热轧板初始组织对冷轧无取向硅钢织构演变的影响

刘朋成; 金自力; 任慧平; 闫志飞; 张磊

您当前的位置：

首页 >

文章列表页 >

热轧板初始组织对冷轧无取向硅钢织构演变的影响

组织和性能 | 更新时间：2026-01-21

- 热轧板初始组织对冷轧无取向硅钢织构演变的影响
- Effect of Original Structure of Hot Rolled Plate on Texture Evolution of Cold Rolled Non-Oriented Silicon Steel
- 特殊钢 2012年33卷第2期页码：55-57
- 作者机构：
  
  1. 内蒙古科技大学材料科学与冶金学院,包头,014010
  2. 包钢集团无缝钢管厂,包头,014010
- 作者简介：
  
  [ "刘朋成(1987-)，男，硕士研究生，硅钢组织织构和性能研究" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2011-10-10，
  
  网络首发：2022-10-18，
  
  纸质出版：2012-10-18
- 稿件说明：
移动端阅览
刘朋成, 金自力, 任慧平, 等. 热轧板初始组织对冷轧无取向硅钢织构演变的影响[J]. 特殊钢, 2012,33(2):55-57.

刘朋成, 金自力, 任慧平, et al. Effect of Original Structure of Hot Rolled Plate on Texture Evolution of Cold Rolled Non-Oriented Silicon Steel[J]. Special Steel, 2012, 33(2): 55-57.
刘朋成, 金自力, 任慧平, 等. 热轧板初始组织对冷轧无取向硅钢织构演变的影响[J]. 特殊钢, 2012,33(2):55-57. DOI：

刘朋成, 金自力, 任慧平, et al. Effect of Original Structure of Hot Rolled Plate on Texture Evolution of Cold Rolled Non-Oriented Silicon Steel[J]. Special Steel, 2012, 33(2): 55-57. DOI：

摘要

研究了27.5 mm热轧板的初始组织(热轧态

850℃退火、950℃退火)对冷轧态和870℃退火的0.5mm冷轧无取向硅钢50W600薄板(/%:0.004C、0.33Si、0.38Mn、0.099P、0.007S、0.32Al)织构演变的影响。结果表明

经冷轧后冷轧板织构中{100}〈011〉和{112}〈110〉织构密度明显增大

末退火热轧板轧成的冷轧板织构密度较退火热轧板轧成的冷轧板强;经未退火热轧板冷轧成的薄板再结晶退火后的织构中主要为{100}〈011〉、{110}〈011〉和{111}〈112〉

退火热轧板冷轧成的薄板再结晶退火后的织构除{100}〈011〉和{110}〈011〉外还有密度较强的高斯织构。

Abstract

The effect of original structure of 27.5 mm hot rolled plate ( hot rolled status

850 °C annealed

950

℃

annealed) on evolution of texture of cold rolled status and 870 T annealed 0. 5 mm cold rolled non-oriented silicon steel 50W600 sheet (/% : 0. 004C

0. 33Si

0. 38Mn

0. 099P

0. 007S

0. 32A1) has been studied. Results show that after cold rolling the texture density of

{100}

011 > and

{112}

110 > in texture of cold rolled sheet increases obviously

and the texture density of sheet cold-rolled by non-annealed hot rolled plate is larger than that cold-rolled by annealed hot rolled plate ； in texture of recrystallization annealed sheet cold-rolled by non-annealed hot rolled plate

the main texture is

{100}〈011〉、{110}〈011〉and {111}〈112〉

while in texture of recrystallization annea

led sheet cold-rolled by annealed hot rolled plate

besides

{100}〈011〉and {110}〈011〉

there is higher density Goss-texture.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

无取向硅钢异步冷轧织构沿厚度的演变

成品厚度对无取向硅钢织构和磁性能的影响

退火温度对薄规格无取向电工钢磁性能和力学性能的影响

时效轧制温度对低温取向硅钢组织、织构及磁性能的影响

轧制条件对冷轧无取向硅钢织构的影响