拉速波动对GCr15轴承钢250mm x280mm连铸坯内部质量的影响

李颇; 范宇静; 张程; 申祖峰

您当前的位置：

首页 >

文章列表页 >

拉速波动对GCr15轴承钢250mm x280mm连铸坯内部质量的影响

工艺技术 | 更新时间：2026-01-21

- 拉速波动对GCr15轴承钢250mm x280mm连铸坯内部质量的影响
- Effect of Fluctuation of Casting Rate on Internal Quality of 250mm x 280mm Bloom of Bearing Steel GCr15
- 特殊钢 2017年38卷第5期页码：22-26
- 作者机构：
  
  东北特钢集团北满特殊钢有限责任公司技术中心,齐齐哈尔,161041
- 作者简介：
  
  [ "李颇(1974-),男，硕士研究生(东北大学)，高级工程师， 1997年内蒙古科技大学(本科)毕业,钢铁冶金和方坯连铸研究。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2017-04-26，
  
  网络首发：2022-07-11，
  
  纸质出版：2017-07-11
- 稿件说明：
移动端阅览
李颇, 范宇静, 张程, 等. 拉速波动对GCr15轴承钢250mm x280mm连铸坯内部质量的影响[J]. 特殊钢, 2017,38(5):22-26.

李颇, 范宇静, 张程, et al. Effect of Fluctuation of Casting Rate on Internal Quality of 250mm x 280mm Bloom of Bearing Steel GCr15[J]. Special Steel, 2017, 38(5): 22-26.
李颇, 范宇静, 张程, 等. 拉速波动对GCr15轴承钢250mm x280mm连铸坯内部质量的影响[J]. 特殊钢, 2017,38(5):22-26. DOI：

李颇, 范宇静, 张程, et al. Effect of Fluctuation of Casting Rate on Internal Quality of 250mm x 280mm Bloom of Bearing Steel GCr15[J]. Special Steel, 2017, 38(5): 22-26. DOI：

摘要

试验用GCr15轴承钢的生产工艺为100t BOF-LF-RH-250mm×280mm连铸坯-Φ70 mm轧材。用碳截面偏析检验、射钉试验及高倍检验等分析检测方法

研究了结晶器冷却水2530 L/min

钢水过热度33~37℃

二冷比水量0.12 L/kg

M-EMS 530 A/2.5 Hz

F-EMS 400 A/3.0 Hz参数下

GCr15轴承钢连铸坯拉速0.52~0.58m/min对连铸坯轴承钢碳偏析、坯壳厚度及末端凝固位置和Φ70mm轧材带状的影响。结果表明

随着连铸拉速的提升

铸坯的宏观碳偏析先呈现下降后呈现上升趋势

凝固末端位置后移

液相穴长度变长

拉速控制在0.55m/min

有利于降低铸坯的宏观碳偏析和轧材球化退火后的带状组织级别。

Abstract

The production process of tested bearing steel GCrl5 is 100t BOF- LF-RH-250mm x280mm bloom casting-φ70mm bar rolling. The effect of bloom casting rate 0.52〜0.58 m/min of bearing steel GCrl5 with casting parameters of mold cooling water rate 2530 L/min

liquid superheating extent 33~37℃

secondary cooling water ratio 0.12 L/kg

M-EMS 530 A/2.5 Hz and F-EMS 400 A/3.0 Hz on bearing steel carbon segregation

shell thickness and end solidification position

and banded structure of Φ70 mm rolled bar has been studied by using the analysis and test methods including bloom cross section carbon segregation examination

nail shot test and optical microscope test Results show that with increasing casting rate the macro carbon segregation of bloom first decreases then increases

the end solidification position moves forward and the length of liquid core becomes longer

to control casting rate 0.55 m/min is available to decrease the bloom macro carbon segregation and the rating of banded structure of rolled products after spheroidizing annealing.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

改善GCr15轴承钢小型棒材低倍质量的连轧工艺实践

60 t BOF-LF(VD) -150 mm x 150 mm 连铸生产 GCr15 轴承钢的工艺实践

氮对GCr15轴承钢高温力学性能的影响

连铸-开坯生产流程325 mm x 280 mm轴承钢铸坯温度变化的数值模拟

80t BOF-LF-VD-CC流程生产GCr15轴承钢控氧的工艺实践