60Si2Mn弹簧钢150 mm x 150 mm铸坯缺陷分析与工艺优化

特殊钢 ›› 2022, Vol. 43 ›› Issue (5): 59-62.

60Si2Mn弹簧钢150 mm x 150 mm铸坯缺陷分析与工艺优化

林鹏^1,2，许正周^1,2，印传磊^1,2，张洪才^1,2，翟万里^1,2，许光乐^1,2

1. 江苏沙钢集团淮钢特钢股份有限公司技术中心，淮安 223002；
2. 江苏省轨道交通用特殊钢新材料重点实验室，淮安 223002 ；

收稿日期:2022-02-10 出版日期:2022-10-01 发布日期:2022-09-29
作者简介:林鹏(1988 -)，男，工程师

Defects Analysis and Process Optimization of 150 mm x 150 mm Casting Billet of 60Si2Mn Spring Steel

Lin Peng^1,2 , Xu Zhengzhou^1,2 , Yin Chuanlei^1,2 , Zhang Hongcai^1,2 , Zhai Wanli^1,2 , Xu Guangle^1,2

1. Technology Center, Huaigang Special Steel Co. , Ltd. Jiangsu Shagang Group, Huai' an 223002 ；
2. Key Laboratory of Special Steel New Materials for Rail Traffic of Jiangsu Province,Huai' an 223002;

Received:2022-02-10 Published:2022-10-01 Online:2022-09-29

摘要/Abstract

摘要： 针对60Si2Mn弹簧钢(/%:0.56～0.64C,1.50～2.00Si, 0.70～1.00Mn,≤0.025P,≤0.020S)的150 mm×150 mm连铸坯角部存在横向表面裂纹缺陷问题，通过采用金相显微镜和扫描电镜对铸坯角部横向表面裂纹缺陷进行分析及试验比对。结果表明：结晶器铜管锥度过大、拉坯阻力大、保护渣润滑效果差以及二次冷却不均匀导致角部产生横向表面裂纹。通过将结晶器铜管锥度从2.2 mm降到1.6 mm、保护渣熔化温度从1182℃降到1072℃、粘度从0.76 Pa·s降到0.52 Pa·s以及二次冷却比水量从0.45L/kg降到0.32L/kg等措施，降低铸坯在铜管内拉坯阻力，改善结晶器冷却传热和二冷段喷淋冷却效果，提高铸坯冷却均匀性，使得铸坯缺陷得到有效控制，铸坯表面探伤合格率从35%提高到92%。

关键词: 60Si2Mn弹簧钢, 150 mm X 150 mm铸坯, 表面裂纹, 结晶器铜管, 保护渣, 二次冷却

Abstract: Facing the quality problems of transverse surface crack at the comer of 150 mm x 150 mm continuous casting billet of 60Si2Mn spring steel(/% ：0.56-0.64C, 1.50-2.00Si,0.70-1.00Mn, ≤0.025P, ≤0.020S) , the transverse surface crack defects at the comer of casting billet are analyzed by metallographic microscope and SEM and it is carrying out test comparison. The result indicates that the defect is caused by the large drag force of the large taper of crystallizer copper tube and the poor lubrication effect of shielding flux and the uneven secondary cooling. By reducing the mold steel tube taper from 2.2 mm to 1.6 mm and the melting temperature of protective slag from 1 182 °C to 1 072 °C and its viscosity from 0.76 Pa·s to 0.52 Pa·s and the secondary specific water from 0.45 L/kg to 0.32 L/kg,to reduce the drag of casting billet in copper tube and improve the cooling heat transfer of the mold, the cooling effect of the secondary cooling section and the cooling uniformity of casting billet, the defects of casting billet have been effective controlled, and the qualified pass rate for casting billet surface defect detection increases from 35% to 92%.

Key words: 60Si2Mn Spring Steel, 150 mm x 150 mm Casting Billet, Surface Crack, Crystallizer Copper Tube, Mold Shielding Flux, Secondary Cooling

林鹏, 许正周, 印传磊, 张洪才, 翟万里, 许光乐. 60Si2Mn弹簧钢150 mm x 150 mm铸坯缺陷分析与工艺优化[J]. 特殊钢, 2022, 43(5): 59-62.

Lin Peng , Xu Zhengzhou , Yin Chuanlei , Zhang Hongcai , Zhai Wanli , Xu Guangle. Defects Analysis and Process Optimization of 150 mm x 150 mm Casting Billet of 60Si2Mn Spring Steel[J]. Special Steel, 2022, 43(5): 59-62.

参考文献

[1] 刘泳，旧志强，马超，等.60Si2Mn弾簧钢中夹杂物对高周疲劳特性影响研究[J].钢铁钒钛,2020,41(6):151-157.
[2] 李云昆，尉文超，何肖飞，等.不同冶炼方法对扭杆弹簧钢超髙周疲劳性能的影响[J].钢铁研究学报,2020,32(11): 1006-1013.
[3] 周力，左龙飞，马建超，等.弹簧钢小方坯成分偏析改善实践[J].上海金属,2018,40(1):51-56.
[4] 聂小龙，高加强，孟开仁，等. 60Si2Mn弹簧钢的断裂失效分析[J].金属热处理,2021,46(8):246-250.
[5] 刘飞，岳峰，刘佳伟，等.100 t LD-LF-RH-CC流程冶炼60Si2Mn弹簧钢非金属夹杂研究[J].特殊钢,2020,41(4):15- 18.
[6] 李小虎，龚志翔，高振波.精炼渣碱度对弹簧钢夹杂物的影响研究[J].炼钢,2020,36(4):70-74.
[7] 杜广巍，郭汉杰.80 t BOF-LF-RH-CC流程冶炼55SiCr弹簧钢洁净度的研究[J] .特殊钢,2016,37(4)：18-22.
[8] 刘锦文，铁占鹏，郭路召，等.SiCaBa合金对55SiCr弾黄钢的脱氧脱硫及夹杂物控制研究[J].特殊钢,2020,41(3) ：20-24.
[9] 王兴宇，韩延申，刘青，等.末端电磁搅拌对弹簧钢连铸坯内部质量的影响[J].钢铁,2020,55(5):5967.
[10] 张正林，陈志亮，丑向红，等.汽车稳定杆用高品质弹簧钢55Cr3生产工艺实践[J].连铸,2018,43(6):7-10.
[11] 王清波，张华，李永超，等. 120 t LF精炼渣系对弹簧钢55SiCrA夹杂物塑性的影响[J].特殊钢,2022,43(1)：34-38.
[12] 刘进步，张新文，张庆武.圆坯表面网状裂纹产生原因及控制[J].连铸,2016,41(2):66-70.
[13] 印传磊，裡万，,蒋栋初，等.42CrMo钢大尺寸夹杂物的来源与控制[J].中国冶金,2021,31(1):36-41.
[14] 蔡开科.连铸坯质量控制[M].北京：冶金工业出版社,2010：209-229.
[15] 何宇明，何生平.结晶器保护渣的润滑与传热控制功能剖析[J]-连铸,2021,46(2)：26
[16] 米源.结晶器保护渣的性能和使用工艺[J].连铸,2007,4(1):39-42.
[17] 林鹏，张洪才，印传磊，等.含硫45钢铸坯缺陷分析与工艺优化[J].特殊钢,2018,39(5):40-43.
[18] 潘伟杰，李民，朱礼龙，等.Na₂O对超高緘度连铸保护渣性能的影响[J].钢铁,2022,57(1):93-101.