三种耐蚀塑料模具钢的耐磨性和磨损机理

颜飞; 徐洲; 金冰忠

您当前的位置：

首页 >

文章列表页 >

三种耐蚀塑料模具钢的耐磨性和磨损机理

试验研究 | 更新时间：2026-01-21

- 三种耐蚀塑料模具钢的耐磨性和磨损机理
- Wear Resistance and Wearing Mechanism of Three Kinds of Corrosion Resistant Plastic Die Steel
- 特殊钢 2007年28卷第5期页码：37-39
- 作者机构：
  
  1. 上海交通大学教育部高温材料及高温测试开放实验室,上海,200030
  2. 宝钢技术中心,上海,201900
- 作者简介：
  
  [ "颜飞(1979-)，男，博士生，2001年武汉科技大学毕业，主要从事模具钢组织性能研究。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2007-05-08，
  
  网络首发：2023-02-14，
  
  纸质出版：2007-02-14
- 稿件说明：
移动端阅览
颜飞, 徐洲, 金冰忠. 三种耐蚀塑料模具钢的耐磨性和磨损机理[J]. 特殊钢, 2007,28(5):37-39.

颜飞, 徐洲, 金冰忠. Wear Resistance and Wearing Mechanism of Three Kinds of Corrosion Resistant Plastic Die Steel[J]. Special Steel, 2007, 28(5): 37-39.
颜飞, 徐洲, 金冰忠. 三种耐蚀塑料模具钢的耐磨性和磨损机理[J]. 特殊钢, 2007,28(5):37-39. DOI：

颜飞, 徐洲, 金冰忠. Wear Resistance and Wearing Mechanism of Three Kinds of Corrosion Resistant Plastic Die Steel[J]. Special Steel, 2007, 28(5): 37-39. DOI：

摘要

通过M200环-块磨损试验机和扫描电镜研究了具有良好耐腐蚀性能的3种塑料模具钢STAVAX (%:0.37C、13.40Cr、0.31V)、M330(%:0.36C、12.88Cr、0.15Mo)和N702(%:0.05C、16.30Cr、4.00Cu、4.00Ni、0.34Nb)的磨损性能和磨损表面形貌。结果表明

STAVAX、M330和N702钢在淬、回火后HRC值分别为55、53和44

磨痕宽度分别为2.61 mm、2.74 mm和7.41 mm。STAVAX和M330钢组织为基体+细球状碳化物

具有较高的耐磨性

而N702钢的基体相对较软

无第二相碳化物

在试验过程中其基体极易磨损

形成大量疲劳裂纹

易导致块状或片状剥落

耐磨性较低。

Abstract

The wear properties and wear surface morphology of three kinds of plastic die steel STAVAX (0.37C

13.40Cr

0.31V)

M330 (0.36C

12.88Cr

0.15Mo) and N702 (0.05C

16.30Cr

4.00Cu

4.00Ni

0.34Nb)with excellent corrosion resistance have been studied by M200 ring-block wear testing machine and scanning clectron micro-scope.Results showed that HRC value of quenched and tempered STAVAX

M330 and N702 steel was respectively 55

53 and 44

and width of wear coat was respectively 2.61 mm

2.74 mm and 7.4l mm; structure of STAVAX steel and M330 steel was matrix + fine spherical carbide and had higher wear resistance

while the matrix of N702 steel was relatively soft and there wasn't second phase - carbide precipitation which had lower wearing resistance

during testing the matrix was easily worm to form a lot of fatigue crack led to block and lamella weaing off.

关键词

Keywords

references

浏览量

下载量