Nb-RE微合金化对复杂刀具用TGM2高速钢组织和性能的影响

特殊钢 ›› 2009, Vol. 30 ›› Issue (6): 45-46.

Nb-RE微合金化对复杂刀具用TGM2高速钢组织和性能的影响

雷利军，朱小坤，李德辉，周英孝，徐文瑛

天工国际有限公司，丹阳212312

收稿日期:2009-05-28 出版日期:2009-12-01 发布日期:2022-11-29
作者简介:雷利军(1963-)，男，工学硕士，高级工程师，1991年河北工业大学毕业，工模具钢研究生产。

Effect of Nb-RE Microalloying on Structure and Properties of High Speed Steel TGM2 for Complicated Tool

Lei Lijun, Zhu Xiaokun, Li Dehui, Zhou Yingxiao ， Xu Wenying

Tiangong International Corp Ltd, Danyang 212312

Received:2009-05-28 Published:2009-12-01 Online:2022-11-29

摘要/Abstract

摘要： Nb-RE微合金化TGM2高速钢(%:0.88～0.89C、4.14～4.16Cr、4.73～4.76Mo、6.09～6.12W、1.85～1.86V、0.05～0.10Nb、0.05～0.06RE)由25 t EAF-30 t LF(VD,加Nb-RE)-1 t ESR工艺冶炼。试验结果表明,经Nb-RE微合金化后,TGM2高速钢Φ96 mm材淬火晶粒尺寸明显细化,晶粒度由原来未微合金化钢的9.5级提高至10～10.5级;淬、回火后硬度HRC为65.2～65.8,600℃4 h红硬性HRC为62.1～62.3,Nb-RE TGM2钢制成刀具的切削寿命较原TGM2钢提高20%。

关键词: Nb-RE微合金化, TGM2高速钢, 复杂刀具, 使用寿命

Abstract: Nb-RE microalloying high speed steel TGM2 (% : 0. 88 ~ 0. 89C, 4. 14 ~ 4. 16Cr, 4. 73 〜4. 76Mo, 6. 09 〜6. 12W, 1.85 ~ 1.86V, 0. 05 〜0. 10Nb, 0. 05 〜0.06RE) was melted by 25 t EAF- 30 t LF (VD, adding Nb- RE) - 1 t ESR process. Test results show that with Nb-RE microalloying, the grain size of quenched Φ96 mm bar of high speed steel TGM2 is obviously fine i. e. the grain rating increases to 10 ~ 10. 5 from 9. 5 of original steel without microalloying； the hardness HRC of quenched and tempered Nb-RE steel is 65. 2 ~65. 8 and its red hardness HRC at 600 °C for 4 h is 62. 1 〜62. 3 ； as compared with original TGM2 steel without added Nb-RE, the service life of tool manufactured by Nb- RE TGM2 steel increases by 20%.

Key words: Nb-RE Microalloying, High Speed Steel TGM2, Complicated Tool, Service Life

雷利军, 朱小坤, 李德辉, 周英孝, 徐文瑛. Nb-RE微合金化对复杂刀具用TGM2高速钢组织和性能的影响[J]. 特殊钢, 2009, 30(6): 45-46.

Lei Lijun, Zhu Xiaokun, Li Dehui, Zhou Yingxiao , Xu Wenying. Effect of Nb-RE Microalloying on Structure and Properties of High Speed Steel TGM2 for Complicated Tool[J]. Special Steel, 2009, 30(6): 45-46.

[1]	张利武, 姚娜. 提高60 t转炉出钢口使用寿命的生产实践[J]. 特殊钢, 2017, 38(1): 36-38.
[2]	于学森, 沈奎, 廖舒纶, 麻晗. 双渣线操作提高结晶器浸入式水口使用寿命的工艺实践[J]. 特殊钢, 2014, 35(6): 32-34.
[3]	雷利军. 丝锥用Nb微合金化TGM2A-S高速钢的开发[J]. 特殊钢, 2011, 32(6): 23-24.