铈对超级双相不锈钢00Cr25Ni7Mo4N热加工性能的影响

特殊钢 ›› 2010, Vol. 31 ›› Issue (4): 58-60.

铈对超级双相不锈钢00Cr25Ni7Mo4N热加工性能的影响

俞飞^1,2, 宋志刚², 郑文杰², 郭忠诚¹, 季祥民², 丰涵³

1昆明理工大学材料科学与工程学院，昆明650093;
2钢铁研究总院结构材料研究所，北京100081

收稿日期:2010-02-26 出版日期:2010-08-01 发布日期:2022-11-20
通讯作者: 通讯作者：宋志刚，教授，钢铁研究总院结构材料研究所，北京100081
作者简介:俞飞(1984-),男，硕士研究生，双相不锈钢材料研究。

Influence of Cerium on Hot Workability of Super Duplex Stainless Steel 00Cr25Ni7Mo4N

Yu Fei^1,2, Song Zhigang², Zheng Wenjie², Guo Zhongcheng¹ , Ji Xiangmin², Feng Han²

1 School of Materials Science and Engineering,Kunming University of Science and Technology,Kunming 650093;
2 Institute for Structural Materials,Central iron and Steel Research Institute,Beijing 100081

Received:2010-02-26 Published:2010-08-01 Online:2022-11-20

摘要/Abstract

摘要： 通过Gleeble-1500D热模拟试验机对0～0.034%Ce的超级双相不锈钢00Cr25Ni7Mo4N(%:0.016～0.020C、24.50～24.72Cr、7.06～7.18Ni、3.61～3.73Mo、0.26～0.27N)进行了950～1 200℃、应变速率5×10^-3s^-1的热拉伸和变形量60%、应变速率1×10⁰s^-1的热压缩试验。结果表明,适量铈的加入能提高00Cr25Ni7Mo4N钢的热塑性,铈含量为0.012%时有最好的热塑性;铈含量为0.021%以上时,该钢的峰值应力低于未加稀土钢;铈的加入有助于钢提前达到稳态流变阶段。

关键词: 超级双相不锈钢, 00Cr25Ni7Mo4N, , 铈, 热加工性

Abstract: Hot tension test with strain rate 5×10^-3s^-1and hot reduction test with deformation 60% and strain rate 1×10⁰s^-1for 0～0.034% Ce super duplex stainless steel 00Cr25Ni7Mo4N (%:0.016～0.020C,24.50～24.72Cr, 7.06~7. 18Ni,3.61~3.73Mo,0.26~0.27N) at 950~1200℃ have been carried out by using Gleeble- 1500D thermal simulation machine. Results show that adding suitable cerium is available to increase the hot plasticity of steel 00Cr25Ni7Mo4N, and the steel containing 0.012Ce% has optimum hot plasticity; as the Ce content is more than 0.021%, the peak stress of the steel is lower than that of steel non-adding rare earth elements; and adding Ce is available to reach steady state deformation stage in advance.

俞飞 , 宋志刚, 郑文杰 , 郭忠诚, 季祥民 , 丰涵. 铈对超级双相不锈钢00Cr25Ni7Mo4N热加工性能的影响[J]. 特殊钢, 2010, 31(4): 58-60.

Yu Fei, Song Zhigang, Zheng Wenjie, Guo Zhongcheng , Ji Xiangmin, Feng Han². Influence of Cerium on Hot Workability of Super Duplex Stainless Steel 00Cr25Ni7Mo4N[J]. Special Steel, 2010, 31(4): 58-60.

[1]	易忠烈, 陈兴润, 魏海霞, 钱张信, 赵得江. 冷却速率对2507超级双相不锈钢σ相析出的影响[J]. 特殊钢, 2023, 44(2): 17-20.
[2]	沈国雄, 徐见平, 吴汉民, 汤磊, 夏亚金, 吴利阳. 典型Cr-Ni-Mo-N高合金双相不锈钢热加工性能研究[J]. 特殊钢, 2020, 41(1): 68-74.
[3]	武敏, 李建春, 李国平, 卫英慧. 铸态超级双相不锈钢S32750热变形行为及组织演变[J]. 特殊钢, 2019, 40(5): 12-16.
[4]	李俊. 固溶处理对超级双相不锈钢S32750组织和性能的影响[J]. 特殊钢, 2012, 33(4): 64-66.
[5]	王佳夫, 刘丽丽, 花福安, 李建平, 王国栋. 2507超级双相不锈钢的热变形行为[J]. 特殊钢, 2011, 32(6): 50-52.
[6]	李国平, 李俊, 张威, 范新智. 固溶温度对超级双相不锈钢S32750板材组织和耐蚀性的影响[J]. 特殊钢, 2009, 30(2): 61-62.
[7]	吴忠忠, 宋志刚, 郑文杰, 陈斌, 陆建生. 固溶温度对超级双相不锈钢00Cr25Ni7Mo4N 组织和性能的影响[J]. 特殊钢, 2006, 27(4): 11-13.