380 mm x 280 mm大方坯连铸结晶器电磁搅拌的数值模拟

李熠; 倪红卫; 张华; 罗荣华

您当前的位置：

首页 >

文章列表页 >

380 mm x 280 mm大方坯连铸结晶器电磁搅拌的数值模拟

试验研究 | 更新时间：2026-01-21

- 380 mm x 280 mm大方坯连铸结晶器电磁搅拌的数值模拟
- Numerical Simulation of Mold Electromagnetic Stirring for 380 mm x 280 mm Bloom Casting
- 特殊钢 2012年33卷第2期页码：10-13
- 作者机构：
  
  武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉,430081
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2011-10-11，
  
  网络首发：2022-10-13，
  
  纸质出版：2012-10-13
- 稿件说明：
移动端阅览
李熠, 倪红卫, 张华, 等. 380 mm x 280 mm大方坯连铸结晶器电磁搅拌的数值模拟[J]. 特殊钢, 2012,33(2):10-13.

李熠, 倪红卫, 张华, et al. Numerical Simulation of Mold Electromagnetic Stirring for 380 mm x 280 mm Bloom Casting[J]. Special Steel, 2012, 33(2): 10-13.
李熠, 倪红卫, 张华, 等. 380 mm x 280 mm大方坯连铸结晶器电磁搅拌的数值模拟[J]. 特殊钢, 2012,33(2):10-13. DOI：

李熠, 倪红卫, 张华, et al. Numerical Simulation of Mold Electromagnetic Stirring for 380 mm x 280 mm Bloom Casting[J]. Special Steel, 2012, 33(2): 10-13. DOI：

摘要

利用有限元分析软件

建立了380 mm×280 mm大方坯结晶器电磁搅拌的三维数学模型

系统研究了电磁搅拌工艺参数(电流250～500 A

频率1.5～3.0 Hz

结晶器铜板厚度34～40 mm)对结晶器内电磁场的分布影响。结果表明

结晶器内磁感应强度沿铸流轴向呈"两端小、中间大"分布;电流从350 A增大到500 A

搅拌器中心的磁感应强度呈线性递增;频率由1.5Hz增大到3.0Hz

搅拌器中心磁感应强度仅减小0.0015 T;随着结晶器铜板厚度的增大

铸坯宽面、窄面和角部的磁感应强度都减小。在实际连铸U71Mn重轨钢中

电流应该维持在400 A以上。

Abstract

A three-dimensional math model of electromagnetic stirring of mold for 380 mm x 280 mm bloom casting is established by using finite element analytic software and the effect of electromagnetic stirring parameters (current intensity 200-500 A

frequency 1.5-3.0 Hz

thickness of mold copper plate 34-40 mm) on distribution of magnetic field in mold is systematically studied. Results show that the max magnetic induction intensity is at center of axis direction of strand and the lower values of magnetic induction intensity are at top and bottom of mold ； with increasing current intensity from 350 A to 500 A

the magnetic induction intensity at center of stirrer increases linearly ； with increasing current frequency from 1.5 Hz to 3.0 Hz

the magnetic induction intensity at center of strand decreases only by 0.0015 T； and with increasing thickness of mold copper plate

the magnetic induction intensity at wide surface

narrow surface and comer of the strand all decreases. In actual casting heavy rail steel U71Mn process

current intensity should be more than 400 A.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

220mm x 1600mm板坯连铸浸入式水口倾角优化的数值模拟和应用

EH420海工钢80 mm特厚板堆垛缓冷数值模拟

4J36因瓦合金钢锭凝固组织的数值模拟研究

12.9级高强度风电紧固件用42CrMoM钢生产工艺实践

薄板坯结晶器内中锰钢流动与凝固行为数值模拟