Effect of Si Content on Structure and Properties of Cold Work Die Steel Cr8Mo2SiV

Li Dongli^1，2, Ma Dangshen², Chi Hongxiao^1，2, Zhan Zhaolin¹ ， Kang Aijun³

1 School of Electrical and Mechanical Engineering, Kunming University of Science and Technology, Kunming 650093 ；
2 Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081 ；
3 Dongbei Special Steel Group, Fushun 113001

Received:2009-09-24 Published:2010-04-01 Online:2022-11-17

摘要/Abstract

摘要： 研究了Si含量对25 kg真空感应炉冶炼的Cr8Mo2SiV钢(%:0.96～0.97C、0.31～0.36Mn、7.98～8.04Cr、2.01～2.08Mo、0.31～1.52Si、0.20V)组织和力学性能的影响。结果表明,随着Si含量的增加,共晶碳化物尺寸变大,数量增多,淬火峰值硬度向高温区移动;经1 030℃淬火,550℃回火后,随着Si含量的提高,Cr8Mo2SiV钢的二次硬化能力和冲击韧性明显提高。Cr8Mo2SiV钢最佳的Si含量为1.5%。

关键词: 冷作模具钢Cr8Mo2SiV, Si含量, 二次硬化, 冲击韧性

Abstract: The effect of Si content on Structure and mechanical properties of steel CrMo2SiV (% : 0. 96 ~ 0. 97C, 0. 31 ~0. 36Mn, 7.98 ~8.04Cr, 2.01 ~2.08Mo, 0. 31 ~ 1. 52Si, 0. 20V) melted by a 25 kg vacuum induction furnace has been studied. Results show that with increasing Si content the size and amount of eutectic carbides in steel increase and the peak hardness of quenched steel moves to higher temperature region ； and with increasing Si content the secondary hardening ability and impact toughness of steel Cr8Mo2SiV quenched at I 030 Y and tempered at 550 °C obviously increase. The optimum Si content in steel Cr8Mo2SiV is 1. 5%.

Key words: Cold Work Die Steel Cr8Mo2SiV, Si Content, Secondary Hardening, Impact Toughness