Φ200mm H11芯棒钢热连轧过程张力影响因素的有限元分析

洪慧平; 程满; 康永林; 冯长桃; 陈溪强

您当前的位置：

首页 >

文章列表页 >

Φ200mm H11芯棒钢热连轧过程张力影响因素的有限元分析

试验研究 | 更新时间：2026-01-21

- Φ200mm H11芯棒钢热连轧过程张力影响因素的有限元分析
- Finite Element Analysis of Influence Parameters on Tension of Φ200 mm H11 Steel Round Bar for Mandrel during Hot Continuous Rolling
- 特殊钢 2006年27卷第3期页码：5-7
- 作者机构：
  
  1. 北京科技大学材料科学与工程学院,北京,100083
  2. 宝山钢铁股份有限公司,上海,201900
- 作者简介：
  
  [ "洪慧平(1963-),男，博士，副教授,从事材料加工计算机辅助工程与模拟仿真优化教学与科研。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2005-12-30，
  
  网络首发：2023-03-09，
  
  纸质出版：2006-03-09
- 稿件说明：
移动端阅览
洪慧平, 程满, 康永林, 等. Φ200mm H11芯棒钢热连轧过程张力影响因素的有限元分析[J]. 特殊钢, 2006,27(3):5-7.

洪慧平, 程满, 康永林, et al. Finite Element Analysis of Influence Parameters on Tension of Φ200 mm H11 Steel Round Bar for Mandrel during Hot Continuous Rolling[J]. Special Steel, 2006, 27(3): 5-7.
洪慧平, 程满, 康永林, 等. Φ200mm H11芯棒钢热连轧过程张力影响因素的有限元分析[J]. 特殊钢, 2006,27(3):5-7. DOI：

洪慧平, 程满, 康永林, et al. Finite Element Analysis of Influence Parameters on Tension of Φ200 mm H11 Steel Round Bar for Mandrel during Hot Continuous Rolling[J]. Special Steel, 2006, 27(3): 5-7. DOI：

摘要

应用MSC.MARC三维热力耦合弹塑性大变形有限元法及其接触分析技术

仿真研究了Φ200mm H11芯棒钢热连轧过程。分析得出

降低末道次轧辊速度V

会增强道次间的堆钢程度;提高末道次轧辊转速V

会增强道次间的拉钢程度;可通过合理修正V

值来改善堆、拉钢关系以及轧制负荷变化和轧材宽展量

以提高圆钢成品精度。提出大规格圆钢热连轧过程应采用微堆钢轧制技术

以保持轧制力、力矩稳定和满足轧材尺寸精度要求。

Abstract

The hot continuous rolling process of 効00 mm Hll steel round bar for mandrel has been simulated and studied by using MSC. MARC 3- dimensional thermo-mechanical coupled elasto-plastic finite element method (FEM) and contact analysis technique. It is obtained by analysis that with decreasing last pass roller speed Vr the compression extent between passes increased; with increasing last pass roller speed V

the tensile extent between passes increased; therefore it is available to modify the relation between compression and tensile

the rolling load change and the widening extent of rolling products by change V

value in order to increase the product dimension precision. It is concluded that the light compression technology between passes shall be adopted during heavy round steel continuous rolling to keep the stability of rolling load and torque and guarantee the require

ment of product dimension precision.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

钢包稳态温度场的有限元模拟

热连轧中间辊道保温工艺对低碳钢相变和组织的影响

20CrMnTiH圆钢精轧后控冷过程温度场有限元分析

165 mm×165 mm方坯连铸结晶器安全性的数值模拟分析

热卷箱在2250热连轧不锈钢带生产中的应用