硼对低温球罐用钢07MnNiMoVDR 50 mm板组织与力学性能的影响

王黎; 吴涛

您当前的位置：

首页 >

文章列表页 >

硼对低温球罐用钢07MnNiMoVDR 50 mm板组织与力学性能的影响

组织和性能 | 更新时间：2026-01-21

- 硼对低温球罐用钢07MnNiMoVDR 50 mm板组织与力学性能的影响
- Effect of Boron on Structure and Mechanical Properties of 50 mm Plate of Steel 07 MnNiMoVDR for Cryogenic Spherical Tank
- 特殊钢 2013年34卷第6期页码：59-61
- 作者机构：
  
  1. 内蒙古伊泰集团有限公司,鄂尔多斯,017000
  2. 舞阳钢铁有限责任公司科技部，舞钢,462500
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2013-07-11，
  
  网络首发：2022-09-08，
  
  纸质出版：2013-09-08
- 稿件说明：
移动端阅览
王黎, 吴涛. 硼对低温球罐用钢07MnNiMoVDR 50 mm板组织与力学性能的影响[J]. 特殊钢, 2013,34(6):59-61.

王黎, 吴涛. Effect of Boron on Structure and Mechanical Properties of 50 mm Plate of Steel 07 MnNiMoVDR for Cryogenic Spherical Tank[J]. Special Steel, 2013, 34(6): 59-61.
王黎, 吴涛. 硼对低温球罐用钢07MnNiMoVDR 50 mm板组织与力学性能的影响[J]. 特殊钢, 2013,34(6):59-61. DOI：

王黎, 吴涛. Effect of Boron on Structure and Mechanical Properties of 50 mm Plate of Steel 07 MnNiMoVDR for Cryogenic Spherical Tank[J]. Special Steel, 2013, 34(6): 59-61. DOI：

摘要

低温球罐用钢07MnNiMoVDR(/%:0.06~0.08C、0.20~0.30Si、1.50~1.60Mn、0.30~0.40Ni、0.10~0.15Cr、0.18~0.25Mo、0.04~0.05V、0.02~0.04Al)50 mm板由100 t UHP EAF-LF-300 mm×2 000 mm CC-4辊可逆轧机轧制工艺生产。研究了0~0.002 0%B对该钢900℃淬火-620℃回火的50 mm板组织和力学性能的影响。结果表明

加硼能显著提高钢板淬透性

以钢板心部得到均匀贝氏体为主的组织;当硼含量超过0.001 5%时

组织粗大并有混晶出现

冲击功下降

抗拉强度750 MPa超出标准上限(730 MPa)。当钢中硼含量控制在0.0005%~0.001 5%时钢板有良好的强韧性匹配

抗拉强度R

为630~690 MPa

冲击功140~275 J

满足标准要求。

Abstract

The 50mm plate of steel 07MnNiMoVDR (/% : 0. 06 ~0. 08C

0. 20 ~0.30Si

1. 50 ~ 1. 60Mn

0.30 ~0. 40Ni

0. 10 ~0. 15Cr

0. 18 ~0. 25Mo

0. 04 ~0. 05V 0. 02 ~0. 04Al) for cryogenic spherical tank is produced by 100 t UHP EAF-LF-300 mm x 2 000 mm CC-four-high reversing mill rolling process. The Effect of 0 ~ 0. 002 0% B on structure and mechanical properties of 50 mm plate of the steel quenched at 900 °C -tempered at 620℃ has been studied. Results show that adding boron can obviously increase hardenability of plate to get homogeneous major bainite structure ； as the boron content in steel is more than 0.001 5%

the structure coarsens with occurrence of mixing grains led to impact energy decreasing and tensile strength of steel (750 MPa) larger than the upper limit of standard (730 MPa). As the boron content in steel is controlled in 0.000 5% ~0.001 5%

the steel plate has excellent strength-toughness matching i. e. tensile strength 630 ~690 MPa and impact energy 140 ~ 275 J to meet the standard requirement.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Zr微合金化HSLA钢粗晶热影响区的组织和性能

形变对无取向硅钢50W470组织和力学性能的影响

冷轧和固溶处理对改进型202不锈钢组织和力学性能的影响

CSP流程生产Q345B钢带的机械性能和强化因素分析

退火工艺对0.17C冷轧链条用钢板组织和性能的影响