100 t底吹氩钢包插入浸渍管对钢液流场影响的数值模拟

吴超; 沈明钢; 张德慧; 周晓东

您当前的位置：

首页 >

文章列表页 >

100 t底吹氩钢包插入浸渍管对钢液流场影响的数值模拟

试验研究 | 更新时间：2026-01-21

- 100 t底吹氩钢包插入浸渍管对钢液流场影响的数值模拟
- Numerical Simulation of Effect of 100 t Bottom-Blowing Argon Ladle with Immersed Cylinder on Liquid Flow Field
- 特殊钢 2015年36卷第2期页码：9-12
- 作者机构：
  
  辽宁科技大学材料与冶金学院,鞍山,114051
- 作者简介：
  
  [ "吴超(1988-),男，硕士研究生(辽宁科技大学)，2012年辽宁科技大学(本科)毕业，炼钢研究。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2014-10-29，
  
  网络首发：2022-08-20，
  
  纸质出版：2015-08-20
- 稿件说明：
移动端阅览
吴超, 沈明钢, 张德慧, 等. 100 t底吹氩钢包插入浸渍管对钢液流场影响的数值模拟[J]. 特殊钢, 2015,36(2):9-12.

吴超, 沈明钢, 张德慧, et al. Numerical Simulation of Effect of 100 t Bottom-Blowing Argon Ladle with Immersed Cylinder on Liquid Flow Field[J]. Special Steel, 2015, 36(2): 9-12.
吴超, 沈明钢, 张德慧, 等. 100 t底吹氩钢包插入浸渍管对钢液流场影响的数值模拟[J]. 特殊钢, 2015,36(2):9-12. DOI：

吴超, 沈明钢, 张德慧, et al. Numerical Simulation of Effect of 100 t Bottom-Blowing Argon Ladle with Immersed Cylinder on Liquid Flow Field[J]. Special Steel, 2015, 36(2): 9-12. DOI：

摘要

以100t单孔底吹氩钢包为原型

应用三维连续性方程、动量N-S方程及湍流κ-ε双方程模拟了底吹氩过程中钢包内的钢液流动状态。利用Mixture多相流模型对单孔吹氩（0~700 L/min）过程进行数值模拟

对比分析插入直径691.05 mm

深650 mmn浸渍管前后钢包内的流动状态和钢液表面的卷渣。结果表明

无浸渍管时

临界卷渣吹气量为102 L/min

插入浸渍管后

临界卷渣吹气量增大到217 L/min。插入浸渍圆筒可以在增加吹氩量的条件下提高钢液搅拌效果

加速钢液混匀。

Abstract

According to the prototype of 100 t ladle with single nozzle bottom-blowing argon

the flow status of liquid in ladle during argon blowing process is simulated by using three dimensional continuity equation

momentum N-S equation and turbulence K-e double equations. The numerical simulation on single nozzle argon blowing (0-700 L/min) process has been carried out by sing Mixture multiphase flow model and the liquid flow status and the phenomenon of slag entrapment at liquid surface in ladle before and after immersing cylinder with diameter 691.05 mm and immersing depth 650 mm are compared and analyzed. Results show that without immersed cylinder the critical slag entrapment argon blowing rate is 102 L/min

while with immerged cylinder the critical slag entrapment argon blowing rate increases to 217 L/min

immerged cylinder may increase liquid stirring effect with increasing argon blowing rate to accelerate liquid mixing.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

150 t钢包底吹氩的水模型研究

100 t 钢包底吹氩工艺优化的物理模拟

180 t钢包底吹氩过程钢液流场特性数值模拟

210 t RH精炼过程夹杂去除和卷渣的物理模拟

130t和160t钢包炉(LF)底吹氩的水模拟研究