BOF-LF-RH-CC流程高压锅炉管用钢12Cr1MoVG的生产实践

特殊钢 ›› 2012, Vol. 33 ›› Issue (5): 35-37.

BOF-LF-RH-CC流程高压锅炉管用钢12Cr1MoVG的生产实践

邓通武

攀钢集团研究院有限公司材料所，攀枝花617000

收稿日期:2012-03-26 出版日期:2012-10-01 发布日期:2022-10-09
作者简介:邓通武(1978-),男，工程师,2002年东北大学毕业,金属压力加工，优特钢新产品开发。

Production Practice of Steel 12CrlMoVG for High Pressure Boiler Tube by BOF-LF-RH-CC Process

Deng Tongwu

Institute for Material Research, Panzhihua Iron and Steel Institute Co Ltd, Panzhihua 617000

Received:2012-03-26 Published:2012-10-01 Online:2022-10-09

摘要/Abstract

摘要： Φ110～Φ280 mm锅炉管用热轧圆钢12Crl MoVG(/%:0.08～0.15C、0.17～0.35Si、0.40～0.70Mn、≤0.015P、≤0.010S、0.90～1.20Cr、0.25～0.35Mo、0.15～0.30V、≤0.015[Alt])的生产工艺流程为120 t顶底复吹转炉-LF-RH-CC-轧制。通过控制铁水[As]、[Sn]、[Sb]、[Pb]、[Bi],控制转炉终点[C]0.04%～0.08%、[P]≤0.010%、[S]≤0.010%,出钢过程铝铁脱氧,钢包喂铝线控制[Alt]≤0.015%并用复合精炼渣和少量铝丸终脱氧,控制中间包钢水过热度20～35℃,全程保护浇注等工艺措施,使试验钢的[As]+[Sn]+[Sb]+[Pb]+[Bi]≤0.029%、[P]≤0.011%、[S]≤0.008%、[Alt]≤0.011%,各类夹杂物级别均≤1.0,满足用户的技术要求。

关键词: 高压锅炉管, 12Cr1MoVG钢, 120 t BOF-LF-RH-CC, 热轧圆钢

Abstract: The production flow sheet of Φ110 〜Φ280 mm hot rolled round steel 12Crl MoVG for boiler tube (/%: 0. 08 〜0. 15C, 0. 17~0. 35Si, 0. 40 -0. 70Mn, ≤0.015P, ≤0.010S, 0. 90 〜1. 20Cr, 0. 25 ~0. 35Mo, 0. 15 -0. 30V, ≤0. 015 [Alt]) is 120 t top and bottom combined blown con verter-LF-RH-CC-Rolling process. With the process measures including to control hot metal [ As], [ Sn], [ Sb], [ Pb] and [ Bi], control converter end point [C]0. 04% 〜0. 080%, [P] ≤0. 010% and [ S] ≤0. 010%, deoxidize by aluminum iron during tapping, feed Al wire in ladle to control [ Alt] ≤0. 015%, refine by compound refining slag and some aluminum shot in LF process, control tundish liquid superheating extent 20 ~ 35 ℃, whole-shielding-cast etc, the [As] + [ Sn] + [ Sb] + [ Pb] + [ Bi] is W 0. 029%, the [P], [ S] and [Als] are respectively ≤0.011%, ≤0. 008% and ≤0. 010%, and the rating of each series inclusion is ≤1.0 to meet the technical requirement of user.

邓通武. BOF-LF-RH-CC流程高压锅炉管用钢12Cr1MoVG的生产实践[J]. 特殊钢, 2012, 33(5): 35-37.

Deng Tongwu. Production Practice of Steel 12CrlMoVG for High Pressure Boiler Tube by BOF-LF-RH-CC Process[J]. Special Steel, 2012, 33(5): 35-37.

[1]	贾进, 黄治成. EH36钢120 t BOF-LF-RH-CC流程精炼过程中夹杂物演变研究[J]. 特殊钢, 2022, 43(4): 10-14.
[2]	任刚, 肖国华, 任根柱, 袁野, 李金波. T12钢高压锅炉管150 mm x 150 mm连铸坯除鳞的工艺实践[J]. 特殊钢, 2020, 41(6): 12-14.
[3]	吴明洋. 100t LF Si-Ca脱氧低铝锅炉管用钢 15CrMoG 夹杂物分析[J]. 特殊钢, 2018, 39(1): 65-67.
[4]	方忠强, 孙彦辉, 汪成义, 蔡开科. 120 t BOF-LF-RH-CC流程冶炼石油套管钢时TiN的析出和控制[J]. 特殊钢, 2014, 35(5): 30-33.
[5]	谷立功, 肖功业, 王国亮. 天津钢管集团股份有限公司T91高压锅炉钢管材的试制[J]. 特殊钢, 2007, 28(4): 58-59.
[6]	葛龙桂, 李国忠. 兴澄特钢连铸连轧高压锅炉管用钢坯的质量控制[J]. 特殊钢, 2005, 26(3): 61-62.