固溶处理对00Cr25Ni7Mo4N双相不锈钢组织和力学性能的影响

特殊钢 ›› 2009, Vol. 30 ›› Issue (3): 58-60.

固溶处理对00Cr25Ni7Mo4N双相不锈钢组织和力学性能的影响

王晓峰¹, 陈伟庆¹, 毕洪运²

1北京科技大学冶金与生态工程学院，北京100083；
2宝山钢铁股份有限公司，上海201900

收稿日期:2008-11-15 出版日期:2009-06-01 发布日期:2022-11-24
作者简介:王晓峰(1979-)，男，博士研究生.钢的质量硏究与品种开发

Influence of Solution Treatment on Structure and Mechanical Properties of Duplex Stainless Steel 00Cr25Ni7Mo4N

Wang Xiaofeng¹ , Chen Weiqing¹ , Bi Hongyun²

1 School of Metallurgical and Ecological Engineering, University of Science and Technology, Beijing 100083 ；
2 Baosteel Co Ltd, Shanghai 201900

Received:2008-11-15 Published:2009-06-01 Online:2022-11-24

摘要/Abstract

摘要： 研究了真空感应炉(6.5 kg锭)熔炼的00Cr25Ni7Mo4N钢(%:0.007～0.009C、24.50～24.84Cr、6.92～6.99Ni、3.65～3.72Mo、0.27～0.30N)的相比例和固溶处理温度对钢的组织和力学性能的影响。结果表明,随固溶温度由1 050℃增至1 200℃,钢中铁素体含量由48%～50%提高至53%～55%。当固溶温度由1 050℃提高至1100℃,钢的强度下降,伸长率和冲击韧性增加,当固溶温度由1 100℃提高至1 200℃,钢的强度增加,伸长率和韧性降低,该钢最佳固溶温度为1 100℃±50℃。

关键词: 00Cr25Ni7Mo4N双相不锈钢, 相比例, 固溶温度, 力学性能

Abstract: Effect of phase proportion and solution temperature on structure and mechanical properties of steel 00Cr25Ni7Mo4N ( % ： 0. 007 ~0.009C, 24. 50 〜24. 84Cr, 6.92 〜6.99Ni, 3.65 〜3. 72Mo, 0. 27 ~0. 30N) melted by vacuum induction furnace (6. 5 kg ingot) has been studied. Results showed that with increasing solution temperature from 1 050 °C to 1 200 °C , ferrite content in steel increased from 48% 〜50% to 53% 〜55% ; with increasing solution temperature from 1 050 °C to 1 100 °C , the strength of steel decreased while the elongation and impact toughness of steel increased ,and with increasing the solution temperature from 1 100 °C to 1 200 °C , the strength of steel increased while the e- longation and impact toughness of steel decreased, so optimum temperature of the steel was 1 100 °C ±50°C.

Key words: Duplex Stainless Steel 00Cr25Ni7Mo4N, Phase Proportion, Solution Temperature, Mechanical Properties

王晓峰, 陈伟庆, 毕洪运. 固溶处理对00Cr25Ni7Mo4N双相不锈钢组织和力学性能的影响[J]. 特殊钢, 2009, 30(3): 58-60.

Wang Xiaofeng , Chen Weiqing, Bi Hongyun. Influence of Solution Treatment on Structure and Mechanical Properties of Duplex Stainless Steel 00Cr25Ni7Mo4N[J]. Special Steel, 2009, 30(3): 58-60.