- BaO 和 Li₂O 对 CaO 基脱硫精炼渣熔点和粘度的影响
- Effect of BaO and Li2O on Melting Point and Viscosity of CaO-Based Refining Fluxes for Desulphuration
- 特殊钢 2005年26卷第4期页码：16-18
- 作者机构：
  
  江苏大学材料科学与工程学院,镇江,212013
- 作者简介：
  
  [ "李桂荣(1976-),女，博士研究生，从事炼钢工艺研究。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2005-01-19，
  
  网络首发：2023-04-08，
  
  纸质出版：2005-04-08
- 稿件说明：
移动端阅览
李桂荣, 祝贞学, 戴起勋, 等. BaO 和 Li₂O 对 CaO 基脱硫精炼渣熔点和粘度的影响[J]. 特殊钢, 2005,26(4):16-18.

李桂荣, 祝贞学, 戴起勋, et al. Effect of BaO and Li2O on Melting Point and Viscosity of CaO-Based Refining Fluxes for Desulphuration[J]. Special Steel, 2005, 26(4): 16-18.
李桂荣, 祝贞学, 戴起勋, 等. BaO 和 Li₂O 对 CaO 基脱硫精炼渣熔点和粘度的影响[J]. 特殊钢, 2005,26(4):16-18. DOI：

李桂荣, 祝贞学, 戴起勋, et al. Effect of BaO and Li2O on Melting Point and Viscosity of CaO-Based Refining Fluxes for Desulphuration[J]. Special Steel, 2005, 26(4): 16-18. DOI：

摘要

以CaO(bal)-SiO

(22.4%)-Al

(11.6%)-CaF

(10%)精炼渣作为基础渣系

用BaO、Li

O替代其中等量的CaO含量

固定(CaO+RxO)/SiO

=2.5(RxO代表BaO或者Li

对该脱硫精炼渣系的熔点和粘度进行了研究。结果显示在传统的CaO基熔渣中加入BaO、Li

O可以降低渣系的熔点和粘度

有效地改善了渣钢反应的动力学条件。当(BaO

O)=15%时

熔渣的熔点分别为1267℃和1185℃

远低于不加添加剂时的熔点1326℃

当温度为1475℃时

熔渣粘度分别为0.98Pa·s和0.51Pa·s

远小于不加添加剂时的粘度1.79Pa·s

使渣系具有良好的流动性和熔化性能。

Abstract

The melting point and viscosity of refining fluxes for desulphuration have been studied of which CaO (balance)-SiO

(22.4%)-Al

(11.6%)-CaF

(10%) refining slag was as basic flux

when the ratio of (CaO+RxO)/SiO

was fixed at 2.5(where RxO- BaO or Li

the BaO or Li

O added and replaced equivalent CaO content in flux. The results showed that the melting point and viscosity of fuxes decreased by added BaO or Li₂O in CaO basic slag effectively to improve the dynamics condition of metal- slag reaction. With 15% BaO or 15%Li₂O

the melting point of flux was 1267 ℃ or 1185 ℃ which were far lower than that of flux free additions- 1326 ℃

and the viscosity o

f flux at 1475 ℃ was 0.98 Pa · s or 0.51 Pa · s which were also far lower than that of flux free additions- 1.79 Pa · s to make the fluxes had excellent flu- idity and melting capacity.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

新型高强韧性弹簧钢40T 和44T 脱碳倾向的研究

真空感应熔炼过程炉衬材料向钢液供氧现象的研究

转炉冶炼超低碳、超低氮钢的工艺技术

高强度弹簧钢60SiCrV7 的性能和应用

30 t EAF-40 t LF冶炼35MnVS 易切削钢的工艺实践

BaO 和 Li2O 对 CaO 基脱硫精炼渣熔点和粘度的影响

Effect of BaO and Li2O on Melting Point and Viscosity of CaO-Based Refining Fluxes for Desulphuration

DOI：

摘要

Abstract

关键词

Keywords

references

BaO 和 Li₂O 对 CaO 基脱硫精炼渣熔点和粘度的影响