九辗矫直机钢板矫直工艺的有限元模拟研究

特殊钢 ›› 2012, Vol. 33 ›› Issue (1): 9-11.

九辗矫直机钢板矫直工艺的有限元模拟研究

张焕军¹，程晓茹¹，任勇¹，王振国¹，詹胜利²，黄大军²

1武汉科技大学材料与冶金学院，武汉430081 ；
2武汉钢铁集团公司热轧总厂，武汉430083

收稿日期:2011-08-30 出版日期:2012-02-01 发布日期:2022-09-19
作者简介:张焕军(1986-),男，硕士研究生，轧制过程计算机控制研究。

A Study on Finite Element Simulation for Leveling Process of Steel Plate by Straightener with Nine-Roll

Zhang Huanjun¹, Cheng Xiaoru¹, Ren Yong¹ , Wang Zhenguo¹ , Zhan Shenli² ， Huang Dajun²

1 College of Materials Science and Metallurgical Engineering, Wuhan University of Science and Technology, Wuhan 430081;
2 Hot Rolling General Plant, Wuhan Iron and Steel Group Corp, Wuhan 430083

Received:2011-08-30 Published:2012-02-01 Online:2022-09-19

摘要/Abstract

摘要： 通过建立的有限元模型,研究了22 mm Q345钢板(/%:≤0.20C、≤O.55Si、≤1.70Mn、O.02～O.15V、0.015～0.060Nb、0.02～O.20Ti)在9辊矫直机矫直时首辊与尾辊的位置对钢板平直度和表面残余应力的影响,得到钢板不平的位置集中在尾部。1~#辊和9~#辊在高度上的自由调节,可以保证钢板出矫直机时不会出现上弯或下弯。钢板的上表面残余应力比下表面低,延钢板长度方向,钢板表面残余应力呈现尾部高、头部低的状态。

关键词: 9辊矫直机, Q345钢, 22mm板, 有限元模拟。平直度, 残余应力

Abstract: The effect of first roll and last roll position on plate flatness and surface residual stress of 22 mm Q345 steel plate (/% ： ≤0. 20C,≤ 0. 55Si, ≤1. 70Mn, 0. 02 - 0. 15V, 0. 015 ~ 0. 060Nb, 0. 02 ~ 0. 20Ti) during leveling process by a 9-roll straightener has been studied by established finite element model to get the position of un-flatness is mainly at tail of plate. With free adjustment of height of Nol (first) roll and No9 (last) roll the plate is ensured no-bending up and down as the plate is out of straightener. The residual stress at upper surface of plate is lower that at bottom surface, and along the length direction of plate, the residual stress at head of plate is lower than that at end of plate.

张焕军, 程晓茹, 任勇, 王振国, 詹胜利, 黄大军. 九辗矫直机钢板矫直工艺的有限元模拟研究[J]. 特殊钢, 2012, 33(1): 9-11.

Zhang Huanjun, Cheng Xiaoru, Ren Yong , Wang Zhenguo, Zhan Shenli, Huang Dajun. A Study on Finite Element Simulation for Leveling Process of Steel Plate by Straightener with Nine-Roll[J]. Special Steel, 2012, 33(1): 9-11.

[1]	杨维宇, 何建中, 梁正伟, 李智丽. 回火工艺对热轧U20Mn2SiCrNiMo贝氏体钢轨组织性能的影响[J]. 特殊钢, 2021, 42(6): 68-71.
[2]	李秀霞. 冷轧变形量和退火对双相高强度钢DP780应力分布的影响[J]. 特殊钢, 2017, 38(1): 59-62.
[3]	肖志余, 李丽容, 刘兵, 刘小宁. Q345钢宽展模型对中厚板轧制压力预算精度的影响[J]. 特殊钢, 2016, 37(6): 13-16.
[4]	刘升, 贺铸, 刘宇鑫. 3Cr13Mo钢板多参数YAG激光焊接残余应力和形变的仿真研究[J]. 特殊钢, 2014, 35(3): 15-18.
[5]	刘炼, 任勇, 程晓茹, 李春光, 尹皓, 詹三林. 45钢中厚板矫直过程温度场有限元模拟及残余应力分析[J]. 特殊钢, 2013, 34(2): 7-10.
[6]	成日金, 王志衡, 王洪富, 夏金魁, 曹龙琼, 张华. Q345钢250 mm x 2 000 mm板坯连铸凝固规律及工艺优化[J]. 特殊钢, 2013, 34(2): 41-44.
[7]	谢凯, 程晓茹, 任勇, 詹胜利, 黄大军. Q345钢中厚板热矫直变形抗力与弹性模量数学模型的研究[J]. 特殊钢, 2011, 32(4): 4-6.
[8]	宋广胜, 刘相华, 王国栋, 隋凤利. 齿轮钢淬火过程多场耦合分析[J]. 特殊钢, 2007, 28(1): 7-9.