双辐冷却低过热度浇铸结晶器流场和温度场耦合数值模拟

张俊婷; 崔小朝; 刘才; 晋艳娟

您当前的位置：

首页 >

文章列表页 >

双辐冷却低过热度浇铸结晶器流场和温度场耦合数值模拟

试验研究 | 更新时间：2026-01-21

- 双辐冷却低过热度浇铸结晶器流场和温度场耦合数值模拟
- Coupled Numerical Simulation of Flow Field and Temperature Field of Mold Concasting at Low Superheat by Two Rollers Cooling
- 特殊钢 2008年29卷第3期页码：30-32
- 作者机构：
  
  1. 太原科技大学应用科学学院,太原,030024
  2. 河北省科学院,石家庄,050081
- 作者简介：
  
  [ "张俊婷(1981-),女，硕士生，助教,2003年中北大学(华北工学院)毕业，液态金属流动性和传热研究。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2007-11-30，
  
  网络首发：2022-12-21，
  
  纸质出版：2008-12-21
- 稿件说明：
移动端阅览
张俊婷, 崔小朝, 刘才, 等. 双辐冷却低过热度浇铸结晶器流场和温度场耦合数值模拟[J]. 特殊钢, 2008,29(3):30-32.

张俊婷, 崔小朝, 刘才, et al. Coupled Numerical Simulation of Flow Field and Temperature Field of Mold Concasting at Low Superheat by Two Rollers Cooling[J]. Special Steel, 2008, 29(3): 30-32.
张俊婷, 崔小朝, 刘才, 等. 双辐冷却低过热度浇铸结晶器流场和温度场耦合数值模拟[J]. 特殊钢, 2008,29(3):30-32. DOI：

张俊婷, 崔小朝, 刘才, et al. Coupled Numerical Simulation of Flow Field and Temperature Field of Mold Concasting at Low Superheat by Two Rollers Cooling[J]. Special Steel, 2008, 29(3): 30-32. DOI：

摘要

提出了一种双辊冷却低过热度浇铸150 mm×150 mm方坯的技术

即使从中间包流出的钢水通过转动的冷却辊浇入结晶器内

通过降低钢水过热度改善铸坯质量。借助流体力学分析软件

对0.45C钢水的数值模拟结果发现

通过冷却辊冷却的钢液过热度降低

结晶器中钢水流冲击深度达250 mm

有利于打断凝固前沿的柱状晶

扩大等轴晶比例

同时结晶器内的钢液流场和温度场分布均匀

且铸坯的凝固状况也明显改善。

Abstract

A technology of low superheat casting for 150 mm x 150 mm billet by two rollers cooling has been put forward

that is the molten steel flowing out from tundish into mold through cooling turning rollers to reduce molten steel superheat and improve quality of casting billet. The results of numerical simulation for a 0. 45C steel by hydromechanics analysis software indicated that the superheat of molten steel through cooling roller reduced

the impact depth of molten steel flow in mold was up to 250 mm

it was available to break columnar crystal at forward position of solidification

moreover the molten steel flow field and temperature field in mold distributed homogeneously and the solidification condition of casting billet improved obviously.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

水口浸入深度对结晶器内钢液流场与温度场的影响

200 mm x200 mm方坯连铸用新型浸入式水口的数值模拟

基于ABAQUS的X70管线钢连铸板坯空冷的热力耦合分析

镍基单晶涡轮叶片定向凝固过程温度场数值模拟研究进展

中间包等离子体加热技术研究进展及应用