特殊钢 ›› 2013, Vol. 34 ›› Issue (5): 64-67.

钙和硼对无取向硅钢退火冷轧板组织和磁性能的影响

万勇¹，陈伟庆¹，吴绍杰^1,2

1.北京科技大学钢铁冶金新技术国家重点实验室,冶金与生态工程学院，北京100083；
2.新余钢铁公司技术中心，新余338001；

收稿日期:2013-04-22 出版日期:2013-10-01 发布日期:2022-09-22
作者简介:万勇(1987-)，男，博士研究生(北京科技大学)，2009年江苏大学毕业，钢的质量研究与品种开发

Effect of Calcium and Boron on Structure and Magnetic Properties of Non-Oriented Silicon Steel

Wan Yong¹ , Chen Weiqing¹ , Wu Shaojie^1,2

1. State Key Laboratory of Advanced Metallurgy, School of Metallurgical and Ecological Engineering, University of Science and Technology, Beijing 100083 ；
2. Technology Center, Xinyu Iron and Steel Co Ltd, Xinyu 338001;

Received:2013-04-22 Published:2013-10-01 Online:2022-09-22

摘要/Abstract

摘要： 不含Ca和B,含Ca(0.0026%Ca)和含Ca-B(0.0027%Ca和0.0045%B)的3种无取向硅钢(/%:0.004~0.006C、1.31~1.38Si、0.34~0.41Mn、0.004S、0.027P、0.36~0.41Als、0.0022~0.002 8T[O]、0.004 8~0.0060N)由6.5 kg真空感应炉冶炼,锻成70 mm扁坯,热轧成2.5 mm板,950℃常化后冷轧成0.5 mm板,在30%H₂+70%N₂气氛经920℃ 3 min退火,炉冷。试验结果表明,无取向硅钢中进行钙处理,钢中可形成CaO·6Al₂O₃和CaS,有效抑制了MnS的析出,有利于退火冷轧板晶粒长大。复合添加ca和B的退火冷轧板中未发现BN;含0.0026%Ca无取向硅钢退火冷轧板具有最强的{100}面织构和Goss织构组分,含0.0027%Ca-0.0045%B无取向硅钢退火冷轧板具有最弱的{112}<110>织构组分。3炉试验钢中,钙处理的0.0026%ca无取向硅钢退火冷轧板的综合磁性能最好,铁损P_1.5/50和磁感应强度B₅₀分别为4.32 W/kg和1.764 T。

关键词: Ca, B, 无取向硅钢, 晶粒尺寸, 织构, 磁性能

Abstract: The 3 kinds of non-oriented silicon steel (/% : 0.004-0.006C, 1.31-1.38Si, 0.34-0.41Mn, 0.004S, 0.027P, 0.36-0.41Als, 0.0022-0.0028 T[O], 0.0048-0.0060N) - non containing Ca and B, containing Ca (0.0026% Ca) , and containing Ca-B (0.0027% Ca and 0.0045% B) is melted by a 6.5 kg vacuum induction furnace ,forged to 70 mm flat blank, hot-rolled to 2.5 mm plate, normalized at 950 °C and cold-rolled to 0.5 mm sheet then in 30% H₂ + 70% N₂ atmosphere annealed at 920 for 3 min, furnace cooling. Test results show that with adding calcium treatment the CaO • 6A1₂O₃ and CaS form in the non-oriented silicon steel it is available to inhibit the deposition of MnS precipitate and favourable to promote the grain growth ； in annealed cold-rolled sheet of non-oriented silicon steel containing Ca and B, the BN has not been found； the annealed cold-rolled sheet of steel containing 0.0026%Ca has strongest {100} face texture and Goss texture； while that of steel containing 0.0027% Ca and 0.0045% B has weakest {112}<110>texture. In three heats of test steels, the comprehensive magnetic property of the steel containing 0.002 6% Ca is best i. e. its iron loss P_1.5/50 and magnetic induction B₅₀ are respectively 4.32 W/kg and 1.764 T.

Key words: Ca, B, Non-Oriented Silicon Steel, Grain Size, Texture, Magnetic Property

万勇, 陈伟庆, 吴绍杰. 钙和硼对无取向硅钢退火冷轧板组织和磁性能的影响[J]. 特殊钢, 2013, 34(5): 64-67.

Wan Yong , Chen Weiqing , Wu Shaojie. Effect of Calcium and Boron on Structure and Magnetic Properties of Non-Oriented Silicon Steel[J]. Special Steel, 2013, 34(5): 64-67.

[1]	彭峰, 李旭, 李博鹏, 张越, 王占忠, 郭士北. 紧固件用10.9级32CrB4调质圆钢的开发[J]. 特殊钢, 2024, 45(6): 8-11.
[2]	孙剑, 刘占礼, 李杰, 张鹏飞, 郑京辉, 邢力勇. BTW1钢连铸板坯高温热塑性行为分析[J]. 特殊钢, 2024, 45(6): 12-16.
[3]	郑安民, 樊轩宇, 黄增鑫, 毛旺旺, 于彦冲, 张金玲, 王社斌. 稀土Ce对20MnTiB冷镦钢中夹杂物演变的影响[J]. 特殊钢, 2024, 45(6): 37-47.
[4]	赵昊乾, 张育明, 马博, 巩延杰, 孟耀青. LF精炼结束后软吹时间对帘线钢LX82 A夹杂物控制的影响[J]. 特殊钢, 2024, 45(6): 53-56.
[5]	唐远寿, 张十庆, 李方, 何钦生, 赵振, 王宏, 邹兴政, 王建桥, 黄雅丽. 淬火温度对M₆C强化2 200 MPa级超高强度钢力学性能的影响[J]. 特殊钢, 2024, 45(5): 108-112.
[6]	王哨兵, 孙文强, 王曼, 周珠, 刘正东, 钟强. Nb对GH4169合金管材组织性能的影响[J]. 特殊钢, 2024, 45(5): 34-39.
[7]	张明. 显微组织对薄壁X65M管线钢落锤试验性能的影响[J]. 特殊钢, 2024, 45(5): 123-126.
[8]	李阳, 赵广迪, 臧喜民, 姜昊源, 王兆宇. B对Fe-Cr-B-C合金热处理后显微组织和强韧性的影响[J]. 特殊钢, 2024, 45(5): 25-33.
[9]	曹玉龙, 张赛康, 汪秀秀, 马崇圣, 李光强. 加热温度对高钒高速钢中M₂C碳化物分解转变行为的影响[J]. 特殊钢, 2024, 45(4): 146-152.
[10]	梅飞强, 赵吉庆, 闫磊, 王云海, 杨钢. 1Cr16Co5Ni2MoWVNbN耐热钢球座模锻成型工艺模拟与试验验证[J]. 特殊钢, 2024, 45(4): 131-138.
[11]	刘朝霞, 孙宪进, 刘俊, 叶建军, 王柯, 徐光琴. 热处理工艺及Nb微合金化对9Ni钢组织性能的影响[J]. 特殊钢, 2024, 45(3): 70-74.
[12]	马立国, 郭大勇, 王秉喜, 高航, 张博, 潘阳. 10B38含硼冷镦钢的研制与开发 [J]. 特殊钢, 2024, 45(3): 10-14.
[13]	刘慧丹, 尹利成, 朱继乔, 刘静, 程朝阳, 戴惠磊. 时效轧制温度对低温取向硅钢组织、织构及磁性能的影响[J]. 特殊钢, 2024, 45(3): 80-84.
[14]	孙文强, 周珠, 徐阿敏, 王哨兵, 苏诚, 沈强. 热处理工艺对高铬低活化铁素体-马氏体钢力学性能的影响[J]. 特殊钢, 2024, 45(2): 105-111.
[15]	王为民, 亓海全, 韩向楠, 眭文杰, 刘安奇, 郭春成, 笪仲钟, 万宇, 李文通. Mo微合金化对82B钢高温力学性能及显微组织的影响[J]. 特殊钢, 2024, 45(2): 79-85.