70 t BOF-LF-VD-CC流程转炉钢氮含量控制的工艺实践

郭志强; 颜学勇; 胡守才

您当前的位置：

首页 >

文章列表页 >

70 t BOF-LF-VD-CC流程转炉钢氮含量控制的工艺实践

工艺技术 | 更新时间：2026-01-21

- 70 t BOF-LF-VD-CC流程转炉钢氮含量控制的工艺实践
- Practice of Process for Control of Nitrogen Content in Converter Steel Melting by 70 t BOF-LF-VD-CC Flow Sheet
- 特殊钢 2013年34卷第6期页码：26-29
- 作者机构：
  
  1. 衢州元立金属制品有限公司,衢州,324000
  2. 湖北新冶钢有限公司,黄石,435001
  3. 唐山建龙实业有限公司，遵化,064200
- 作者简介：
  
  [ "郭志强(1973-),男，硕士(北京科技大学),1997年包头钢铁学院毕业,炼钢工艺和质量控制。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2013-05-17，
  
  网络首发：2022-09-06，
  
  纸质出版：2013-09-06
- 稿件说明：
移动端阅览
郭志强, 颜学勇, 胡守才. 70 t BOF-LF-VD-CC流程转炉钢氮含量控制的工艺实践[J]. 特殊钢, 2013,34(6):26-29.

郭志强, 颜学勇, 胡守才. Practice of Process for Control of Nitrogen Content in Converter Steel Melting by 70 t BOF-LF-VD-CC Flow Sheet[J]. Special Steel, 2013, 34(6): 26-29.
郭志强, 颜学勇, 胡守才. 70 t BOF-LF-VD-CC流程转炉钢氮含量控制的工艺实践[J]. 特殊钢, 2013,34(6):26-29. DOI：

郭志强, 颜学勇, 胡守才. Practice of Process for Control of Nitrogen Content in Converter Steel Melting by 70 t BOF-LF-VD-CC Flow Sheet[J]. Special Steel, 2013, 34(6): 26-29. DOI：

摘要

炼钢厂冶炼20CrMnTi

40Cr

GCr15钢的生产流程为70 t BOF-LF-VD-220 mm×220 mm CC工艺。由22炉20CrMnTi

40Cr和45钢中氮含量分析得出转炉出钢后钢中平均氮含量-[N

]

为21.70×10

-6

LF精炼后平均[N

]

48.95×10

-6

中间包平均[N

]

63.62×10

-6

。通过将铁水比从85%提高到92.3%

控制转炉终点[P

]

≤0.008%

出钢前钢包充氩

LF精炼快速形成泡沫渣

渣层厚100~120 mm

防止钢水吸氮

连铸时采用长水口控制吹氩量等措施

6炉GCr15钢冶炼结果表明

LF精炼后[N

]

为51.8×10

-6

~60.2×10

-6

VD后[N

]

29.1×10

-6

~33.9×10

-6

钢材中氮含量为31.8×10

-6

~40.0×10

-6

满足用户对钢材冷加工的需要。

Abstract

The flow sheet for steelmaking steel 20CrMnTi

0. 45C

40Cr and GCrl5 at melting shop is 70 t BOF-LF- VD-220 mm x220 mm CC process. It is obtained by analysis of 22 heats of steel 20CrMnTi

40Cr and 0. 45C that the average nitrogen content in steel after BOF tapping- [N

]

is 21.70 x 10

-6

end LF refining the average [N

]

48. 95 x 10

-6

and in tundish the average [N

]

63. 62 x 10

-6

. With increasing hot metal ratio from original 85% to 92. 3%

controlling BOF end [P

]

≤0. 008%

ladle filling argon before tapping

quick forming foamed slag in LF refining with slag thickness 100 ~ 120 mm to prevent liquid absorbing nitrogen

using long nozzle and controlling

argon blowing rate

the results by melting 6 heats of steel GCrl5 show that the [N

]

at end LF refining is 51. 8 x 10

-6

~ 60. 2 x 10

-6

the [ N

]

at end VD is 29. 1 x 10

-6

~33. 9 x 10

-6

and the nitrogen content in products is 31. 8 x 10

-6

~40. 0 x 10

-6

all products meet the requirement for cold working.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

130 t BOF-LF-150 mm x 150 mm CC 流程控制高碳钢SWRH82B氮含量的工艺实践

90 t电弧炉-LF(VD)-连铸-连轧流程生产链轨节钢35MnBM的工艺实践

氧气顶吹转炉-LF+VD流程生产高碳铬轴承钢的工艺实践

100t EBT电弧炉-LF-CC流程生产38CrMoAl钢的工艺实践

弹簧钢100 t DC EAF-LF-VD流程无铝脱氧工艺实践