低合金钢残余元素Cu-As-Sn的晶界偏析对晶间脆性断裂的影响

耿明山; 王新华; 张炯明

您当前的位置：

首页 >

文章列表页 >

低合金钢残余元素Cu-As-Sn的晶界偏析对晶间脆性断裂的影响

试验研究 | 更新时间：2026-01-21

- 低合金钢残余元素Cu-As-Sn的晶界偏析对晶间脆性断裂的影响
- Effect of Grain Boundary Segregation of Residual Elements Cu-As-Sn on Intergranular Embrittlement Fracture of Low Alloying Steel
- 特殊钢 2009年30卷第4期页码：14-16
- 作者机构：
  
  北京科技大学冶金与生态工程学院,北京,100083
- 作者简介：
  
  [ "耿明山(1979-),男，博士生，2005年河北理工大学毕业，连铸-热轧坯研究。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2009-01-06，
  
  网络首发：2022-12-20，
  
  纸质出版：2009-12-20
- 稿件说明：
移动端阅览
耿明山, 王新华, 张炯明. 低合金钢残余元素Cu-As-Sn的晶界偏析对晶间脆性断裂的影响[J]. 特殊钢, 2009,30(4):14-16.

耿明山, 王新华, 张炯明. Effect of Grain Boundary Segregation of Residual Elements Cu-As-Sn on Intergranular Embrittlement Fracture of Low Alloying Steel[J]. Special Steel, 2009, 30(4): 14-16.
耿明山, 王新华, 张炯明. 低合金钢残余元素Cu-As-Sn的晶界偏析对晶间脆性断裂的影响[J]. 特殊钢, 2009,30(4):14-16. DOI：

耿明山, 王新华, 张炯明. Effect of Grain Boundary Segregation of Residual Elements Cu-As-Sn on Intergranular Embrittlement Fracture of Low Alloying Steel[J]. Special Steel, 2009, 30(4): 14-16. DOI：

摘要

用Gleeble-1500热模拟机、扫描电镜和俄歇能谱仪研究了0.10Cu-0.07As-0.05Sn对低合金钢(%:0.15C、0.36Si、1.40Mn、0.003S、0.019P)高温延塑性的影响

凝固过程中的偏析和热处理过程的晶界偏析。结果表明

Cu-As-Sn在晶界的偏析明显加剧第Ⅲ脆性凹槽区的深度和宽度

提高该区上限临界温度;连铸坯不存在明显的Cu-As-Sn晶界偏析

850℃拉伸至屈服的试样和热轧板试样存在明显的Cu-As-Sn晶界偏析

说明热变形加剧残余元素的晶界偏析。

Abstract

Effect of 0. 10Cu-0.07As-0.05Sn on segregation in solidification

grain boundary segregation in heat treatment and ductility of low alloying steel (%:0. 15C

0.36Si

1.40Mn

0.003S

0.019P) at elevated temperature have been studied by Gleeble- 1500 hot simulator

scanning electron microscope and Auger electron spectroscopy. Results showed that the segregation of Cu-As-Sn at grain boundary obviously increased the width and depth of depression of Ⅲ brittleness zone and raised upper limit of critical temperature of this zone; there was no-obviously Cu-As-Sn grain boundary segregation in cost billet and there was obviously grain boundary segregation in sample tensile-strained to yield at 850 ℃; and in sample of hot-rolled plate

it indicated the hot deformation promoted grain boundary segregation of residual elements.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Al₂O₃-CaO基预熔精炼渣吸收Al₂O₃夹杂的动力学研究

CaO-Al₂O₃渣系对20CrMoH齿轮钢中总氧和硫的影响

帘线钢钢包渣线砖侵蚀分析和提高寿命的工艺措施

高碱度高AI₂O₃炉渣下合金钢液中非金属夹杂物的行为

Al-Nb对700 ℃发电机组转子用GH706合金组织和拉伸性能的影响