Application and Dynamics Effect of Compound Inoculation for High Manganese Steel

Wang Zhongjue

Anhui University of Science and Technology, Wuhu 241000

Received:2005-04-23 Published:2005-10-01 Online:2023-04-01

摘要/Abstract

摘要： 采用V_渣+Ti+Zn复合孕育剂在炼钢炉和钢包中对高锰钢进行“二步法”处理,起到控制和改善碳化物的析出量和形态,净化钢液,净化晶界和细化晶粒的孕育效果。叙述了稀土复合变质效果,钢水成分、微合金化元素,孕育剂成分,界面扰动的动力学效应。应用表明,成分(%)为0.901.15C,11.514.0Mn,1.01.5Cr高锰钢经V_渣+Ti+Zn复合孕育处理后,铸态力学性能有显著改善:钢的抗拉强度、延伸率、冲击韧性分别由401MPa、3.7%和2.3J/cm²提高到491MPa、8.4%和23J/cm²。

关键词: 高锰钢, V_渣+Ti+Zn, 复合孕育, 动力学效应

Abstract: As the high manganese steel is treated by "top step process” in steelmaking furnace and in ladle using V_slag + Ti + Zn compound inoculation agent, the inoculation effect to control and improve precipitated amount and morphology of carbide, clean grain boundary and fine grain shall be got. Hie dynamics effects of compound inoculation modified effect of rare earth elements, composition of liquid steel, microalloying elements, inoculation composition and interface fluctuation are presented in this paper. Hie application results showed that the as cast mechanical properties of 0.90~1.15C, 11.5~14.0Mn, 1.0~1.5Cr high manganese steel were obviously improved by V_slag + Ti + Zn compound inoculation treatment, the tensile strength, elongation and impact toughness of steel were respectively increased to 491 MPa, 8.4% and 23 J/cm² from 401 MPa, 3.7% and 2.3 J/cm² .

Key words: High Manganese Steel, V_slag + Ti + Zn, Compound Inoculation, Dynamic Effect

王仲珏. 铸造高锰钢复合孕育的动力学效应和应用[J]. 特殊钢, 2005, 26(5): 39-41.

Wang Zhongjue. Application and Dynamics Effect of Compound Inoculation for High Manganese Steel[J]. Special Steel, 2005, 26(5): 39-41.

[1]	潘胡江, 杨新明, 李光强, 杨治争, 霍旭东. Ti微合金化对高锰钢组织和性能的影响[J]. 特殊钢, 2024, 45(2): 74-78.
[2]	孔令种, 邓志银, 朱苗勇. 中高锰钢在真空精炼过程中的气化行为[J]. 特殊钢, 2018, 39(4): 17-19.
[3]	王为波, 赵朋成, 张敏, 马伯江, 李镇江, 赵程, 侯俊英. 高锰钢铁路辙叉应力状态有限元分析[J]. 特殊钢, 2007, 28(2): 44-46.
[4]	张敏, 王为波, 周永欣, 吕振林, 安强 . 加工硬化对1.14C-12.72Mn 钢铁路辙叉表面剥落的影响[J]. 特殊钢, 2005, 26(3): 45-47.