优质弹簧钢60Si2CrVAT控轧控冷工艺的热模拟研究

试验研究 | 更新时间：2026-01-21

- 优质弹簧钢60Si2CrVAT控轧控冷工艺的热模拟研究
- Thermal Simulation Study on Controlled Rolling and Cooling Process for Quality Spring 60Si2CrVAT
- 特殊钢 2007年28卷第6期页码：21-23
- 作者机构：
  
  北京科技大学材料科学与工程学院,北京,100083
- 作者简介：
  
  [ "黄学启(1978-),男，硕士研究生，高强度优质弹簧钢的研究与开发。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2007-05-31，
  
  网络首发：2022-12-27，
  
  纸质出版：2007-12-27
- 稿件说明：
移动端阅览
黄学启, 刘雅政, 崔娟. 优质弹簧钢60Si2CrVAT控轧控冷工艺的热模拟研究[J]. 特殊钢, 2007,28(6):21-23.

黄学启, 刘雅政, 崔娟. Thermal Simulation Study on Controlled Rolling and Cooling Process for Quality Spring 60Si2CrVAT[J]. Special Steel, 2007, 28(6): 21-23.
黄学启, 刘雅政, 崔娟. 优质弹簧钢60Si2CrVAT控轧控冷工艺的热模拟研究[J]. 特殊钢, 2007,28(6):21-23. DOI：

黄学启, 刘雅政, 崔娟. Thermal Simulation Study on Controlled Rolling and Cooling Process for Quality Spring 60Si2CrVAT[J]. Special Steel, 2007, 28(6): 21-23. DOI：

摘要

用Gleeble-1500热模拟实验机测定了优质弹簧钢60Si2CrVAT的CCT曲线

并用光学显微镜和透射电镜研究了不同的终轧温度、冷却速度下的组织和相变。结果表明

冷速为1℃/s时

弹簧钢60Si2CrVAT中的珠光体含量约为98%;随着冷速的增加

铁素体和珠光体的含量逐渐减小

贝氏体和马氏体含量逐渐增加;当冷速达到9℃/s时

基体全部为马氏体;终轧温度850℃、冷速为1℃/s时

弹簧钢60Si2CrVAT的索氏体含量达到90%

强塑性最好

即R

1301 MPa

p0.2

928 MPa

A 23.8%

Z 38.6%。

Abstract

The continuous cooling transformation(CCT)curves

structure and phase transformation of quality spring steel 60Si2CrVAT with different finishing rolling temperature and cooling rate have been examined and studied by Gleeble-1500 thermal mechanical simulator

optical microscope and transmission electron microsope. Results showed that as cooling rate was1 ℃/s

the pearlite content in spring steel 60Si2CrVAT was about 98%;with increasing cooling rate the ferite and pearlite content gradually decreased while bainite and martensite content increased; and as cooling rate was up to 9 ℃/g

the matrix was all martensite.With finishing temperature 850 ℃ and cooling rate 1 ℃/s

the sorbite content in spring steel 60Si2CrVAT was up to90% with excellent strength and toughness i.e. R

1301 MPa

p0.2

928 Mpa

A23.8% and Z38.6%.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

热变形后冷却速度对铁素体-贝氏体微合金钢组织演变的影响

模拟控轧控冷过程含Nb超低碳钢的组织演变

TRIP钢 TMP和热处理过程中的组织演变

控轧控冷和冷床保温工艺对42CrMo钢φ50 mm轧材力学性能的影响

Nb-Ti微合金化含铬J55石油套管用钢的生产实践