2.5 mm x 10 mm 65Mn扁钢丝表面横裂纹原因分析和工艺改进

贾旭岗; 杨晓奇; 梁世勇

您当前的位置：

首页 >

文章列表页 >

2.5 mm x 10 mm 65Mn扁钢丝表面横裂纹原因分析和工艺改进

工艺技术 | 更新时间：2026-01-21

- 2.5 mm x 10 mm 65Mn扁钢丝表面横裂纹原因分析和工艺改进
- An Analysis on Factors of Surface Transversal Cracks of Steel 65Mn 2.5 mm x 10 mm Flat Wire and Process Improvement
- 特殊钢 2017年38卷第5期页码：34-36
- 作者机构：
  
  安阳钢铁股份有限公司第一炼轧厂,安阳,455004
- 作者简介：
  
  [ "贾旭岗(1979-),男，工程师,2004年河北理工大学(本科)毕业，冶金工艺研究和新产品开发。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2017-04-20，
  
  网络首发：2022-07-13，
  
  纸质出版：2017-07-13
- 稿件说明：
移动端阅览
贾旭岗, 杨晓奇, 梁世勇. 2.5 mm x 10 mm 65Mn扁钢丝表面横裂纹原因分析和工艺改进[J]. 特殊钢, 2017,38(5):34-36.

贾旭岗, 杨晓奇, 梁世勇. An Analysis on Factors of Surface Transversal Cracks of Steel 65Mn 2.5 mm x 10 mm Flat Wire and Process Improvement[J]. Special Steel, 2017, 38(5): 34-36.
贾旭岗, 杨晓奇, 梁世勇. 2.5 mm x 10 mm 65Mn扁钢丝表面横裂纹原因分析和工艺改进[J]. 特殊钢, 2017,38(5):34-36. DOI：

贾旭岗, 杨晓奇, 梁世勇. An Analysis on Factors of Surface Transversal Cracks of Steel 65Mn 2.5 mm x 10 mm Flat Wire and Process Improvement[J]. Special Steel, 2017, 38(5): 34-36. DOI：

摘要

由65Mn钢（/%:0.65C，0.24Si，1.00Mn，0.014P，0.006S）Φ6.5mm盘条冷拔和轧制的2.5mm×10mm扁钢丝出现表面横裂现象。通过对缺陷分析，得出由于铸坯表面增碳，使盘条表面形成条带状分布的块状碳化物的异常组织，并在冷拔过程中异常组织处形成微裂纹，在轧制压扁阶段，微裂纹扩展、合并形成宏观裂纹。连铸过程中钢液卷入保护渣富碳层会造成连铸坯局部表面增碳。通过改进150 mm×150 mm方坯连铸工艺，即液面波动由7~8 mm降低3~4 mm

浸入式水口插入深度由70~80 mm增至90~100 mm，保护渣粘度由0.35Pa·s优化成0.40Pa·s，连铸拉速由2.1~2.4m/min降至2.1~2.2m/min，65Mn扁钢丝的表面横裂纹率由原来的2.33%降至0。

Abstract

The surface transversal cracks occur on steel 65Mn (/%： 0.65C

0.24Si

1. 00Mn

0.014P

0.006S) 2.5mm X 10mm flat wire cold-drawn and rolled by φ6.5mm Coil. With analysis on defects it is obtained that due to casting billet surface carburization the abnormal structure of carbide block with strip distribution forms on coil surface

and in cold-drawing process the micro cracks form at abnormal structure and in flat-rolling process the micro cracks develop and combine to macro cracks. During casting process the liquid entraps enriched carbon layer of mold flux led to casting billet local surface carburization. With improving the 150 mm X 150 mm billet casting process including decreasing liquid surface fluctuating extend from original 7~8 mm to 3~4 mm

increasing depth of immersion n

ozzle from 70~80 mm to 90~100 mm

optimizing viscosity of mold powder from 0.35 Pa

·s

to 0.40 Pa

·s

and decreasing casting speed from 2.1~2.4 m/min to 2.1~2.2 m/min

the ratio of surface cracks of steel 65Mn flat wire decreases from original 2.33% to 0.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

钎具钢55SiMnMo轧材表面裂纹的成因分析及工艺改进

SWRH82B钢盘条笔尖状断口的分析和工艺改进

42CrMo钢曲轴锻件表面裂纹形成机理分析和工艺改进

重轨钢连铸坯中心偏析的分析和工艺改进

0Cr13C不锈钢线材表面混晶缺陷及工艺改进