IF钢罩式退火过程中再结晶组织与织构的演变

组织和性能 | 更新时间：2026-01-21

- IF钢罩式退火过程中再结晶组织与织构的演变
- A Study on Evolution of Recrystallization Structure and Textures in an IF Steel during Batch Annealing Process
- 特殊钢 2012年33卷第6期页码：39-42
- 作者机构：
  
  1. 北京科技大学冶金与生态工程学院,北京,100083
  2. 包钢技术中心,包头,014010
- 作者简介：
  
  [ "冯岩青(1977-),女，博士研究生，工程师,2002年西安工业大学毕业，板材产品研发。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2012-06-02，
  
  网络首发：2022-09-29，
  
  纸质出版：2012-09-29
- 稿件说明：
移动端阅览
冯岩青, 王福明. IF钢罩式退火过程中再结晶组织与织构的演变[J]. 特殊钢, 2012,33(6):39-42.

冯岩青, 王福明. A Study on Evolution of Recrystallization Structure and Textures in an IF Steel during Batch Annealing Process[J]. Special Steel, 2012, 33(6): 39-42.
冯岩青, 王福明. IF钢罩式退火过程中再结晶组织与织构的演变[J]. 特殊钢, 2012,33(6):39-42. DOI：

冯岩青, 王福明. A Study on Evolution of Recrystallization Structure and Textures in an IF Steel during Batch Annealing Process[J]. Special Steel, 2012, 33(6): 39-42. DOI：

摘要

研究了IF钢(/%:0.005C、0.02Si、0.16Mn、0.011P、0.004S、0.042Als、0.061Ti、0.003 1 N)0.8 mm冷轧板在500～800℃退火时的再结晶组织及织构

采用X射线衍射技术结合微观组织观察分析了IF钢罩式退火过程中{111}再结晶织构形成机制和显微组织演变规律。结果表明

随退火温度的升高

再结晶数量逐渐增多

640℃为实验钢实际再结晶温度

同时{111}再结晶织构强度亦逐渐增大

{111}取向的晶粒主要在再结晶过程中形成

并在{111}取向晶粒长大过程中

γ纤维织构之间也发生相互转化

主要由{111}〈112〉织构转变为{111}〈110〉织构。

Abstract

The recrystallization structure and textures of an IF steel (/% : 0. 005C

0. 02Si

0. 16Mn

0. 011P

0. 004S

0. 042Als

0. 061 Ti

0. 003 1N) 0. 8 mm cold-rolled sheet during annealing at 500 ~800 ℃ are studied and the forming mechanism of ｛111｝ recrystallization textures and evolution law of structure of IF steel during batch annealing process are analyzed by X-ray diffraction technique combined with microstructure observation. Results show that with increasing annealing temperature the recrystallized volume increases

the real recrystallization temperature of test steel is 640 ℃

and with increasing annealing temperature the density of {111} recrystallized textures gradually increases

the {111} oriented grains mainly form during recrystallizing process and during growing process of the {111} oriented grains

the transfer between γ fiber textures occurs

it is mainly from {111} < 112 > texture transfers to {111} < 110 > texture.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

模拟CSP试制0.42%Cu Hi-B钢初次再结晶退火工艺试验

CSP-低碳钢DC03冷轧板的组织和织构

冷轧压下率对DQ级深冲带钢组织和性能的影响

基于CSP工艺热轧及冷轧过程3%Si钢组织和织构的演变

轧制工艺对X80管线钢组织、织构和性能的影响