HRB335热轧带肋钢筋轧后双线穿水冷却技术的应用

特殊钢 ›› 2013, Vol. 34 ›› Issue (1): 34-36.

HRB335热轧带肋钢筋轧后双线穿水冷却技术的应用

焦国利¹，刘霞²，何文萍²

1包钢西创机制公司，包头014010；
2包头钢铁职业技术学院机械系，包头014010

收稿日期:2012-07-27 出版日期:2013-02-01 发布日期:2022-09-13
作者简介:焦国利(1966-).男，硕士，高级工程师,1988年大连理工大学毕业，工艺材料研究

Application of Double Through-Water Cooling Technology for HRB335 Hot-Rolled Ribbed Steel Bar after Rolling

Jiao Guoli¹ , Liu Xia²， He Wenping²

1 Northwest Venture Machineiy and Equipment Manufacturing Co Ltd, Baosteel, Baotou 014010;
2 Department of Mechanical Engineering, Baotou Iron and Steel Vocational Technology Institute, Baotou 014010

Received:2012-07-27 Published:2013-02-01 Online:2022-09-13

摘要/Abstract

摘要： 针对轧机产量提高后冷床冷却能力不足的问题,安装了轧后棒材穿水冷却装置。生产结果表明,HRB335Φ16 mm热轧带肋钢筋(/%:0.20C、0.20～0.40Si、0.4～1.2Mn),原终轧速度10.5～11.0 m/s,钢材至冷床温度1020～1050℃,钢筋的屈服、抗拉强度和伸长率分别为342 MPa、520 MPa和16.5%;使用穿水系统后终轧速度提高至11.5～12.0 m/s,钢材至冷床的温度降至880～900℃,通过冷床后降至260℃,钢筋的屈服、抗拉强度和伸长率分别为360 MPa,556 MPa和16.9%,生产率提高3%～5%。

Abstract: In view of the problem of insufficient capacity of cooling bed with increasing output of rolling mill products, the through-water cooling unit for rolled bar is installed. Production results show that for HRB335 Φ16 mm hot-rolled ribbed steel bar (/%: 0. 20C, 0. 20 〜0. 40Si, 0. 4 ~ 1. 2Mn), with original finishing rolling speed 10. 5 -11.0 m/s, the beginning temperature of steel bar at cooling bed is 1 020 ~ 1 050 °C, the yield, tensile strength and elongation of ribbed bar are respectively 342 MPa, 520 MPa and 16. 5% ； and after using through-water cooling system, the finishing rolling speed increases to 11.5 ~ 12. 0 m/s, the beginning temperature of steel bar at cooling bed decreases to 880 ~ 900 °C and at outlet of cooling bed the temperature of bar is 260 °C, the yield, tensile strength and elongation of ribbed bar increase respectively to 360 MPa, 556 MPa and 16. 9%, and the productivity of mill increases by 3% - 5%.

焦国利, 刘霞, 何文萍. HRB335热轧带肋钢筋轧后双线穿水冷却技术的应用[J]. 特殊钢, 2013, 34(1): 34-36.

Jiao Guoli , Liu Xia, He Wenping. Application of Double Through-Water Cooling Technology for HRB335 Hot-Rolled Ribbed Steel Bar after Rolling[J]. Special Steel, 2013, 34(1): 34-36.