热处理对高强度易切削沉淀硬化不锈钢2Cr16Ni3Mo2CuN力学性能的影响

李志; 高谦; 高登攀; 江志华; 姜洪胜; 许广鹏

您当前的位置：

首页 >

文章列表页 >

热处理对高强度易切削沉淀硬化不锈钢2Cr16Ni3Mo2CuN力学性能的影响

试验研究 | 更新时间：2026-01-21

- 热处理对高强度易切削沉淀硬化不锈钢2Cr16Ni3Mo2CuN力学性能的影响
- Effect of Heat Treatment on Mechanical Properties of High Strength Free-Cutting Precipitation Hardening Stainless Steel 2Cr16Ni3Mo2CuN
- 特殊钢 2005年26卷第6期页码：23-25
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2005-06-20，
  
  网络首发：2023-04-11，
  
  纸质出版：2005-04-11
- 稿件说明：
移动端阅览
李志, 高谦, 高登攀, 等. 热处理对高强度易切削沉淀硬化不锈钢2Cr16Ni3Mo2CuN力学性能的影响[J]. 特殊钢, 2005,26(6):23-25.

李志, 高谦, 高登攀, et al. Effect of Heat Treatment on Mechanical Properties of High Strength Free-Cutting Precipitation Hardening Stainless Steel 2Cr16Ni3Mo2CuN[J]. Special Steel, 2005, 26(6): 23-25.
李志, 高谦, 高登攀, 等. 热处理对高强度易切削沉淀硬化不锈钢2Cr16Ni3Mo2CuN力学性能的影响[J]. 特殊钢, 2005,26(6):23-25. DOI：

李志, 高谦, 高登攀, et al. Effect of Heat Treatment on Mechanical Properties of High Strength Free-Cutting Precipitation Hardening Stainless Steel 2Cr16Ni3Mo2CuN[J]. Special Steel, 2005, 26(6): 23-25. DOI：

摘要

高强度易切削沉淀硬化不锈钢2Cr16Ni3Mo2CuN在退火状态下有优良的切削性能。研究了经过一级退火温度710~800℃和二级退火温度570~620℃处理后2Cr16Ni3Mo2CuN钢的布氏硬度(HB)值

以及1 050~1 085℃45 min油冷

-70℃2 h

150

170℃回火后的力学性能。试验结果表明

710~740℃5 h空冷+620℃5 h空冷处理后

2Cr16Ni3Mo2CuN钢HB值在321以下;1 050~1 085℃淬火

150~200℃回火处理后

该钢强度极限σ

≥1 520 MPa

≥12%

冲击功A

≥40 J。2Cr16Ni3Mo2CuN钢具有明显的二次硬化特征

二次硬化峰温度范围为480~520℃。

Abstract

The high strength free-cutting precipitation hardening stainless steel 2Cr16Ni3Mo2CuN has excellent cutting property in annealing conditions. The Brinell hardness(HB)number of steel 2Cr16N3Mo2CuN treated by first annealing at temperature between 710 ℃ and 800 ℃ and second annealing at temperature between 570 ℃ and 620 ℃ and the mechanical properties of steel treated with 1050~1085 ℃ for 45 min oil cooling

-70 ℃ for 2 h and 150 ℃ or 170 ℃ tempering have been studied. The test results showed that HB number of steel 2Cr16Ni3Mo2CuN treated with 710~740 ℃ for 5 h + 620 ℃5 h was less than 321 and tensile strength σ

of steel was ≥1520 MPa

≥12% and impact energy A

≥40 J. The steel 2Cr16Ni3Mo2CuN showed obvious secondary harde

ring effect and the peak temperature range of this effect was between 480 ℃ and 520℃.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

舵杆用Q345D钢热处理工艺对组织和性能的影响

高压锅炉用12Cr2Mo高强韧406 mmx40.5 mm钢管的热处理、组织和性能

新型V-Ti-B微合金化调质Q690E钢板的开发

单重 50 t 级别 174 mm 12Cr2Mo1Ｒ(H) 钢板研发

磷微合金化对镍/镍铁基合金凝固、热变形和性能的影响及作用机制研究进展