惰性气体保护5 t电渣炉重熔铁路用G20CrNi2MoA渗碳轴承钢

周立新; 丁磊; 苏春阳; 潘明旭; 张洲; 柳学胜

您当前的位置：

首页 >

文章列表页 >

惰性气体保护5 t电渣炉重熔铁路用G20CrNi2MoA渗碳轴承钢

工艺技术 | 更新时间：2026-01-21

- 惰性气体保护5 t电渣炉重熔铁路用G20CrNi2MoA渗碳轴承钢
- Carburized Bearing Steel G20CrNi2MoA for Railway Remelted by an Inert Gas Shielding Atmosphere 5 t Electroslag Remelting Furnace
- 特殊钢 2012年33卷第5期页码：25-28
- 作者机构：
  
  湖北新冶钢有限公司1技术中心, 2炼钢事业部,黄石,435001
- 作者简介：
  
  [ "周立新(1968-),男，硕士，高级工程师，《特殊钢》编委，北京科技大学毕业，特殊钢产品研发及工艺研究。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2012-05-02，
  
  网络首发：2022-10-09，
  
  纸质出版：2012-10-09
- 稿件说明：
移动端阅览
周立新, 丁磊, 苏春阳, 等. 惰性气体保护5 t电渣炉重熔铁路用G20CrNi2MoA渗碳轴承钢[J]. 特殊钢, 2012,33(5):25-28.

周立新, 丁磊, 苏春阳, et al. Carburized Bearing Steel G20CrNi2MoA for Railway Remelted by an Inert Gas Shielding Atmosphere 5 t Electroslag Remelting Furnace[J]. Special Steel, 2012, 33(5): 25-28.
周立新, 丁磊, 苏春阳, 等. 惰性气体保护5 t电渣炉重熔铁路用G20CrNi2MoA渗碳轴承钢[J]. 特殊钢, 2012,33(5):25-28. DOI：

周立新, 丁磊, 苏春阳, et al. Carburized Bearing Steel G20CrNi2MoA for Railway Remelted by an Inert Gas Shielding Atmosphere 5 t Electroslag Remelting Furnace[J]. Special Steel, 2012, 33(5): 25-28. DOI：

摘要

试验和分析了全封闭气罩氩气保护电渣重熔与常规大气下电渣重熔铁路用G20CrNi2MoA渗碳轴承钢(/%:0.19C、0.49Cr、1.75Ni、0.23Mo、0.071Al)的冶金效果。结果表明

氩气保护电渣重熔锭Si和Mn的烧损量(3%～12%和4%～10%)低于常规电渣重熔锭Si和Mn的烧损量(15%～18%和7%～10%);当G20CrNi2MoA钢电极的氧含量为10×10

-6

时

氩气保护电渣锭的氧含量(15×10

-6

)低于常规电渣锭的氧含量(21.3×10

-6

);氩气保护电渣锭的冶金质量明显优于未经气体保护的常规电渣锭。

Abstract

The metallurgy effect of carburized bearing steel G20CrNi2MoA for railway (/% ： 0

19C

0. 49Cr

1.75Ni

0. 23Mo

0. 071 Al) by argon shielding atmosphere electroslag remelting ( ESR) in closed hood and by normal atmospheric ESR has been tested and analyzed. Results show that the loss of Si and Mn of argon shield atmosphere ESR ingot (3% 〜12% and 4% - 10% ) is less than the loss of Si and Mn of normal atmospheric ESR ingot (15% ~ 18% and 7% ~ 10% ) ； as the oxygen content in electrode of steel G20CrNi2MoA is 10 x 10

-6

the oxygen content in argon shield atmosphere ESR ingot (15 x 10

-6

) is lower than that in normal atmospheric ESR ingot (21.3 x 10

-6

) ； and the metallurgical quality of argon shield atmosphere ESR ingot is obviously better than that of normal non gas shielding ESR ingot.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

汽车用低碳齿轮钢的LF-VD 脱氧工艺

100t转炉-LF(VD)工艺冶炼轴承钢的氧含量控制

莱钢50t EBT EAF-LF(VD)-CC生产GCr15轴承钢的工艺实践

贵阳特钢60t Consteel EAF-LF(VD)-CC流程生产GCr15轴承钢的工艺实践

南钢100t UHP EAF-LF(VD)-CC生产GCr15轴承钢的工艺实践