立式板坯连铸机结晶器内液面波动的物理模拟

特殊钢 ›› 2011, Vol. 32 ›› Issue (3): 12-14.

立式板坯连铸机结晶器内液面波动的物理模拟

赵志刚^1,2，胡坤太²，陈远清²，施哲¹，仇圣桃²

1昆明理工大学冶金与能源工程学院，昆明650093；
2钢铁研究总院连铸技术国家工程研究中心，先进钢铁流程及材料国家重点实验室，北京100081

收稿日期:2011-01-05 出版日期:2011-06-01 发布日期:2022-10-17
通讯作者: 施哲，教授，昆明理工大学冶金与能源工程学院，昆明650093
作者简介:赵志刚( 1985-),男，硕士研究生，2009年昆明理工大学毕业,连铸技术与仿真研究。
基金资助:
科技部科研院所技术开发研究专项资金项目(NC- STE-2006-JK-ZX-030)

Physical Modeling of Fluctuation of Liquid Level in Mold of Vertical Slab Concaster

Zhao Zhigang^1，2, Hu Kuntai², Chen Yuanqing², Shi Zhe¹，Qiu Shengtao²

1 College of Metallurgical and Energy Engineering, Kunming University of Science and Technology, Kunming 650093；
2 The State Key Laboratory of Advanced Processes and Products for Iron and Steel, National Engineering Research Center of Continuous Casting Technology, Central Iron and Steel Research Institute, Beijing 100081

Received:2011-01-05 Published:2011-06-01 Online:2022-10-17

摘要/Abstract

摘要： 为优化200 mm×1 300 mm立式板坯连铸结晶器浸入式水口,采用1:1水模型模拟研究水口结构参数(侧孔断面-40 mm×80 mm,40 mm×40 mm和侧孔角度+15°和-15°)以及工艺参数(浸入深度-100～130 mm,拉速0.45～0.65 m/min)对液面波动的影响。结果表明:水口结构参数对液面波动的影响较明显;侧孔断面40 mm×40 mm,侧孔角度+15°的2^#水口的使用性能相对较好;浸入深度对液面波动量的影响不大;拉速对液面波动的影响与水口结构有关,对拉速变化的敏感程度由大到小的次序是2^#水口(40 mm×40 mm,+15°),4^#水口(40 mm×40mm,-15°),3^#水口(40 mm×80 mm,-15°),1^#水口(40 mm×80 mm,+15°)。

关键词: 立式连铸机, 结晶器, 液面波动, 浸人式水口

Abstract: In order to optimize the submerged entry nozzle (SEN) for 200 mm x 1 300 mm vertical slab casting mold, the effect of parameters of nozzle structure (cross section dimension of side port- 40 mm x40 mm and 40 mm x80 mm, and angle of port- + 15° and - 15°) and process parameters ( submerged depth 100 ~ 130 mm and casting speed 0. 45 ~ 0. 65 m/min) on fluctuation of liquid level has been simulated and studied by 1 ： 1 water model. Results show that the effect of nozzle structure parameters on fluctuation of liquid level is more obvious and the structure of 2^# nozzle with side port dimension 40 mm x40 mm and angle of port +15° has better service performance； the effect of submerged depth on fluctuation of liquid level isn' t appreciable ； and the effect of casting speed on fluctuation of liquid level relates to nozzle structure, and the descending order of sensitivity of nozzle structure to casting speed is nozzle 2^#(40 mm x40 mm, +15°), nozzle 4^#(40 mm x40 mm, - 15°) , nozzle 3^# (40 mm x 80 mm, - 15°) and nozzle 1^#(40 mm x 80 mm, + 15°).

Key words: Vertical Concaster, Mold, Fluctuation of Liquid Level, Submerged Entry Nozzle

赵志刚, 胡坤太, 陈远清, 施哲, 仇圣桃. 立式板坯连铸机结晶器内液面波动的物理模拟[J]. 特殊钢, 2011, 32(3): 12-14.

Zhao Zhigang Hu Kuntai, Chen Yuanqing, Shi Zhe, Qiu Shengtao. Physical Modeling of Fluctuation of Liquid Level in Mold of Vertical Slab Concaster[J]. Special Steel, 2011, 32(3): 12-14.

[1]	王玉平, 吴健博. 1000～2200 mm宽板坯连铸机结晶器流场优化与应用[J]. 特殊钢, 2024, 45(5): 85-89.
[2]	刘启龙, 邓勇, 李华刚, 韦如军, 曹成虎, 张敏. IF钢板坯结晶器电磁搅拌数值模拟与工艺实践[J]. 特殊钢, 2023, 44(6): 83-88.
[3]	周伟基, 姚玉东, 刘佳伟, 岳峰, 史建凯. 结晶器电磁搅拌对Q355NE Φ800 mm圆坯凝固组织及偏析的影响[J]. 特殊钢, 2023, 44(3): 64-68.
[4]	林鹏, 许正周, 印传磊, 张洪才, 翟万里, 许光乐. 60Si2Mn弹簧钢150 mm x 150 mm铸坯缺陷分析与工艺优化[J]. 特殊钢, 2022, 43(5): 59-62.
[5]	杨文轩, 王勇, 高锦国, 刘威, 杨树峰, 李京社. 1 500 mm x230 mm板坯结晶器液面波动与卷渣行为水力学模型试验和应用[J]. 特殊钢, 2022, 43(2): 21-26.
[6]	韩秀丽, 闫晓鹏, 刘磊, 赵凯, 王程, 杜亮. 连铸结晶器保护渣渣膜传热特性研究进展[J]. 特殊钢, 2021, 42(6): 6-13.
[7]	党爱国, 钟保军, 田新中, 李永超. 160 mm x 160 mm连铸坯结晶器电磁搅拌对钢液流场影响的数值模拟[J]. 特殊钢, 2020, 41(6): 6-11.
[8]	王东兴, 杨伟勇, 汪春梅, 陶群南, 黄雁, 左小坦. 含铌钢HRB400Nb 180 mm x 180 mm铸坯角部裂纹分析及改进工艺[J]. 特殊钢, 2020, 41(5): 25-28.
[9]	郎炜旳, 翟俊, 陈洋, 李晓军, 常国栋. 不锈钢连铸板坯结晶器钢液喂稀土丝工艺试验研究[J]. 特殊钢, 2020, 41(3): 35-38.
[10]	张洪才, 林鹏, 许正周, 印传磊, 许光乐. 钢球用钢Φ380mm连铸圆坯表面裂纹原因分析及工艺改进[J]. 特殊钢, 2020, 41(1): 39-42.
[11]	郑文超, 夏旺苟, 何浪, 陈国生, 张念. 汽车曲轴用含硫易切削钢C38N2硫化物控制的工艺实践[J]. 特殊钢, 2019, 40(1): 43-46.
[12]	谢志彬, 邵青立, 张国平, 王子霖, 何宁, 王然. 快速抽锭电渣重熔M2高速钢160 mm x160 mm铸坯工艺及质量[J]. 特殊钢, 2019, 40(1): 47-51.
[13]	杨传浩, 刘仲礼, 姜科, 宋道滨. 60 t电渣炉结晶器冷却水流速计算-设计优化和重熔不锈钢的应用[J]. 特殊钢, 2018, 39(6): 25-27.
[14]	林鹏, 张洪才, 印传磊, 翟万里, 许光乐. 含硫45钢铸坯缺陷分析与工艺优化[J]. 特殊钢, 2018, 39(5): 40-43.
[15]	刘启龙, 仇圣桃, 占树华, 王志政. 气体流量及水口底部形状对板坯结晶器内流场影响的水模型试验[J]. 特殊钢, 2018, 39(2): 1-5.