二次硬化超高强度钢AF1410奥氏体晶粒长大行为

廉学魁; 厉勇; 刘宪民; 王春旭; 李建新; 严晓红

您当前的位置：

首页 >

文章列表页 >

二次硬化超高强度钢AF1410奥氏体晶粒长大行为

组织和性能 | 更新时间：2026-01-21

- 二次硬化超高强度钢AF1410奥氏体晶粒长大行为
- Growth Behavior of Austenite Grain of Secondary Hardening Ultra-high Strength Steel AF1410
- 特殊钢 2010年31卷第5期页码：61-63
- 作者机构：
  
  1. 钢铁研究总院结构材料研究所,北京,100081
  2. 抚顺特殊钢股份有限公司,抚顺,113001
- 作者简介：
  
  [ "廉学魁(1984-)，男，硕士研究生，高强度钢的组织和性能。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2010-04-07，
  
  网络首发：2022-11-12，
  
  纸质出版：2010-11-12
- 稿件说明：
移动端阅览
廉学魁, 厉勇, 刘宪民, 等. 二次硬化超高强度钢AF1410奥氏体晶粒长大行为[J]. 特殊钢, 2010,31(5):61-63.

廉学魁, 厉勇, 刘宪民, et al. Growth Behavior of Austenite Grain of Secondary Hardening Ultra-high Strength Steel AF1410[J]. Special Steel, 2010, 31(5): 61-63.
廉学魁, 厉勇, 刘宪民, 等. 二次硬化超高强度钢AF1410奥氏体晶粒长大行为[J]. 特殊钢, 2010,31(5):61-63. DOI：

廉学魁, 厉勇, 刘宪民, et al. Growth Behavior of Austenite Grain of Secondary Hardening Ultra-high Strength Steel AF1410[J]. Special Steel, 2010, 31(5): 61-63. DOI：

摘要

研究了二次硬化超高强度AF1410钢(%:0.165C、14.10Co、9.83Ni、1.92Cr、1.05Mo)在800～1200℃ 5～180 min加热的奥氏体晶粒长大行为。结果表明

AF1410钢奥氏体平均晶粒尺寸随加热温度的升高和保温时间延长而增大

加热温度超过1100℃后

奥氏体晶粒发生严重粗化;不同加热温度下

该钢的奥氏体平均晶粒尺寸与保温时间符合Beck关系;建立了AF1410钢的奥氏体晶粒长大数学模型

800～1200℃加热时

该钢奥氏体晶粒长大平均激活能为220.2 kJ/mol

其奥氏体平均晶粒尺寸与加热温度之间符合Arrhenius关系。

Abstract

The growth behavior of austenite grain of secondary hardening ultra-high strength steel AF1410 (% : 0.165C

14.10Co

9.83Ni

1.92Cr

1.05Mo) heating at 800 ~ 1200 °C for 5 - 180 min has been studied. Results show that with increasing heating temperature and holding time the average austenite grain size of steel AF1410 increases

and the austenite grains coarsen seriously at temperature more than 1100

℃

at different heating temperature; the relation between average austenite grain size of steel and holding time corresponds to Beck equation ； the math model for austenite grain growth of steel AF1410 has been established

with heating at 800〜1200 °C the average activation energy for austenite grain growth of the steel is 220.2 kJ/mol

and the relation between its average austenite grain size and heating temperature conforms to Arrhenius-type equation.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

车削非调质钢SG4201奥氏体晶粒的长大行为

GH4151镍基高温合金棒材微观组织研究

Nb微合金化对Cr-Co-Ni-Mo系超高强度不锈钢腐蚀疲劳性能的影响

预热处理工艺对SCr420H齿轮钢高温渗碳奥氏体晶粒长大行为的影响

非调质钢38MnVS奥氏体动态再结晶的研究