氩直流辉光等离子体钢液脱氮的研究

特殊钢 ›› 2007, Vol. 28 ›› Issue (5): 7-9.

氩直流辉光等离子体钢液脱氮的研究

徐芳泓¹，孙铭山¹，丁伟中²，鲁雄刚²

1. 太原钢铁(集团)有限公司技术中心，太原 030003；
2. 上海大学，上海 200072；

收稿日期:2007-04-23 出版日期:2007-10-01 发布日期:2023-02-13
作者简介:徐芳泓(1966-)，男，高级工程师,1989年东北工学院毕业，从事产品开发研究工作。
基金资助:
国家自然科学基金资助项目(59974016)

A Study on Nitrogen Removal from Molten Steel in Argon DC Glow Plasma

Xu Fanghong¹ , Sun Mingshan¹ , Ding Weizhong² , Lu Xionggang²

1. Taiyuan Iron and Steel (Group) Co Ltd, Taiyuan 030003 ；
2. Shanghai University, Shanghai 200072 ；

Received:2007-04-23 Published:2007-10-01 Online:2023-02-13

摘要/Abstract

摘要： 用25 kg真空感应炉对0.02%C钢液进行氩直流(DC)辉光等离子体条件的脱氮实验,研究了氩辉光等离子体对钢液脱氮动力学的影响。结果表明,氩辉光等离子体钢液脱氮速度和脱氮效果明显优于真空钢液脱氮,当钢液氧含量为180×10^-6,在氩辉光等离子体下钢液中氮含量可降至9×10^-6。氩辉光等离子体对钢液的脱氮效果体现在界面化学反应上,提供了加速脱氮反应的动力学条件。

关键词: 氩直流辉光等离子体, 低碳钢液, 脱氮

Abstract: The nitrogen removal from 0. 02% C molten steel in argon direct current (DC) glow plasma has been tested by a 25 kg vacuum induction furnace and the effect of argon glow plasma on kinetics of nitrogen removal from molten steel was studied. Results showed that the nitrogen removal speed and efficiency from molten steel in argon glow plasma were obviously better than that in vacuum, as oxygen content in molten steel was 180 x 10^-6, in argon glow plasma the nitrogen content in molten steel could decrease to 9 x 10^-6. The effect of argon glow plasma on nitrogen removal from molten steel was embodied in interface chemical reaction to provide the kinetics condition for accelerating nitrogen removal reaction.

Key words: Argon DC Glow Plasma, Low Carbon Molten Steel, Nitrogen Removal

徐芳泓, 孙铭山, 丁伟中, 鲁雄刚. 氩直流辉光等离子体钢液脱氮的研究[J]. 特殊钢, 2007, 28(5): 7-9.

Xu Fanghong , Sun Mingshan , Ding Weizhong , Lu Xionggang. A Study on Nitrogen Removal from Molten Steel in Argon DC Glow Plasma[J]. Special Steel, 2007, 28(5): 7-9.

[1]	罗小雨, 郭靖, 郭汉杰, 李泽友. IN718镍基高温合金熔体脱氮和TiN析出热力学研究[J]. 特殊钢, 2024, 45(1): 33-41.
[2]	迟云广, 邓志银, 朱苗勇. 泡沫渣对120t转炉钢液脱氮的影响[J]. 特殊钢, 2017, 38(2): 40-43.
[3]	邹勇, 孙铭山. 85 t VOD精炼超纯铁素体不锈钢的脱氮工艺及效果[J]. 特殊钢, 2009, 30(6): 39-41.
[4]	孙亚琴, 陈麒忠, 张琢, 金鸣林. 增碳剂煅烧脱氮工艺实验研究[J]. 特殊钢, 2006, 27(5): 30-31.