- 油缸用25Mn钢100 t EAF-LF-VD-软吹氩-CC流程B类夹杂物的控制
- Controlling of Grade B Inclusion in 100 t EAF-LF-VD-Soft Ar Browing-CC Flowsheet in 25Mn Steel for Hydraulic Cylinder
- 特殊钢 2021年42卷第4期页码：51-55
- 作者机构：
  
  湖南衡阳华菱钢管有限公司技术中心,衡阳,421001
- 作者简介：
  
  [ "肖鸿光(1968-)，男，高级工程师，1987年重庆大学(本科)毕业，钢铁冶金新产品、新工艺研发。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2021-01-28，
  
  网络首发：2022-03-09，
  
  纸质出版：2021-03-09
- 稿件说明：
移动端阅览
肖鸿光. 油缸用25Mn钢100 t EAF-LF-VD-软吹氩-CC流程B类夹杂物的控制[J]. 特殊钢, 2021,42(4):51-55.

肖鸿光. Controlling of Grade B Inclusion in 100 t EAF-LF-VD-Soft Ar Browing-CC Flowsheet in 25Mn Steel for Hydraulic Cylinder[J]. Special Steel, 2021, 42(4): 51-55.
肖鸿光. 油缸用25Mn钢100 t EAF-LF-VD-软吹氩-CC流程B类夹杂物的控制[J]. 特殊钢, 2021,42(4):51-55. DOI：

肖鸿光. Controlling of Grade B Inclusion in 100 t EAF-LF-VD-Soft Ar Browing-CC Flowsheet in 25Mn Steel for Hydraulic Cylinder[J]. Special Steel, 2021, 42(4): 51-55. DOI：

摘要

衡钢采用硅钙脱氧工艺、控制EAF钢水中全氧含量、LF渣系中Al

含量、控制精炼时间≥40 min、VD真空脱气、软吹时间≥20 min、保护浇注防止钢水二次氧化和促使钢中夹杂物上浮等应用工艺措施

可有效降低钢水中B类夹杂物Al

数量和尺寸以提高钢的洁净度。生产实践表明:油缸钢生产中精炼炉控制钢水[Al

]

s≤0.004%、T[O

]

≤0.002 0%、精炼终渣（FeO） ≤0.8%、碱度（R）控制在2.0～3.2有利于B类夹杂物控制。当B类夹杂物不超过1.0级有利于控制刮滚工艺"白点"的产生。

Abstract

The measures as applying the process of Si-Ca deoxidation

controlling the total content of oxygen in the EAF molten steel and the content of Al

in LF slag

Control refining time ≥40 min

vacuum degassing(VD)

control soft blow time ≥20 min

and protecting cast to prevent secondary oxidation of the molten steel and promote the floating o£ inclusions in the steel are adopted at Hengsteel. The number and size of Grade B inclusion Al

in the molten steel are reduced to improve the cleanliness of steel. Production practice shows that controlling steel [Al

]

s≤0.004%

T[O

]

≤0.0020%

refined final slag (FeO) ≤0.8% and alkalinity (R) between 2.0 and 3.2 in liquid of hydraulic cylinder steel are available to control Grade B inclusion. Grade B inclusions not exceeding class 1.0 is beneficial to c

ontrol the production of " white spots" in the SRB process.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

N80级油管典型缺陷分析及控制的工艺实践

镁处理对45钢中夹杂物的改质效果

铸坯缺陷对SWRH82B钢盘条冷拔质量的影响

动态轻压下对重轨钢U75V疏松和夹杂物的影响

EAF-VOD-VAR和VIM-VAR冶炼工艺对G50超高强度钢韧性的影响