C、Si含量和冷轧压下率对低碳钢Q195冷轧板力学性能的影响

赵海泉; 王新宇; 赖奇; 周兰花

您当前的位置：

首页 >

文章列表页 >

C、Si含量和冷轧压下率对低碳钢Q195冷轧板力学性能的影响

组织和性能 | 更新时间：2026-01-21

- C、Si含量和冷轧压下率对低碳钢Q195冷轧板力学性能的影响
- Effect of C、Si Content and Cold-Rolling Reduction on Mechanical Properties of Cold-Rolled Plate of Low Carbon Steel Q195
- 特殊钢 2018年39卷第6期页码：51-53
- 作者机构：
  
  攀枝花学院机钛学院,攀枝花,617000
- 作者简介：
  
  [ "赵海泉(1975-)男，博士(2018年钢铁研究总院毕业)，高级工程师,,钒钛、钢铁材料研究。王新宇(1979-),女，硕士，高级工程师,2005年中南大学硕士毕业，电磁纯铁新产品新工艺研发。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2018-05-29，
  
  网络首发：2022-05-26，
  
  纸质出版：2018-05-26
- 稿件说明：
移动端阅览
赵海泉, 王新宇, 赖奇, 等. C、Si含量和冷轧压下率对低碳钢Q195冷轧板力学性能的影响[J]. 特殊钢, 2018,39(6):51-53.

赵海泉, 王新宇, 赖奇, et al. Effect of C、Si Content and Cold-Rolling Reduction on Mechanical Properties of Cold-Rolled Plate of Low Carbon Steel Q195[J]. Special Steel, 2018, 39(6): 51-53.
赵海泉, 王新宇, 赖奇, 等. C、Si含量和冷轧压下率对低碳钢Q195冷轧板力学性能的影响[J]. 特殊钢, 2018,39(6):51-53. DOI：

赵海泉, 王新宇, 赖奇, et al. Effect of C、Si Content and Cold-Rolling Reduction on Mechanical Properties of Cold-Rolled Plate of Low Carbon Steel Q195[J]. Special Steel, 2018, 39(6): 51-53. DOI：

摘要

研究了不同C、Si含量对低碳钢冷轧板(/%:0.005～0.034 C

0.008～0.054 Si

0.28～0.30 Mn

0.023-0.026 P

0.004～0.007 S

0.044～0.060 Al)力学性能的影响

工业生产流程为铁水预处理-80tBOFRH-连铸-热轧-酸洗-冷轧。结果表明:C、Si含量越高

强度、硬度越高

伸长率越低。采用工业生产的Q195热轧板(/%:0. 0112 C

0.009 Si

0.30 Mn

0.025 P

0.006 S

0.052 Al)进行实验室冷轧试验

试验结果表明冷轧压下率由41%升高到57%

强度、硬度逐渐降低

伸长率略有升高.当C含量为0.005%～0.010%

Si含量为≤0.012%

冷轧下率为40%～50%

Q195冷轧板的抗拉强度(Rm)≤660MPa

(HRB)硬度值为86～89

满足技术要求.

Abstract

The effect of C and Si content on mechanical property of low carbon cold-rolled steel(/% ：0.0051 ~0.0344 C

0.008 ~0.054 Si

0.28 ~0.30 Mn

0.023 ~0.026 P

0. 004 - 0.007 S. 0.044 ~0. 060 Al)has been studied. Industrial process is hot metal pretreatment-80tBOF-RH-continuous casting - hot rolling-acid pickling-cold rolling. Results show that the higher the C or Si content

the higher the strength and hardness

the lower the elongation. Cold rolling test was carried out in the laboratory

the test material was low carbon steel hot rolled (/% :0.0112C

0.009Si

0.30Mn

0.025P

0.006S

0.052Al) which produced in plant. Results of cold rolling test show that when the cold rolling reduction ratio increases from 41% to 57%

strength and hardness gradually increase

the elongating slightly elevate

When the content of C was 0. 005% ~ 0. 010%

Si was ≤0.012% and cold rolling rate was 40% ~ 50%

the tensile strength (Rm) of cold rolled sheet was less than 660 MPa and hardness (HRB) was 86 - 89. meeting technical requirement.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

新型高强韧性弹簧钢40T 和44T 脱碳倾向的研究

真空感应熔炼过程炉衬材料向钢液供氧现象的研究

转炉冶炼超低碳、超低氮钢的工艺技术

高强度弹簧钢60SiCrV7 的性能和应用

30 t EAF-40 t LF冶炼35MnVS 易切削钢的工艺实践