铁路轴箱轴承用8620钢3 t钢锭轧制产品研发

李博鹏; 陶士君; 张剑锋; 刘月云; 陆竹君; 吕文俊

doi:10.20057/j.1003-8620.2023-00011

您当前的位置：

首页 >

文章列表页 >

铁路轴箱轴承用8620钢3 t钢锭轧制产品研发

产品研发 | 更新时间：2025-05-09

- 铁路轴箱轴承用8620钢3 t钢锭轧制产品研发
- Development of Rolled Steel Products from 3 t Ingot of Grade 8620 for Railway Axle Box Bearings
- 特殊钢 2024年45卷第3期页码：1-4
- 作者机构：
  
  1.大冶特殊钢有限公司，黄石 435001
  2.高品质特殊钢湖北省重点实验室，黄石 435001
- 作者简介：
  
  李博鹏（1981—），男，本科，高级工程师；E-mail：liboepng@citicsteel.com
- 基金信息：
- DOI：10.20057/j.1003-8620.2023-00011
  中图分类号： TF119
- 收稿：2023-02-06，
  
  纸质出版：2024-05-30
- 稿件说明：
移动端阅览
李博鹏,陶士君,张剑锋等.铁路轴箱轴承用8620钢3 t钢锭轧制产品研发[J].特殊钢,2024,45(03):1-4.

Li Bopeng,Tao Shijun,Zhang Jianfeng,et al.Development of Rolled Steel Products from 3 t Ingot of Grade 8620 for Railway Axle Box Bearings[J].Special Steel,2024,45(03):1-4.
李博鹏,陶士君,张剑锋等.铁路轴箱轴承用8620钢3 t钢锭轧制产品研发[J].特殊钢,2024,45(03):1-4. DOI： 10.20057/j.1003-8620.2023-00011.

Li Bopeng,Tao Shijun,Zhang Jianfeng,et al.Development of Rolled Steel Products from 3 t Ingot of Grade 8620 for Railway Axle Box Bearings[J].Special Steel,2024,45(03):1-4. DOI： 10.20057/j.1003-8620.2023-00011.

摘要

针对中国铁路客车和货车轴箱轴承用钢主要使用电渣钢的现状，采用铁水+废钢→70 t 电弧炉→LF→RH→3 t钢锭→均热坑→1350+750/650轧机轧制的流程生产规格

https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=58410055&type=

https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=58410074&type=

2.03200006

2.87866688

60～

https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=58410277&type=

https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=58410275&type=

2.37066650

3.38666677

120 mm 8620钢（质量分数/%：0.18～0.22 C，0.15～0.30 Si，0.75～0.95 Mn，0.45～0.65 Cr，0.45～0.70 Ni，0.15～0.25 Mo，≤0.020 P，≤0.015 S，0.020～0.050 Al）。通过控制出钢留钢留渣、炉后造渣和合金化，真空处理时间≥25 min，氩气弱搅拌，控制钢水过热度，全过程Ar气保护，模铸自动浇注，轧制后控制冷却等工艺措施，生产的产品宏观夹杂物检测含量≤10 mm/dm

，晶粒度8～8.5级，密度达到7.854 g/cm³，钢材各项指标满足标准要求。

Abstract

Based on the current quality situation of ESR bearing steel for passenger railway and wagons in China， the grade 8620 steel bars with diameters between 60 mm and 120 mm are produced with the process as follows： 70 t EAF（Hot Metal+Scrap）→LF→RH→3 t steel ingot→soaking pit →1350+750/650 rolling mill， whose chemical composition are（%）： 0.18-0.22 C，0.15-0.30 Si，0.75-0.95 Mn，0.45-0.65 Cr，0.45-0.70 Ni，0.15-0.25 Mo，≤0.020 P，≤0.015 S，0.020-0.050 Al. By taking technological measures such as steel and slag retention operation，slag formation and alloy addition during tapping， vacuum holding time ≥25 min and soft argon blowing， superheat control， full process Argon protection casting and automatic pouring as well as controlling cooling after rolling etc， to keep 8620 steel bars conform to all technical specification requirements， especially， macro-inclusions of finished bars less than 10 mm/dm³， grain size class 8-8.5， and the density being 7.854 g/cm³.

关键词

Keywords

references

傅志寰，刘忠民，李子明 . 中国铁路百年发展与创新［A］. 中国铁路 . 2021 （ 7 ）： 1 - 7 .

曹文全，俞　峰，王存宇，等 . 高端装备用轴承钢冶金质量性能现状及未来发展方向［J］. 特殊钢， 2021 ， 42 （ 1 ）： 1 - 10 .

杨晓蔚 . 铁路轴箱轴承的可靠性［J］. 轴承， 2013 （ 10 ）： 5 - 7+11 .

肖爱平，张　洲，李德胜，等 . 电渣重熔渣系对GCr15轴承钢洁净度的影响［J］. 特殊钢， 2022 ， 43 （ 6 ）： 34 - 37 .

安　杰，李　涛，王　哲，等 . 60 t电弧炉全废钢熔炼技术［J］. 工业加热， 2020 ， 49 （ 5 ）： 18 - 20 .

李博鹏，王占忠，柳　萍，等 . 120 t BOF-LF-RH-410 mm×530 mm大方坯连铸18CrNiMo7-6钢的工艺实践［J］. 特殊钢， 2019 ， 40 （ 3 ）： 32 - 34 .

蔡开科 . 转炉-精炼-连铸过程钢中氧的控制［J］. 钢铁， 2004 ， 39 （ 8 ）： 49 - 57 .

杨建虹，雷建中，叶健熠，等 . 滚动轴承疲劳寿命的影响因素［J］. 轴承， 2001 （ 5 ）： 28 - 30 .

耿　克，吴　明，翁韶华，等 . 高纯净GCr15轴承钢脆性夹杂物的控制［J］. 特殊钢， 2008 ， 29 （ 5 ）： 54 - 55 .

吴宗双，包燕平，刘建华，等 . 长水口氩封保护浇铸对车轮钢 <math id="M15"><mi>ϕ</mi></math> https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=58410280&type= https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=58410279&type= 1.86266661 2.53999996 450 mm圆坯质量的影响［J］. 特殊钢， 2007 ， 28 （ 2 ）： 54 - 55 .

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

暂无数据