The ratio of gauge of 0.80~1.20 mm cold- rolled 304 stainless steel - carbon steel(Q235A

08Al)-304 stainless steel clad plate produced by “exploding + rolling” process is 1:10:1. The clad plate has nice market prospect in building gate

window screen wall and cooker commodity field. The results of analysis on cold bending crack of clad plate sample showed that the probability of occurred crack with base plate of higher carbon content (0. 16%C) Q235A steel was greater than that with base plate of lower carbon content (0.06% C)08Al steel

the bending performance of cold- rolled clad plate was influenced by inclusion in steel

grain size and heat treatment of steel. The bending performance of cold- rolled clad plate was obviously improved by using 08Al steel as base plate

controlling 1050 ℃ heat treatment process to get grain size rating≤8 .