20钢Φ300 mm圆铸坯中间裂纹成因分析和改善工艺措施

特殊钢 ›› 2012, Vol. 33 ›› Issue (2): 37-39.

20钢Φ300 mm圆铸坯中间裂纹成因分析和改善工艺措施

张志宏^1,2，刘江伟²，郑锦峰²，刘伟平²，成国光¹

1. 北京科技大学冶金与生态工程学院，北京 100083；
2. 承德建龙特殊钢有限公司，承德 067201；

收稿日期:2011-10-14 出版日期:2012-04-01 发布日期:2022-10-14
作者简介:张志宏( 1975-)，男，博士研究生，1997年包钢钢铁学院毕业，特殊钢开发

An Analysis on Cause of Formation of 0.20C Steel Φ300 mm Round Casting Bloom Intermediate Cracks and Improved Process Measure

Zhang Zhihong^1，2 , Liu Jiangwei² , Zheng Jinfeng² , Liu Weiping² , Cheng Guoguang¹

1. School of Metallurgical and Ecological Engineering, University of Science and Technology, Beijing 100083 ；
2. Chengde Jianlong Special Steel Co Ltd, Chengde 067201；

Received:2011-10-14 Published:2012-04-01 Online:2022-10-14

摘要/Abstract

摘要： 针对20钢φ300mm圆铸坯低倍组织出现中间裂纹的位置和形貌,结合连铸设备和工艺进行分析,得出结晶器内坯壳厚度不均匀,拉矫机矫直压力波动大,铸坯在受到热应力和矫直应力的作用下沿晶界开裂形成中间裂纹。通过改善结晶器软化水和连铸二冷水的质量,钢水过热度由25～35℃降至20～30℃,结晶器电磁搅拌电流由550 A降至350 A,稳定矫直压力,铸坯矫直温度≥950℃,避免了圆铸坯中间裂纹的出现。

关键词: Φ300 mm圆铸坯, 中间裂纹, 矫直力

Abstract: According to location and morphology of intermediate cracks occurred in macrostructure of 0.20C steel 4>300 mm round casting bloom and combining with analysis on casting equipment and process, it is obtained that with uneven shell thickness formed in mold, larger fluctuation of hydraulic force of withdraw straightening stands on bloom, the intermediate cracks along intergranular boundary form in bloom under action of heat stress and straightening stress. With improving the quality of mold softened water and secondary water for casting, decreasing superheating extent of liquid from 25-35 °C to 20-30 °C , decreasing mold electromagnetic stirring current from 550 A to 350 A, stabling the hydraulic force, and straightening bloom temperature ≥ 950 °C , the intermediate cracks in round casting bloom are eliminated.

Key words: Φ300 mm Casting Round Bloom, Intermediate Cracks, Straightening Force

张志宏, 刘江伟, 郑锦峰, 刘伟平, 成国光. 20钢Φ300 mm圆铸坯中间裂纹成因分析和改善工艺措施[J]. 特殊钢, 2012, 33(2): 37-39.

Zhang Zhihong , Liu Jiangwei , Zheng Jinfeng , Liu Weiping , Cheng Guoguang. An Analysis on Cause of Formation of 0.20C Steel Φ300 mm Round Casting Bloom Intermediate Cracks and Improved Process Measure[J]. Special Steel, 2012, 33(2): 37-39.

[1]	黄华, 时朋召, 徐李军, 夏春祥, 赵英杰. LD-氩站流程生产Q235B钢连铸板坯中间裂纹的分析与控制[J]. 特殊钢, 2022, 43(2): 55-58.
[2]	王振国, 任勇, 程晓茹, 詹胜利, 黄大军. Q345B低温变形抗力模型及在矫直工艺中的应用[J]. 特殊钢, 2012, 33(2): 33-36.
[3]	麻晓光, 王天瑶, 张秀平. 包钢X65管线钢Φ300 mm圆铸坯的试制[J]. 特殊钢, 2010, 31(2): 43-44.
[4]	刘纲, 朱荣, 钟春生, 刘剑, 周振华, 王慧霞. 水平连铸工艺对40Cr钢φ150 mm管坯中间裂纹的影响[J]. 特殊钢, 2009, 30(3): 40-41.
[5]	王勇, 苏春霞, 张起生. [P]对低碳Si-Mn-B钢170 mm x1 650 mm铸坯断裂的影响[J]. 特殊钢, 2009, 30(3): 42-43.