膨胀及原位观测法研究低碳贝氏体钢轨U25CrNi连续冷却相变

万菲; 刘晓卫; 朱敏; 闻臻

您当前的位置：

首页 >

文章列表页 >

膨胀及原位观测法研究低碳贝氏体钢轨U25CrNi连续冷却相变

组织和性能 | 更新时间：2026-01-21

- 膨胀及原位观测法研究低碳贝氏体钢轨U25CrNi连续冷却相变
- Investigation on Continuous Cooling Transformation Process of Low Carbon Bainite Rail Steel U25CrNi by Dilatation and in-situ Observation Method
- 特殊钢 2022年43卷第3期页码：79-84
- 作者机构：
  
  1. 宝钢股份中央研究院,武汉,430080
  2. 中国铁路郑州局集团有限公司工务部,郑州,450052
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2021-08-10，
  
  网络首发：2022-06-22，
  
  纸质出版：2022-06-22
- 稿件说明：
移动端阅览
万菲, 刘晓卫, 朱敏, 等. 膨胀及原位观测法研究低碳贝氏体钢轨U25CrNi连续冷却相变[J]. 特殊钢, 2022,43(3):79-84.

万菲, 刘晓卫, 朱敏, et al. Investigation on Continuous Cooling Transformation Process of Low Carbon Bainite Rail Steel U25CrNi by Dilatation and in-situ Observation Method[J]. Special Steel, 2022, 43(3): 79-84.
万菲, 刘晓卫, 朱敏, 等. 膨胀及原位观测法研究低碳贝氏体钢轨U25CrNi连续冷却相变[J]. 特殊钢, 2022,43(3):79-84. DOI：

万菲, 刘晓卫, 朱敏, et al. Investigation on Continuous Cooling Transformation Process of Low Carbon Bainite Rail Steel U25CrNi by Dilatation and in-situ Observation Method[J]. Special Steel, 2022, 43(3): 79-84. DOI：

摘要

利用Formastor-F淬火膨胀仪热模拟和VL2000DX-SVF17SP高温激光共聚焦显微镜观察

研究了U25CrNi低碳贝氏体钢轨(/%:0.25C

1.73Si

1.69Mn

0.012P

0.002S

1.40Cr

0.57]Ni

0.49Mo

0.06V)从950℃以不同冷却速度连续冷却后的膨胀曲线和金相组织。结果表明

低冷速下(0.2℃/s)

实验钢组织主要为贝氏体;随冷却速度增大至1℃/s

实验钢组织逐渐过渡为贝氏体和马氏体

且贝氏体板条尺寸随冷速增大而逐渐减小;当冷速达到2℃/s时

冷却过程中基本只发生马氏体相变

实验钢硬度随冷速增大而逐渐增大。

Abstract

By Formastor-F quenching dilatometer thermal simulation and VL2000DX-SVF17SP high temperature laser scanning confocal microscope ( LSCM) observation

the dilatation curve and microstructure of a low carbon bainite rail steel of U25CrNi (/% ：0.25C

1.73Si

1.69Mn

0.012P

0.002S

1.40Cr

0.57Ni

0.49Mo

0. 06V) during continuous cooling process from 950 °C at different cooling rates are studied. The results show that at low cooling rate (0. 2 °C/s)

the microstructure of test steel is mainly bainite ； as the cooling rate increases to 1 °C/s

the microstructure gradually transforms to bainite and martensite

and the size of the bainite plate gradually decreases with the increase of the cooling rate； when the cooling rate reaches 2 °C/s

basically only the martensite transformation occurs during the cooling process

and the hardness of the test steel gradually increases with the increase of the cooling rate.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

NM400马氏体耐磨钢静态CCT曲线

Nb-Ti微合金高强度钢1.5mm冷轧板退火组织和第二相析出行为

热轧冷却速率对微合金非调质钢34Mn2VN组织的影响

固溶温度对022Cr22Ni5Mo3N双相不锈钢组织和性能的影响

Q & P(淬火和分配)工艺对25Si2Ni3钢组织和力学性能的影响