10B21含硼冷镦钢轧后结疤成因分析及工艺改进

肖广阔; 韩鹏龙; 孙晓林; 高春群; 刘志国

您当前的位置：

首页 >

文章列表页 >

10B21含硼冷镦钢轧后结疤成因分析及工艺改进

工艺技术 | 更新时间：2026-01-21

- 10B21含硼冷镦钢轧后结疤成因分析及工艺改进
- Forming Reason and Process Improvement of Seab Defects Rolled Boron-bearing Cold Heading Steel 10B21
- 特殊钢 2022年43卷第5期页码：39-42
- 作者机构：
  
  1. 邯郸钢铁集团有限责任公司冷轧厂,邯郸,056015
  2. 邯郸钢铁集团有限责任公司一炼钢厂,邯郸,056015
  3. 河北工程大学材料科学与工程学院,邯郸,056038
- 作者简介：
  
  [ "肖广阔(1998-)，男，助理工程师" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2022-02-07，
  
  网络首发：2022-09-28，
  
  纸质出版：2022-09-28
- 稿件说明：
移动端阅览
肖广阔, 韩鹏龙, 孙晓林, 等. 10B21含硼冷镦钢轧后结疤成因分析及工艺改进[J]. 特殊钢, 2022,43(5):39-42.

肖广阔, 韩鹏龙, 孙晓林, et al. Forming Reason and Process Improvement of Seab Defects Rolled Boron-bearing Cold Heading Steel 10B21[J]. Special Steel, 2022, 43(5): 39-42.
肖广阔, 韩鹏龙, 孙晓林, 等. 10B21含硼冷镦钢轧后结疤成因分析及工艺改进[J]. 特殊钢, 2022,43(5):39-42. DOI：

肖广阔, 韩鹏龙, 孙晓林, et al. Forming Reason and Process Improvement of Seab Defects Rolled Boron-bearing Cold Heading Steel 10B21[J]. Special Steel, 2022, 43(5): 39-42. DOI：

摘要

通过实验及热力学分析得出，轧制10B21钢结疤形成主要原因为钢中平均N含量为127×10

-6

导致铸坯角部冷却过程中在奥氏体晶界析出细小的BN和AlN夹杂，增加了铸坯的裂纹敏感性，形成铸坯裂纹。通过提高铁水比≥920 kg/t、转炉终点C-T-P(碳-温度-磷)命中率≥85%、出钢口圆流出钢以及LF加热次数≤3次，时间≤25 min等措施可将钢中的氮含量稳定控制在≤50×10

-6

有效避免10B21钢轧后盘条结疤，提高成材率，降低成本。

Abstract

Through experiments and thermodynamic analysis

it is obtained that the main cause of the scab forming of rolled 10B21 steel is the average nitrogen content in steel being 127 x 10

-6

lead to the precipitation of fine BN and AIN inclusions at the austenite grain boundary at the comer of cast billet during cooling

increasing the crack sensitivity of the billet and forming the billet crack

the nitrogen content in steel can be stably controlled below 50 x 10

-6

by increasing the consumption of molten iron ≥ 920 kg/t

increasing the C-T-P ( Carbon-Temperature-Phosphorus) hit rate ≥ 85% at the end of die converter

discharging steel from the outlet round

healing number of times of LF ≤ 3 time

and ≤ 25 minutes casting. It can effectively prevent wire rod scarring of 10B21 steel after rolling to improve the yield of rolled steel and to reduce the production cost.