- Effect of Concasting Technology Parameters on Center Carbon, Segregation of High Carbon Steel Billet
- 特殊钢 2005年26卷第4期页码：33-35
- 作者机构：
  
  北京科技大学冶金与生态工程学院,北京,100083
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2004-12-25，
  
  网络首发：2023-05-17，
  
  纸质出版：2005-05-17
- 稿件说明：
移动端阅览
冯军, 陈伟庆. 连铸工艺参数对高碳钢小方坯中心碳偏析的影响[J]. 特殊钢, 2005,26(4):33-35.

冯军, 陈伟庆. Effect of Concasting Technology Parameters on Center Carbon, Segregation of High Carbon Steel Billet[J]. Special Steel, 2005, 26(4): 33-35.
冯军, 陈伟庆. 连铸工艺参数对高碳钢小方坯中心碳偏析的影响[J]. 特殊钢, 2005,26(4):33-35. DOI：

冯军, 陈伟庆. Effect of Concasting Technology Parameters on Center Carbon, Segregation of High Carbon Steel Billet[J]. Special Steel, 2005, 26(4): 33-35. DOI：

摘要

采用多元线性回归方法分析了在给定结晶器电磁搅拌条件下(230～245A)

碳含量0.58%～0.83%

二冷比水量0.82～2.86L/kg

拉速1.90～3.0m/min

过热度17～60℃范围内

各参数对140mm×140mm和150mm×150mm小方坯中心碳偏析的影响

并采用BP神经网络进行预测计算。多元回归分析结果表明

影响中心碳偏析的显著因素是钢中碳含量

其次是连铸拉速和二冷比水量;随钢中碳含量、拉速和过热度增加

铸坯中心碳偏析增大

随二冷比水量增加

中心碳偏析减小。

Abstract

The each technology parameters in range of carbon 0.58% -0.83%

water ratio in secondary cooling zone 0.82-2.86 L/kg

casting speed 1. 9 〜3.0 m/min and superheating of liquid steel 17 ~ 60 ℃： on center carbon segregation of 140 mm x 140 mm and 150 mm x 150 mm billet has been analyzed at given mould electromagnetic stirring (230 ~ 245 A) using multivariate linear regression analysis

and the predicted calculation was carried out using Back Propagation (BP) neural networks. Hie results by multivariate regression analysis showed that the carbon content in steel was remarkable factor to influence the center carbon segregation

next were casting speed and water; and with carbon content in steel

casting speed and superheating of liquid steel increasing

the center carbon segregation in billet increased and with water ratio in secondary cooling zone increasing

the center carbon segregation decreased.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

GCr15轴承钢大方坯凝固过程微观偏析模型及应用研究

连铸参数和末端电磁搅拌对82B钢小方坯中心碳偏析的影响

SWRH82B钢盘条笔尖状断口的分析和工艺改进

优化连铸工艺改善SWRH82A钢150 mm x 150 mm 铸坯中心碳偏析实践