abstract

摘要： 用二维切片跟踪铸坯凝固传热的方法建立了X80管线钢（/%:0.04C,1.85Mn,0.25Si,0.006P,0.003S,0.30Ni,0.21Mo,0.06Nb,0.02V）238 mm×1650 mm板坯连铸过程中垂直拉坯方向传热的数学模型,通过ANSYS对X80管线钢连铸过程中温度场及坯壳厚度的渐变进行计算,得出拉速1.2mm/min时,出结晶器坯壳厚为18.14 mm,铸坯液芯长22.58 m。凝固壳厚度计算值射钉测试结果的相对误差≤2.5%,凝固末端位置的相对误差为0.68%。分析了过热度（25~55℃）,拉速（1.2~1.3m/min）和二冷水量（79.2~96.8 m³/h）对切片各点温度和凝固末端位置的影响。结果表明,增大拉速、减小二冷配水量,连铸坯表面温降变慢,凝固末端位置距离结晶器液面越远,凝固时间变长;该X80管线钢板坯连铸最佳工艺参数为钢水过热度35℃,拉速1.2 m/min和二冷配水量88m³/h。

关键词: X80管线钢, 238 mm X 1 650 mm板坯, 连铸, 温度场, 坯壳厚度, 凝固末端

Abstract: The mathematical model for heat transfer of pipe line steel X80 (/% : 0. 04C, 1. 85Mn, 0. 25Si, 0. 006P, 0. 003S, 0. 30Ni, 0. 21Mo, 0. 06Nb, 0. 02V) 238 mm x 1 650 mm slab at vertical direction of strand has been established by two-dimensional cutting slice tracing slab solidification heat transfer method, and the calculation for change of shell thickness and temperature field of pipe line steel X80 slab during casting is carried out by ANSYS soft ware. It is obtained that with casting speed 1. 2 m/min the shell thickness of slab at out of mold is 18. 14 mm and the slab liquid core length is 22. 58 m. The relative error of solidification shell thickness between calculated data and measured data is ≤ 2. 5% , and that of terminal position of solidification is 0. 68%. The effect of superheating extent (25 - 55 °C ) , casting speed ( 1. 2 -1. 3 m/min) and secondary cooling water rate (79. 2 -96. 8 m³/h) on temperature at each point of cutting slice and terminal position of solidification is analyzed. The results show that with increasing casting speed and reducing secondary cooling water rate the slab surface temperature drops slowly, the terminal position of solidification distance from mold is farther and the solidification time is longer. The optimum process parameters for casting slab of pipe line steel X80 are superheating extent 35 ℃,casting speed 1. 2 m/min and secondary cooling water rate 88 m³/h.

周亚罗, 刘文广, 李国旳, 孟凡伟. X80管线钢238 mm x 1 650 mm连铸坯温度场及凝固末端位置的数学模拟[J]. 特殊钢, 2016, 37(4): 5-8.

Zhou Yaluo, Liu Wenguang, Li Guoyun , Meng Fanwei. Mathematical Simulation on Terminal of Solidification and Temperature Field of Casting X80 Pipe Line Steel 238 mm x 1 650 mm Slab[J]. Special Steel, 2016, 37(4): 5-8.

参考文献

[1] Eddy A L,Marin H T,Jose J R M,et al. Effect of C and Mn Variations upon the Solidification Mode and Surface Cracking Susceptibility of Peritectic Steelsf [J]. ISIJ International,2009,49(6) ：851-858.
[2]Yoon J K. Applications of Numerical Simulation to Continuous Casting Technology [J].ISIJ International ,2008,48 (7) ： 879-884.
[3]朱苗勇，杜钢，阎立懿.现代冶金学[M].北京:冶金工业出版社,2009.
[4]Wang Weiling, Luo Sen, Zhu Miaoyong. Numerical Simulation of Dendritic Growth o£ Continuously Cast High Carbon Steel [J]. Metallurgical and Materials Transactions A,2015 ,46( 1) ；396-406.
[5] Boyko Yu S,Karatsuba V I,Shevenionov D N,et al. The Design of a Continuous Casting Machine for Production of Quality Billets from Steels with a Wide Range of Grades [J]. Metallurgist ,2014,57 (9- 10):891-898.
[6]贾光霖，齐雅丽,张国志，等.合金钢连铸坯动态凝固过程数值模拟[J].东北大学学报(自然科学版),2004,25(2):129-132.
[7]Wang B, Walker B N,Samarasekera I V. Shell Growth Surface Quality and Mould Taper Design for High Speed Casting of Stainless Steel Billets [J]. Candian Metallurgical Quaterly,2000,39(4) ：441-456.
[8]尚利洪，麻永林.U74钢大方坯连铸温度场的模拟及液芯长度变化研究[J].连铸,2001(2):16-18.
[9]Bratu V,Moritici C, Oros C ,et al. Mathematical Model of Solidification Process in Steel Continuous Casting Taking into Account the Convective Heat Transfer at Liquid-Solid Interface [J]. Computational Materials Science,2014,94 ：2-7.
[10]蔡开科，孙彦辉,韩传基.连铸坯质量控制零缺陷战略[J].连铸,2011(51) ：288-298,
[11]冯亮花，朱苗勇，刘坤.连铸板坯凝固末端位置的研究[J].钢铁,2009,44(5):23-26.
[12]赵莉萍，麻永林,王宝峰，等.不锈钢板坯连铸温度场及凝固末端位置的研究[J] .包头钢铁学院学报,2002,21(1)： 16-18.
[13]Louhenkilpi Seppo, Uoti Markku, Kytonen Heli, et al. Effect of Thermophysical Material Data on Heat Transfer in Continuous Casting [J]. Modeling of Casting, Welding and Advanced Solidification Process,2003,43(6) ：733.
[14]张志祥，闵义，姜茂发-37Mn5连铸圆坯凝固过程数学模拟[J].东北大学学报(自然科学版),2010,31 (7) ：966-969.
[15] Masahito H, Masayuki K, Akihiro Y. Growth of Solidified Shell Just below the Meniscus in Continuous Casting Mold [J]. ISIJ International 2009,49(3 ) ：365-374.
[16]张晓明.实用连铸连轧技术[M].北京:化学工业出版社,2008.