- An Analysis on Solidified Film Structure and Mineralogical Phase of Mould Powder for Compact Strip Production
- 特殊钢 2006年27卷第1期页码：21-23
- 作者机构：
  
  1. 北京科技大学,北京,100083
  2. 内蒙古科技大学材料与冶金学院,包头,014010
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2005-08-25，
  
  网络首发：2006-02-01，
  
  纸质出版：2006-02-01
- 稿件说明：
移动端阅览
董方, 王艺慈, 王宝峰. CSP结晶器保护渣固态渣膜结构和矿相的分析[J]. 特殊钢, 2006,27(1):21-23.

董方, 王艺慈, 王宝峰. An Analysis on Solidified Film Structure and Mineralogical Phase of Mould Powder for Compact Strip Production[J]. Special Steel, 2006, 27(1): 21-23.
董方, 王艺慈, 王宝峰. CSP结晶器保护渣固态渣膜结构和矿相的分析[J]. 特殊钢, 2006,27(1):21-23. DOI：

董方, 王艺慈, 王宝峰. An Analysis on Solidified Film Structure and Mineralogical Phase of Mould Powder for Compact Strip Production[J]. Special Steel, 2006, 27(1): 21-23. DOI：

摘要

通过光学显微镜、扫描电镜及X射线衍射分析，研究了1537 mm×67 mm CSP连铸结晶器保护(%:34.6CaO

28.6SiO₂

8.8C

8.5F

8.6Na₂O)固态渣膜的结构、矿相组成和析晶率，分析结果表明，绝大多数固态渣膜厚0.6~1.3mm

呈三层结构：结晶层-玻璃层-结晶层，靠结晶器壁侧为0.10～0.14mm 厚的结晶层；CSP 固态渣膜的析晶率为40%～80%

结晶矿相主要为枪晶石(3CaO ·2SiO₂ ·CaF₂)和矿物Na₂O ·Al₂O₃ ·SiQ₂。通过调整固态渣膜的厚度及枪晶石等矿物的析晶率，可达到控制渣膜传热，提高连铸坯表面质量的目的

Abstract

The solidified film structure

mineralogical phase and crystallization rate of 1537 mm×67 mm mould pow- der(34.6CaO

28.6SiQ₂

8.8C

8.5F

8.6Na₂O)for Compact Strip Production(CSP)have been studied by optical and scanning electron microscope and X-ray diffraction analysis. The results showed that most of the solidified flux films had three layers with total thickness 0.6~1.3 mm:crystallizing layer - glassy layer - crystallizing layer

of which the thickness of crystallizing layer at the side near mould was 0.10～0.14 mm; the crystallization rate of CSP solidified flux film was 40% ~80%

and the crystallized mineralogical phases were cuspidine(3CaO ·2SiO₂ ·CaF₂)and mineralogical phase Na₂O · Al₂O₃ · SiO₂ .The thermal transformation shall be controlled by adjusting the thickness of solidified flux film and crystallization rate of cuspidine in the film to increase the surface quality of concasting slab

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

新型高强韧性弹簧钢40T 和44T 脱碳倾向的研究

真空感应熔炼过程炉衬材料向钢液供氧现象的研究

转炉冶炼超低碳、超低氮钢的工艺技术

高强度弹簧钢60SiCrV7 的性能和应用

30 t EAF-40 t LF冶炼35MnVS 易切削钢的工艺实践