- 含氟精炼渣冶金性能研究及其无氟化设计
- Research on the Metallurgical Properties of Fluorine-Containing Refining Slag and Its Fluoride-Free Design
- 特殊钢 2025年46卷第2期页码：72-77
- 作者机构：
  
  1.北京科技大学绿色低碳钢铁冶金全国重点实验室，北京 100083
  2.宁波钢铁有限公司，宁波 315807
- 作者简介：
  
  李昊哲（1999—），男，硕士； E-mail:2986351031@qq.com
- 基金信息：
- DOI：10.20057/j.1003-8620.2024-00229
  中图分类号： TF718
- 收稿：2024-09-23，
  
  纸质出版：2025-03-30
- 稿件说明：
移动端阅览
李昊哲,金进文,高放等.含氟精炼渣冶金性能研究及其无氟化设计[J].特殊钢,2025,46(02):72-77.

Li Haozhe,Jin Jinwen,Gao Fang,et al.Research on the Metallurgical Properties of Fluorine-Containing Refining Slag and Its Fluoride-Free Design[J].Special Steel,2025,46(02):72-77.
李昊哲,金进文,高放等.含氟精炼渣冶金性能研究及其无氟化设计[J].特殊钢,2025,46(02):72-77. DOI： 10.20057/j.1003-8620.2024-00229.

Li Haozhe,Jin Jinwen,Gao Fang,et al.Research on the Metallurgical Properties of Fluorine-Containing Refining Slag and Its Fluoride-Free Design[J].Special Steel,2025,46(02):72-77. DOI： 10.20057/j.1003-8620.2024-00229.

摘要

针对某钢厂在LF精炼过程中大量使用氟化钙的问题，本研究提出了一种无氟精炼渣系的优化方案。通过FactSage软件计算，确定了无氟精炼渣的最佳成分比例：CaO的质量分数为52%~58%，SiO

为8%~12%，Al

为25%~35%，MgO为5%~7%，碱度控制在4~6之间，（CaO）/（Al

）比值为1.5~2.0。与原渣系相比，新的无氟渣系在1 500 ℃下即可完全熔化，熔化温度降低了60 ℃，曼内斯曼指数约为0.15，满足LF精炼渣的性能要求。在实际生产中应用优化后的渣系，与优化前相比，轧材的全氧含量下降了24%，氮含量下降了21.3%，精炼过程中夹杂物数量减少了22.9%，中间包过程中夹杂物数量减少了22.4%。结果表明，无氟渣系能显著提高钢水的洁净度，对提升钢材质量具有重要作用，同时，也符合当前环保和节能的发展趋势。这些改进不仅提升了钢材的质量，还符合当前环保和节能的发展趋势，减少了对冶金设备的腐蚀和环境的污染，具有重要的环保和经济效益。通过本研究，钢铁企业可以在不使用氟化钙的情况下，依然实现高效的精炼过程，显著提升钢材的洁净度和质量。

Abstract

In view of the large use of calcium fluoride in LF refining process， an optimization scheme of fluorine-free refini

ng slag system is proposed.Calculated by FactSage software， the optimal composition of the fluorine-free refining slag was determined to be： the mass fraction of CaO：52%-58%， SiO

：8%-12%， Al

：25%-35%， MgO：5%-7%， with a basicity of 4-6 and a （CaO）/（Al

）ratio of 1.5-2.0. Compared to the original slag system， the new fluorine-free slag system can be completely melted at 1 500 ℃， reducing the melting temperature by 60 ℃， and has a Mannesmann index of approximately 0.15， which meets the performance requirements of LF refining slag. Using the optimized slag system in the actual production， the application of the optimized slag system resulted in a 24% reduction in total oxygen content， a 21.3% reduction in nitrogen content， a 22.9% reduction in the number of inclusions during refining process， and a 22.4% reduction in the number of inclusions during the tundish process compared to the pre-optimization slag system. The results demonstrate that the fluorine-free slag system not only significantly improves the cleanliness of molten steel and enhances the quality of steel but also aligns with current development trend of environmental protection and energy saving， reducing the corrosion of metallurgical equipment and environmental pollution， thus offering significant environmental protection and economic benefits. This study provides a viable solution for steel enterprises to achieve efficient refining processes and significantly improve the cleanliness and quality of steel without using calcium fluoride.

关键词

Keywords

references

Vantadori S ， Ronchei C ， Scorza D ， et al . Influence of non-metallic inclusions on the high cycle fatigue strength of steels ［J］. International Journal of Fatigue ， 2022 ， 154 ： 106553 .

Zhao Y X ， Ren G Q ， Chen L M ， et al . Influence of non-metallic inclusions on very high-cycle fatigue performance of high-strength steels and interpretation via crystal plasticity finite element method ［J］. Metals ， 2024 ， 14 （ 8 ）： 948 .

郭　帅，朱航宇，韩　赟，等 . 夹杂物对钢塑性和韧性的影响研究进展［J］. 钢铁研究学报， 2022 ， 34 （ 8 ）： 713 - 726 .

袁传泉 . 非金属夹杂物在炼钢过程中的控制方法研究［J］. 冶金与材料， 2024 ， 44 （ 8 ）： 1 - 3 .

黄永生，孙光涛，顾　超，等 . 铝脱氧轴承钢GCr15精炼渣最优成分的分析与实践［J］. 中国冶金， 2017 ， 27 （ 12 ）： 44 - 48 .

Yoon B H ， Heo K H ， Kim J S ， et al . Improvement of steel cleanliness by controlling slag composition ［J］. Ironmaking & Steelmaking ， 2002 ， 29 （ 3 ）： 214 - 217 .

Bielefeldt W V ， Vilela A C F . Study of inclusions in high sulfur， Al-killed Ca-treated steel via experiments and thermodynamic calculations ［J］. Steel Research International ， 2015 ， 86 （ 4 ）： 375 - 385 .

朱富强，汪金林，范鼎东，等 . 20钢管LF精炼渣系优化的工业试验［J］. 特殊钢， 2020 ， 41 （ 5 ）： 45 - 47 .

湛景震，高志勇，范才兵，等 . 我国萤石资源利用现状和战略规划分析［J］. 矿业研究与开发， 2024 ， 44 （ 5 ）： 251 - 259 .

喻　林，梁新腾，张彦恒，等 . 环保型无氟化渣剂在攀钢炼钢中的应用［J］. 特殊钢， 2021 ， 42 （ 2 ）： 46 - 48 .

付景慧，李　勇，郭佳宁，等 . 首钢京唐300 t转炉少氟炼钢技术研究［J］. 山西冶金， 2023 ， 46 （ 7 ）： 53 - 56 .

Guan X ， Yan Z ， Zheng J ， et al . LF Refining Process Optimization Strategy ［J］. Journal of Materials， Processing and Design ， 2024 ， 8 （ 1 ）： 129 - 135 .

张保忠，孙国敏，李志伟，等 . 65Mn钢LF精炼渣系优化及工业试验［J］. 特殊钢， 2023 ， 44 （ 4 ）： 65 - 69 .

赵东伟，包燕平，王敏，等 . 高洁净度铝镇静钢LF精炼渣成分优化［J］. 炼钢， 2013 ， 29 （ 2 ）： 9 - 13 .

李小明，席浩栋，缪德军，等 . 炼钢流程钢中氮的溶解及控制技术［J］. 钢铁， 2021 ， 56 （ 10 ）： 36 - 44+53 .

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

不同余钢量对钢水洁净度的影响

超超临界锅炉管P92耐热钢用大圆坯开发

第三代FC结晶器控流装置的电磁参数优化

改善模具钢洁净度与抛光性能的冶炼工艺实践

帘线钢XLX72 A中氧化物夹杂的演变解析与去除