The 3.5mm hot-rolled plate of stainless steel 06Cr13 (/%：0.03C

0.45Si

0.22Mn

0.020P

0.002S

12.20Cr) cold-rolls down to 0.375mm cold-rolled sheet by 11 passes. The effect of 800~925℃ annealing on texture ingredient and mechanical properties of stainless steel 06Cr13 cold-rolled sheet has been studied by using CCT-AV-Ⅱ simulation continuous annealing unit. Results show that with increasing annealing temperature the amount of {111} fiber texture being favourable for deep drawability increases

while the sum of amounts of {001}<110>

{114}<111>

{112}<110>

{112}<111> and {110}<110> texture being unfavourable for deep drawability decreases；as annealing at 875°C

difference between{111}<110> and {111}<112> texture ingredient is largest and the uniformity of {111} fiber texture is poorest；and the obvious anisotropy of strength and elongation of stainless steel 06Cr13 cold-rolledtor sheet annealed at 875℃ occurs. Based on comprehensive analysis the suitable annealing temperature for stainless steel 06Cr13 cold-rolled sheet is (850土10)℃.