- Study on Regularity of Temperature Reduction of IF Steel Slab Casting Liquid with 210 t Top and Bottom Combined Blown Converter-RH Flow Sheet
- 特殊钢 2011年32卷第1期页码：40-43
- 作者机构：
  
  1. 北京科技大学冶金工程研究院,北京,100083
  2. 首钢技术研究院,北京,100041
- 作者简介：
  
  [ "王毓男(1987-),男，博士研究生,2008年北京科技大学本科毕业，钢水温度精确控制技术研究。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2010-09-17，
  
  网络首发：2022-09-27，
  
  纸质出版：2011-09-27
- 稿件说明：
移动端阅览
王毓男, 包燕平, 崔衡, 等. 210 t顶底复吹转炉-RH流程IF钢板坯连铸钢水温降规律的研究[J]. 特殊钢, 2011,32(1):40-43.

王毓男, 包燕平, 崔衡, et al. Study on Regularity of Temperature Reduction of IF Steel Slab Casting Liquid with 210 t Top and Bottom Combined Blown Converter-RH Flow Sheet[J]. Special Steel, 2011, 32(1): 40-43.
王毓男, 包燕平, 崔衡, 等. 210 t顶底复吹转炉-RH流程IF钢板坯连铸钢水温降规律的研究[J]. 特殊钢, 2011,32(1):40-43. DOI：

王毓男, 包燕平, 崔衡, et al. Study on Regularity of Temperature Reduction of IF Steel Slab Casting Liquid with 210 t Top and Bottom Combined Blown Converter-RH Flow Sheet[J]. Special Steel, 2011, 32(1): 40-43. DOI：

摘要

对迁钢210 t顶底复吹转炉-RH-板坯连铸工艺条件下的IF钢温度状况进行了统计和分析

根据RH初始温度和废钢加入量对RH处理过程温降的影响

建立RH处理过程钢水温度变化的数学模型

得出转炉出钢至开始连铸时的总温降为162.52℃

转炉出钢至RH到站平均温降为79.54℃

RH过程平均温降39.10℃

RH出站至中间包的温降为44.58℃;利用多元统计回归分析

可较好地预测RH过程的温降。

Abstract

The statistics and analysis on temperature condition of IF steel liquid in current 210 t top and bottom combined blown converter-RH-slab casting process condition at Qian An Iron and Steel Co have been carried out

and the math model for change of liquid temperature during RH treatment process is established in accordance with the effect of RH initial temperature of liquid and crape adding amount on temperature reduction of liquid during RH treatment process. It is obtained that the total temperature reduction of liquid from converter tapping to initial casting is 162. 52°C including the average temperature reduction 79. 54 °C. from converter tapping to RH station

39. 10 °C during RH process

44. 58 °C leaving RH station to tundish ； and the temperature reduction of liquid during RH process can be predicted reliably by using multiple regression analysis.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

热轧参数对粗奥氏体晶粒铌钢变形抗力的影响

基于改进人工神经网络的LF钢水终点温度预报

大圆坯连铸二冷配水设计模型的开发

高铁用EA4T车轴钢热变形行为及变形抗力模型的试验研究

0. 47C-0. 36Si-0. 67Mn钢连铸板坯低温轧制过程变形抗力模型