- 38MnSiVS5 非调质钢的 CCT 曲线测定与分析
- Determination and Analysis of CCT Curves of Non-Quenched and Tempered Steel 38MnSiVS5
- 特殊钢 2022年43卷第1期页码：82-85
- 作者机构：
  
  北京交通大学机械与电子控制工程学院,北京,100044
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2021-05-26，
  
  网络首发：2022-03-18，
  
  纸质出版：2022-03-18
- 稿件说明：
移动端阅览
张念, 陈章明, 赵红强, 等. 38MnSiVS5 非调质钢的 CCT 曲线测定与分析[J]. 特殊钢, 2022,43(1):82-85.

Zhang Nian, Chen Zhangming, Zhao Hongqiang, et al. Determination and Analysis of CCT Curves of Non-Quenched and Tempered Steel 38MnSiVS5[J]. Special Steel, 2022, 43(1): 82-85.
张念, 陈章明, 赵红强, 等. 38MnSiVS5 非调质钢的 CCT 曲线测定与分析[J]. 特殊钢, 2022,43(1):82-85. DOI：

Zhang Nian, Chen Zhangming, Zhao Hongqiang, et al. Determination and Analysis of CCT Curves of Non-Quenched and Tempered Steel 38MnSiVS5[J]. Special Steel, 2022, 43(1): 82-85. DOI：

摘要

采用淬火膨胀仪、光学显微镜、维氏硬度计等研究了典型非调质钢38MnSiVS5(/%:0.37C

0.78Si

0.012P

0.045S

0.03Mo

0.120V

0.004Nb

0.003Ti)的显微组织和硬度。测定了其过冷奥氏体连续冷却转变(CCT)曲线。结果表明

38MnSiVS5钢的CCT曲线可分为高温转变区域、中温转变区域和低温转变区域。当冷却速度≤0.89℃/s时为全高温转变区

组织为铁素体和珠光体;当冷却速度为1.78～4.45℃/s时为高温、中温两相复合转变区

组织为铁素体、珠光体和贝氏体;当冷却速度为8.9℃/s时

为高温、中温、低温三相复合转变区

组织为铁素体、珠光体、贝氏体和马氏体;当冷却速度为17.8℃/s时

铁素体和珠光体消失

为中温、低温两相复合转变区

组织为贝氏体+马氏体;当冷却速度≥44.5℃/s时为马氏体转变区。随着冷却速度从0.06℃/s增大到44.5℃/s

38MnSiVS5钢的HV5显微硬度值由213增加至568。

Abstract

The microstructure and micro-hardness of typical non-quenched and tempered steel 38MnSiVS5 ( /% : 0. 37C

0. 78Si

0. 012P

0. 045S

0. 03Mo

0. 120V

0. 004Nb

0. 003Ti) are analyzed by using thermal dilatometer

optical microscope and Vickers hardness tester. The continuous cooling transformation ( CCT ) curves of supercooled austenite are tested. The results show that the CCT curve of steel 38MnSiVS5 could be divided into high temperature transition region

middle temperature transition region and low temperature transition region. With cooling rate ≤0.89 ℃/s

the high temperature transition region is formed with microstructure ferrite and pearlite; With the cooling rate 1.78 ～4.45 ℃/s

the high temperature transition region and middle temperature compound transition region is formed with microstructure ferrite

pearlite and bainite; as the cooling rate up to 8. 9 ℃/s

the high temperature transition region

middle temperature transition region and low temperature transition region are formed with microstructure ferrite

pearlite

bainite and martensite; as the cooling rate up to 17. 8 ℃/s

the F + P structure disappears

the middle temperature transition region and low temperature transition region are formed

the microstructure is bainite and martensite; as the cooling rate ≥44.5 ℃/s

the microstructure is martensite. With the increase of cooling rate from 0. 06 to 44. 5 ℃/s

the HV5 micro-hardness number of 38MnSiVS5 steel increased from 213 to 568.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

新型高强韧性弹簧钢40T 和44T 脱碳倾向的研究

120 t转炉-LF+RH-TB生产LZ50车轴钢坯的化学成分和质量控制

莱钢50t EBT EAF-LF(VD)-CC生产GCr15轴承钢的工艺实践

贵阳特钢60t Consteel EAF-LF(VD)-CC流程生产GCr15轴承钢的工艺实践

TRIP钢 TMP和热处理过程中的组织演变